Laser repairing method for hot roller with toughness and strength

A technology of laser repair and hot roll, which is applied in the field of laser cladding, can solve problems such as poor surfacing, easy cracks, and insufficient hardness, and achieve high fusion rate, small roll deformation, and uniform thickness and hardness.

Inactive Publication Date: 2017-04-19
DANYANG HONGTU LASER TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the reason of the material, the surfacing of hot rolls is very poor. Using ordinary surfacing methods will easily cause defects such as cracks, pores, and insufficient hardness, which makes the repair of rolls of this type of material difficult.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Laser repairing method for hot roller with toughness and strength
  • Laser repairing method for hot roller with toughness and strength
  • Laser repairing method for hot roller with toughness and strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The specific steps of the laser repair method of the hot roll of the present embodiment are as follows:

[0024] A. Pretreat the surface of the hot roll to be repaired, and test and analyze the hot roll.

[0025] Remove the dust, oil and rust on the hot roll; detect the size of each part of the hot roll, determine the failure part and its wear amount; check the radial and end runout of the hot roll to check whether the roll is deformed; remove the roll by grinding The fatigue layer of the failure part shall be 0.5mm, and shall be cleaned.

[0026] B. According to the failure analysis results of the hot roll, optimize the process parameters and perform multi-layer laser cladding.

[0027] Using the preset powder feeding method, the fast cross-flow carbon dioxide laser is used as the light source to perform continuous spiral feed lap scanning on the hot roll; the laser power is 2150W, and the elevation (that is, the distance between the laser and the object, elevation = ...

Embodiment 2

[0036] The specific steps of the laser repair method of the hot roll of the present embodiment are as follows:

[0037] A. Pretreat the surface of the hot roll to be repaired, and test and analyze the hot roll.

[0038]Remove the dust, oil and rust on the hot roll; detect the size of each part of the hot roll, determine the failure part and its wear amount; check the radial and end runout of the hot roll to check whether the roll is deformed; remove the roll by grinding The fatigue layer of the failure part shall be 0.5mm, and shall be cleaned.

[0039] B. According to the failure analysis results of the hot roll, optimize the process parameters and perform multi-layer laser cladding.

[0040] Using the preset powder feeding method, the fast cross-flow carbon dioxide laser is used as the light source to carry out continuous spiral feed lap scanning on the hot roll; the laser power is 2160W, the elevation is 235mm, the spot size is 12mm×1.8mm, and the scanning speed is 150mm / m...

Embodiment 3

[0049] The specific steps of the laser repair method of the hot roll of the present embodiment are as follows:

[0050] A. Pretreat the surface of the hot roll to be repaired, and test and analyze the hot roll.

[0051] Remove the dust, oil and rust on the hot roll; detect the size of each part of the hot roll, determine the failure part and its wear amount; check the radial and end runout of the hot roll to check whether the roll is deformed; remove the roll by grinding The fatigue layer of the failure part shall be 0.5mm, and shall be cleaned.

[0052] B. According to the failure analysis results of the hot roll, optimize the process parameters and perform multi-layer laser cladding.

[0053] Using the pre-set powder feeding method, the fast cross-flow carbon dioxide laser is used as the light source to perform continuous spiral feed lap scanning on the hot roll; the laser power is 2200W, the elevation is 240mm, the spot size is 12mm×1.8mm, and the scanning speed is 140mm / m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a laser repairing method for a hot roller with toughness and strength. A transitional alloy layer, an intermediate alloy layer and a surface alloy layer are arranged on the surface of the hot roller layer by layer in a laser cladding manner; alloy powder adopted by the transitional alloy layer is prepared from the following components in percentage by mass: 0.2 to 0.3 percent of C, 3.2 to 3.6 percent of Si, 1.2 to 1.8 percent of B, 2.2 to 2.6 percent of Fe, 7 to 8 percent of Cr and the balance being Ni; alloy powder adopted by the intermediate alloy layer is prepared from the following components in percentage by mass: 0.4 to 0.5 percent of C, 3.8 to 4.3 percent of Si, 11.2 to 11.93 percent of B, 2.5 to 3.2 percent of Fe, 10 to 12 percent of Cr and the balance being Ni; and alloy powder adopted by the surface alloy layer is prepared from the following components in percentage by mass: 0.05 to 0.1 percent of C, 3.0 to 3.16 percent of Si, 2 to 4 percent of Fe, 16 to 19 percent of Cr, 27 to 30 percent of Mo and the balance being Co. The surface of the hot roller repaired by adopting the laser repairing method for the hot roller has good wear resistance, corrosion resistance and hot hardness; and in addition, the inner part of the hot roller has the toughness and the strength, and a good laser cladding effect is realized.

Description

technical field [0001] The invention relates to a laser cladding method, in particular to a laser cladding method for a hot roll with both toughness and strength in mind. Background technique [0002] Rolls are the largest consumables in my country's metallurgical industry, and hot rolls are one of the main consumable spare parts in steel rolling production, and their consumption is far greater than that of cold rolls. The consumption of hot rolls is about 5% to 15% of the production cost of steel rolling. The quality of hot rolls is not only related to the cost of rolling steel production and the production rate of rolling mills, but also affects the quality of rolled products to a large extent. With the development of steel rolling technology, the speed and automation of rolling mills have been continuously improved, which puts forward higher requirements for the quality of hot rolls, especially the wear resistance, strength and toughness of hot rolls. [0003] The obvio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C24/10C22C19/05
CPCC23C24/103C22C19/056C22C19/058
Inventor 何建方刘少彬马万花
Owner DANYANG HONGTU LASER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com