Method for preparing cathode material AgCuO2 through anodic oxidation electrodeposition

A cathode material, anodic oxidation technology, applied in the direction of electrolytic inorganic material coating, circuit, electrical components, etc., to achieve the effect of simple experimental equipment, environmental friendliness and low cost

Inactive Publication Date: 2017-05-10
ZHEJIANG UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] So far, AgCuO 2 The preparation is mainly through the precursor Ag 2 Cu 2 o 3 It is obtained by chemical oxidation (ozone, persulfate, etc.) or electrochemical oxidation, so it is necessary to prepare the precursor Ag 2 Cu 2 o 3 , and then oxidized to give the product AgCuO 2 , however, by anodic electrodeposition from the corresponding salt AgNO 3 , Cu(NO 3 ) 2 Get AgCuO directly in one step 2 method has not yet been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cathode material AgCuO2 through anodic oxidation electrodeposition
  • Method for preparing cathode material AgCuO2 through anodic oxidation electrodeposition
  • Method for preparing cathode material AgCuO2 through anodic oxidation electrodeposition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1) The working electrode, that is, the activation of ITO conductive glass: wash the ITO conductive glass with acetone for 3 times, then clean the conductive glass with deionized water in an ultrasonic cleaner for 30 minutes, and then place the conductive glass in dilute nitric acid solution for 30 seconds. , and finally washed with deionized water and set aside;

[0016] 2)AgCuO 2 Preparation of thin film electrodes: 0.000375mol of AgNO 3 and 0.0003mol of Cu(NO 3 ) 2 ·3H 2 O was stirred and dissolved in a certain amount of distilled water, and 0.05mol of NH was added dropwise while stirring. 3 , making it with Ag + and Cu 2+ Fully complex until the solution is dark blue and clear, then add 0.025mol NaOH solution to adjust the pH of the solution, and finally add distilled water to obtain a clear electrolyte solution with a volume of 100mL; ITO conductive glass is used as the working electrode, and the platinum sheet electrode is used as the counter electrode. The ...

Embodiment 2

[0020] 1) The working electrode, that is, the activation of ITO conductive glass: wash the ITO conductive glass with acetone for 3 times, then clean the conductive glass with deionized water in an ultrasonic cleaner for 30 minutes, and then place the conductive glass in dilute nitric acid solution for 30 seconds. , and finally washed with deionized water and set aside;

[0021] 2)AgCuO 2 Preparation of thin film electrodes: 0.000375mol of AgNO 3 and 0.0003mol of Cu(NO 3 ) 2 ·3H 2 O was stirred and dissolved in a certain amount of distilled water, and 0.05mol of NH was added dropwise while stirring. 3 , making it with Ag + and Cu 2+ Fully complex until the solution is dark blue and clear, then add 0.025mol NaOH solution to adjust the pH of the solution, and finally add distilled water to obtain a clear electrolyte solution with a volume of 100mL; ITO conductive glass is used as the working electrode, and the platinum sheet electrode is used as the counter electrode. The ...

Embodiment 3

[0025] 1) The working electrode, that is, the activation of ITO conductive glass: wash the ITO conductive glass with acetone for 3 times, then clean the conductive glass with deionized water in an ultrasonic cleaner for 30 minutes, and then place the conductive glass in dilute nitric acid solution for 30 seconds. , and finally washed with deionized water and set aside;

[0026] 2)AgCuO 2 Preparation of thin film electrodes: 0.000375mol of AgNO 3 and 0.0003mol of Cu(NO 3 ) 2 ·3H 2 O was stirred and dissolved in a certain amount of distilled water, and 0.05mol of NH was added dropwise while stirring. 3 , making it with Ag + and Cu 2+Fully complex until the solution is dark blue and clear, then add 0.025mol NaOH solution to adjust the pH of the solution, and finally add distilled water to obtain a clear electrolyte solution with a volume of 100mL; ITO conductive glass is used as the working electrode, and the platinum sheet electrode is used as the counter electrode. The s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing cathode material AgCuO2 through anodic oxidation electrodeposition. The method is characterized in that in strong alkaline mixed electrolyte, ammonia water and Ag + are complexed and ammonia water and Cu2 + are complexed through an anodic electrodeposition method, constant current electrodeposition is carried out in a water bath at the temperature of 40 DEG C, an AgCuO2 thin film electrode which has the sheet-like morphology and is deposited on ITO conductive glass is obtained in a short period of time, and then tests of X-ray powder diffraction, field emission scanning electron microscopy representation and a discharging experiment in an alkaline solution are conducted on the deposited AgCuO2 thin film electrode. The method has the beneficial effects that the used raw materials are low in cost, equipment is simple, operation is easy, convenient and fast, and meanwhile the environmental friendliness is achieved.

Description

technical field [0001] The invention relates to a cathode material AgCuO prepared by anodic oxidation electrodeposition 2 The method belongs to the technical field of inorganic electrode material preparation technology. Background technique [0002] AgCuO 2 It is a material with a layered crystal structure. There is a phenomenon of charge delocalization between its atoms, and some Cu presents a special valence state of +3. Therefore, it is also a kind of electrode material with good conductivity. It can be used as a cathode material for alkaline secondary batteries, and the charge and discharge time can be less than 29 seconds. [0003] So far, AgCuO 2 The preparation is mainly through the precursor Ag 2 Cu 2 o 3 It is obtained by chemical oxidation (ozone, persulfate, etc.) or electrochemical oxidation, so it is necessary to prepare the precursor Ag 2 Cu 2 o 3 , and then oxidized to give the product AgCuO 2 , however, by anodic electrodeposition from the correspon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D9/06H01M4/48H01M4/54
CPCC25D9/06H01M4/48H01M4/54Y02E60/10
Inventor 刘润芦琴燕
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com