Water-based high-adhesion diving joint priming paint as well as preparation method and application thereof
A high-adhesion, grid-seam technology, applied in the field of decorative materials, can solve the problems of poor adhesion of putty, too short drying time, and peeling of the textured paper paint film, so as to improve the decoration effect, excellent permeability, simple craftsmanship
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0071] The raw material formula (wt %) of water-based high-adhesion gap primer is shown in Table 1 below.
[0072] The raw material formula (wt %) of the water-based high-adhesion partition primer of table 1 embodiment 1
[0073]
[0074] The preparation method of water-based high-adhesion grid gap primer may further comprise the steps:
[0075] (1) Stir hydroxyethyl cellulose and 20.0wt% deionized water at a rotating speed of 1200rpm, mix and dissolve to obtain solution A; mix 50.0wt% wetting and dispersing agent, 50.0wt% multifunctional additive and 30.0 Wt% defoamer and solution A were stirred at a speed of 800rpm, and mixed uniformly to obtain solution B; solution B, inorganic pigments, fillers and 50wt% deionized water were stirred at room temperature at a speed of 1500rpm, mixed evenly, and ground Until the particle size of the inorganic pigment and inorganic filler is below 45 μm, slurry C is obtained;
[0076] (2) At a stirring speed of 600rpm, add the remaining w...
Embodiment 2
[0079] The raw material formulation (wt%) of the water-based high-adhesion gap primer is shown in Table 2 below.
[0080] The raw material formula (wt %) of the water-based high-adhesion partition primer of table 2 embodiment 2
[0081]
[0082] The preparation method of water-based high-adhesion grid gap primer may further comprise the steps:
[0083] (1) Stir hydroxyethyl cellulose and 25.0wt% deionized water at a rotating speed of 1100rpm, mix and dissolve to obtain solution A; mix 60.0wt% wetting and dispersing agent, 50.0wt% multifunctional additive and 30.0 Wt% defoamer and solution A were stirred at a speed of 700rpm, and mixed uniformly to obtain solution B; solution B, inorganic pigments, fillers and 40wt% deionized water were stirred at room temperature at a speed of 1400rpm, mixed evenly, and ground Until the particle size of inorganic pigments and fillers is below 45 μm, slurry C is obtained;
[0084] (2) At a stirring speed of 700rpm, add the remaining wettin...
Embodiment 3
[0087] The raw material formulation (wt%) of the water-based high-adhesion grid gap primer is shown in Table 3 below.
[0088] The raw material formula (wt %) of the water-based high-adhesion partition primer of table 3 embodiment 3
[0089]
[0090]
[0091] The preparation method of water-based high-adhesion grid gap primer may further comprise the steps:
[0092] (1) Stir hydroxyethyl cellulose and 30.0wt% deionized water at a rotating speed of 1000rpm, mix and dissolve to obtain solution A; mix 50.0wt% wetting and dispersing agent, 30.0wt% multifunctional additive and 50.0 Wt% defoamer and solution A were stirred at a speed of 600rpm, and mixed uniformly to obtain solution B; solution B, inorganic pigments, fillers and 40wt% deionized water were stirred at room temperature at a speed of 1200rpm, mixed evenly, and ground Until the particle size of inorganic pigments and fillers is below 45 μm, slurry C is obtained;
[0093] (2) At a stirring speed of 800rpm, add the...
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
minimum film forming temperature | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com