Preparation method of bamboo chips for weaving bamboo crafts
The technology of bamboo handicrafts and bamboo chips, which is applied in the field of bamboo product manufacturing, can solve the problems of personal safety hazards, easy breakage, and lack of flexibility of the staff, and achieve the effects of reducing production costs, prolonging service life, and improving utilization rate.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0028] The invention provides a kind of preparation method of bamboo chips for weaving bamboo handicrafts, comprising the following steps:
[0029] Step 1. Put the bamboo tube into the first soaking solution, and soak once at a temperature of 50° C. to 60° C. for 1 to 2 days; the first soaking solution is used for mold prevention, anticorrosion and insecticide.
[0030] Step 2, freezing the bamboo tube after soaking once; the freezing treatment can increase the strength of the bamboo material and prolong the service life.
[0031] Step 3, placing the frozen bamboo tubes in the second soaking liquid, and soaking for a second time at a temperature of 50° C. to 60° C. for 1 hour to 3 hours to obtain bamboo slices. The second soaking liquid is used to soften and lubricate the bamboo to make it more stable. The combined effect of the three steps can make the bamboo material have good flexibility, no insects, suitable for weaving various handicrafts, and the service life of the wea...
Embodiment 1
[0043] The preparation method of bamboo chips for weaving bamboo handicrafts comprises the steps:
[0044] A. Put the bamboo tube into the first soaking solution prepared by mixing hydrochloric acid, sodium chloride, and water in a ratio of 2:1:20 according to the mass ratio, and heat to 50° C. for soaking for 2 days;
[0045] B. Take out the bamboo tube soaked in step A and put it in the cold storage, and freeze it at -10°C for 15 minutes;
[0046] C. Take out the frozen bamboo tube in step B and put it into the second soaking solution prepared by mixing absolute ethanol, sulfur, zinc stearate and water in a ratio of 2:1:4:20 according to the mass ratio, and heat Soak at 60°C for 1 hour;
[0047] D. Take out the bamboo tube soaked in step C, rinse with water, and dry;
[0048] E. Open the bamboo tube dried in step D and shape it.
[0049] After testing, the hardness of the bamboo chips treated in this embodiment is 18HB.
Embodiment 2
[0051] The preparation method of bamboo chips for weaving bamboo handicrafts comprises the steps:
[0052] A. put the bamboo tube into the first soaking solution prepared by mixing hydrochloric acid, sodium chloride, and water in a ratio of 2:1:20 according to the mass ratio, and heat to 60° C. for soaking for 2 days;
[0053] B. Take out the bamboo tube soaked in step A and put it in the cold storage, and freeze it at -5°C for 20 minutes;
[0054] C. Take out the frozen bamboo tube in step B and put it into the second soaking solution prepared by mixing absolute ethanol, sulfur, zinc stearate and water in a ratio of 2:1:4:20 according to the mass ratio, and heat Soak at 60°C for 2 hours;
[0055] D. Take out the bamboo tube soaked in step C, rinse with water, and dry;
[0056] E. Open the bamboo tube dried in step D and shape it.
[0057] After testing, the hardness of the bamboo chips treated in this embodiment is 18HB.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com