A compound, its preparation method and its application in lithium ion secondary battery

A technology of composites and lithium compounds, applied in the field of Si-O-C-Li composites, can solve problems such as difficult processing and inability to use in batches, and achieve the effects of stable structure, improved cycle life, and avoiding agglomeration problems

Active Publication Date: 2021-01-05
BTR NEW MATERIAL GRP CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the generated lithium silicate phase has not undergone secondary treatment, showing strong alkalinity, difficult to process in the later stage, and cannot be used in batches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A compound, its preparation method and its application in lithium ion secondary battery
  • A compound, its preparation method and its application in lithium ion secondary battery
  • A compound, its preparation method and its application in lithium ion secondary battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] SiO with a carbon coating on the surface x (x=0.95) 50g, lithium source LiNH 2 12.5g was dispersed at a high speed until uniformly mixed; then placed in an argon atmosphere for heat treatment at 500°C for 2 hours, cooled naturally to room temperature to take out the composite, and then removed impurities by impregnation and dried to obtain a surface-treated composite.

[0082] image 3 It is the SEM picture of the compound obtained in this embodiment. It can be seen from the figure that the dark area formed by the nano-silicon inlaid lithium-containing compound is uniformly distributed in the particles, forming an island with the nano-silicon inlaid lithium-containing compound as an island. Island structure for the sea.

Embodiment 2

[0084] SiO with a carbon coating on the surface x (x=0.95) 500g, lithium source Li 2 CO 3 125g was dispersed at a high speed until uniformly mixed; then placed in an argon atmosphere for heat treatment at 500°C for 2 hours, cooled naturally to room temperature to take out the composite, and then removed impurities by impregnation and dried to obtain a surface-treated composite.

Embodiment 3

[0086] Take SiO with a carbon coating on the surface x (x=0.95) 50g, lithium source metal lithium powder 10.8g were mixed under vacuum for 3h; then placed in an argon atmosphere for heat treatment at 500°C for 2h, cooled naturally to room temperature to take out the composite, and then removed impurities by impregnation and dried , to obtain a surface-treated composite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite, which comprises nano-silicon, lithium-containing compound and carbon coating, or comprises nano-silicon, silicon oxide, lithium-containing compound and carbon coating. The method of the present invention comprises: (1) mixing carbon-coated silicon oxide with a lithium source in a solid state; (2) heat-treating the pre-lithium precursor obtained in step (1) in a vacuum or a non-oxidizing atmosphere to obtain a composite . The method of the present invention is simple, has low requirements on equipment, and is low in cost. The structure of the obtained composite is stable, and the structure and properties will not be deteriorated after long-term storage. Coulombic efficiency and good cycle performance, the charge capacity is above 1920mAh / g, the discharge capacity is above 1768mAh / g, and the first effect is above 90.2%.

Description

technical field [0001] The invention belongs to the field of negative electrode materials for lithium ion batteries, and relates to a composite, its preparation method and application, in particular to a Si-O-C-Li composite, its preparation method and its application in lithium ion secondary batteries. Background technique [0002] Lithium-ion secondary batteries are widely used in portable electronic products, electric vehicles and energy storage. However, at the first charge, the electrolyte is unstable to form an SEI film on the electrode surface, which consumes a large amount of lithium, resulting in low initial Coulombic efficiency. In the first cycle of graphite, 5-20% of the lithium is used to form the SEI film, while Si, Sn, and SiOx need to consume 20-50% of the lithium. In this regard, researchers have made a series of optimized designs, such as preparing nanowires, porous nanostructures and carbon coatings. Although the cycle performance is improved, the contact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/48H01M4/58H01M4/587H01M10/0525B82Y30/00
CPCH01M4/366H01M4/386H01M4/483H01M4/5825H01M4/587H01M10/0525B82Y30/00H01M4/364H01M2004/027H01M4/625H01M4/1391H01M4/1397H01M4/0471Y02E60/10H01M4/62H01M10/052C01B32/05C01B32/158C01B32/182C01B33/021C01B33/113B82Y40/00C01P2004/80C01P2006/40C01B33/025C01B33/12C01P2004/03C01P2006/12H01M4/131H01M4/485
Inventor 庞春雷屈丽娟任建国岳敏
Owner BTR NEW MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com