Preparation method of anatase type titanium dioxide
An anatase-type titanium dioxide, anatase-type technology, applied in the direction of titanium dioxide, titanium oxide/hydroxide, nanotechnology, etc., can solve the problem of not being able to prepare high-purity anatase-type titanium dioxide, and achieve a controllable particle size range and production The effect of low cost and simple operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0017] The invention provides a kind of preparation method of anatase type titanium dioxide, comprises the following steps:
[0018] a. Preheat oxygen to 850-1050°C through a preheating furnace, and preheat titanium tetrachloride to 750-950°C through another preheating furnace under the protection of nitrogen or argon;
[0019] b. Pass the oxygen preheated in step a and titanium tetrachloride into the reactor at a molar ratio of 2-15:1 at a speed of 0.2-0.4m / s to react, and control the reaction temperature to 850-1050°C , the reaction time is 2-15s; after the reaction, anatase TiO is collected 2 .
[0020] The present invention prepares anatase TiO 2 The key is to preheat the oxygen and titanium tetrachloride gas first, so that the reaction can proceed smoothly. The present invention limits the preheating temperature range of the titanium tetrachloride preheater to 750-950°C, and the temperature is lower than 750°C. It cannot be fully carried out, the temperature is too hig...
Embodiment 1
[0024] Embodiment 1 prepares anatase titanium dioxide with the method of the present invention
[0025] To prepare anatase titanium dioxide, the specific operation steps are as follows:
[0026] a. Preheat oxygen to 850°C through a preheating furnace, and preheat titanium tetrachloride to 750°C through another preheating furnace under the protection of nitrogen or argon;
[0027] b. Pass the oxygen preheated in step a and titanium tetrachloride in a molar ratio of 2:1 into the reactor at a speed of 0.2m / s to react, control the reaction temperature to be 850°C, and the reaction time to be 15s; After the reaction, the anatase TiO was collected 2 .
[0028] In embodiment 1, the obtained TiO 2 99.8% pure, anatase TiO 2 Content is 100%, TiO 2 The particle size is 20-300nm, and the particle size is controllable.
Embodiment 2
[0029] Embodiment 2 prepares anatase titanium dioxide with the method of the present invention
[0030] To prepare anatase titanium dioxide, the specific operation steps are as follows:
[0031] a. Preheat oxygen to 1050°C in a preheating furnace, and preheat titanium tetrachloride to 950°C in another preheating furnace under the protection of nitrogen or argon;
[0032] b. Pass the oxygen preheated in step a and titanium tetrachloride in a molar ratio of 15:1 into the reactor at a speed of 0.4m / s to react, control the reaction temperature to be 1050°C, and the reaction time to be 2s; After the reaction, the anatase TiO was collected 2 .
[0033] In embodiment 2, the obtained TiO 2 99.8% pure, anatase TiO 2 Content is 100%, TiO 2 The particle size is 20-300nm, and the particle size is controllable.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap