Production method of ultraviolet-resistant splash-proof environment-friendly umbrella cloth

A technology of anti-ultraviolet and production methods, which is applied in the direction of improved hand-feeling fibers, liquid-repelling fibers, textiles and papermaking, etc. It can solve the problems of poor waterproof effect of polyester umbrella cloth, poor anti-ultraviolet effect, immature waterproof treatment, etc. problem, to achieve the effect of guaranteed UV resistance, excellent UV resistance, and simple and easy production method

Inactive Publication Date: 2017-06-20
张小玲
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But because the polyester fabric itself has the characteristics that creases are prone to occur, the creases are not easy to restore, and the coating adhesion on it is poor and easy to fall off, so the anti-ultraviolet effect of the existing polyester umbrella cloth is not good. At the same time, Due to the immature waterproof treatment of polyester fabrics for umbrellas at present, the waterproof effect of polyester umbrella fabrics is poor; The water repelling effect is still worse than other high-grade umbrella fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of ultraviolet-resistant splash-proof environment-friendly umbrella cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for making an anti-ultraviolet, water-repellent, and environmental-friendly umbrella cloth comprises the following steps:

[0030] Step 1, base fabric treatment: take the polyester base fabric, remove the dust and impurities on the surface of the base fabric, wash with water and dry to shape;

[0031] Step 2, softening and finishing: put water into the cylinder, add 13.2g / L cetyl sultaine and 33g / L ethanol into the water according to the water volume, raise the temperature to 55°C at a rate of 2°C / min, After stirring evenly at 1 min, then add 5 g / L citric acid, stir evenly at a constant temperature of 250 r / min, cool, immerse the polyester base fabric obtained in step 1, dipping and rolling, the rolling rate is 80%;

[0032] Step 3, one-time drying and setting: Dry the polyester base fabric softened and finished in step 2 at a temperature of 130°C and a speed of 35m / min for 2 minutes;

[0033] Step 4, water-repellent finishing: put water into the tank, add 60g...

Embodiment 2

[0037] A method for making an anti-ultraviolet, water-repellent, and environmental-friendly umbrella cloth comprises the following steps:

[0038] Step 1, base fabric treatment: take the polyester base fabric, remove the dust and impurities on the surface of the base fabric, wash with water and dry to shape;

[0039] Step 2, softening and finishing: put water into the tank, add 12.5g / L cetyl sultaine and 30g / L ethanol into the water according to the water volume, raise the temperature to 50°C at a rate of 2°C / min, After stirring evenly at 1 min, add 4 g / L citric acid, stir evenly at a constant temperature of 200 r / min, cool down, immerse the polyester base fabric obtained in step 1, dipping and rolling, and the rolling rate is 80%;

[0040] Step 3, one-time drying and shaping: drying and shaping the polyester base fabric softened and finished in Step 2 at a temperature of 120°C and a speed of 30m / min for 1 minute;

[0041] Step 4, water repellent finishing: put water into the...

Embodiment 3

[0045] A method for making an anti-ultraviolet, water-repellent, and environmental-friendly umbrella cloth comprises the following steps:

[0046] Step 1, base fabric treatment: take the polyester base fabric, remove the dust and impurities on the surface of the base fabric, wash with water and dry to shape;

[0047] Step 2, softening and finishing: put water into the tank, add 14.8g / L cetyl sultaine and 35g / L ethanol into the water according to the water volume, raise the temperature to 60°C at a rate of 2°C / min, After stirring evenly at 1 min, add 6 g / L citric acid, stir evenly at a constant temperature of 300 r / min, cool, immerse the polyester base fabric obtained in step 1, dipping and rolling, and the rolling rate is 80%;

[0048] Step 3, one-time drying and shaping: drying and shaping the polyester base fabric softened and finished in Step 2 at a temperature of 135°C and a vehicle speed of 40m / min for 3 minutes;

[0049] Step 4, water repellent finishing: put water into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production method of an ultraviolet-resistant splash-proof environment-friendly umbrella cloth and belongs to the technical field of umbrella cloth. The production method comprises the following steps: step one, treating base cloth; step two, softening finishing; step three, primary drying and shaping; step four, splash-proof finishing; step five, secondary drying and shaping; and step six, carrying out waterproof ultraviolet-resistant treatment, and drying to obtain the ultraviolet-resistant splash-proof environment-friendly umbrella cloth. The polyester base cloth is subjected to softening finishing, primary drying and shaping treatment, splash-proof finishing, secondary drying and shaping and waterproof ultraviolet-resistant treatment; especially, corresponding finishing solutions and adhesive materials are cooperated in the softening finishing, the splash-proof finishing and the waterproof ultraviolet-resistant treatment and are used for carrying out special treatment on the polyester base cloth, so that the produced polyester umbrella cloth has excellent ultraviolet resistance, water resistance and splash-proof performance; environment-friendly additives are used for treating the polyester base cloth in the production process, so that the produced umbrella cloth is friendly to the human body and the environment.

Description

technical field [0001] The invention belongs to the technical field of umbrella cloth, and in particular relates to a method for making an anti-ultraviolet, water-repellent and environment-friendly umbrella cloth. Background technique [0002] Polyester, also known as polyester fiber, has the advantages of high strength, good elasticity, good wear resistance, and good corrosion resistance. Polyester is widely used in clothing manufacturing, daily necessities manufacturing and industrial product manufacturing. After-finishing the polyester base fabric to endow it with new special functions is a commonly used means to improve the performance of polyester fabrics. [0003] At present, polyester is widely used in umbrella fabrics because of its low cost. Its texture is thicker, it is more reflective, and its color is brighter. Usually, polyester fabrics are post-processed and used as umbrella fabrics. The dual-purpose umbrella cloth is mainly treated with waterproof and anti-ul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/14D06N3/12D06N3/04D06M13/463D06M13/207D06M15/256D06M13/188D06M15/53D06M101/32
CPCD06N3/0036D06M13/188D06M13/207D06M13/463D06M15/256D06M15/53D06M2101/32D06M2200/12D06M2200/50D06N3/0063D06N3/04D06N3/128D06N3/142D06N2209/103D06N2209/128D06N2209/1664D06N2209/1678
Inventor 张小玲