A technology of reconstituting tobacco leaves and ternary compounding, which is applied in the directions of tobacco, application and treatment of tobacco, can solve the problem of low retention rate of fillers, and achieve the effects of improving retention rate, saving energy and improving physical indicators.

Active Publication Date: 2017-06-30
CHINA TOBACCO ZHEJIANG IND
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention aims to provide a method for improving the filler retention rate of reconstituted tobacco leaf products by papermaking method by using diatomite, titanium dioxide and calcium carbonate ternary composite filler, which is used to solve the problem of low filler retention rate in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Tobacco raw materials are sampled according to the mass ratio of tobacco stems: tobacco powder: crushed tobacco leaves at a mass ratio of 5:4:1, the tobacco powder and crushed tobacco leaves are mixed and extracted with water, and the mixed powder material is obtained after extraction; the tobacco stems are extracted with water separately, and the extraction Afterwards, the tobacco stem material is obtained. The extraction process conditions are as follows: the ratio of tobacco raw material to water is 1:6, the pH is 4-6, the extraction temperature is 50°C, and the extraction time is 2-3 hours.

[0046] (2) Solid-liquid separation is performed on the mixed end material, and the separated solid phase material is coarsely ground to make a mixed end slurry; the tobacco stem material is subjected to solid-liquid separation after pre-grinding, and the separated solid phase material is coarsely ground to make Tobacco stem paste. Combining the mixed powder slurry and the ...

Embodiment 2

[0052] (1) Tobacco raw materials are sampled according to the mass ratio of tobacco stems: tobacco powder: crushed tobacco leaves at a mass ratio of 5:4:1, the tobacco powder and crushed tobacco leaves are mixed and extracted with water, and the mixed powder material is obtained after extraction; the tobacco stems are extracted with water separately, and the extraction Afterwards, the tobacco stem material is obtained. The extraction process conditions are as follows: the ratio of tobacco raw material to water is 1:6, the pH is 4-6, the extraction temperature is 50°C, and the extraction time is 2-3 hours.

[0053] (2) Solid-liquid separation is performed on the mixed end material, and the separated solid phase material is coarsely ground to make a mixed end slurry; the tobacco stem material is subjected to solid-liquid separation after pre-grinding, and the separated solid phase material is coarsely ground to make Tobacco stem paste. Combine the mixed powder slurry and the to...

Embodiment 3

[0059] (1) Tobacco raw materials are sampled according to the mass ratio of tobacco stems: tobacco powder: crushed tobacco leaves at a mass ratio of 5:4:1, the tobacco powder and crushed tobacco leaves are mixed and extracted with water, and the mixed powder material is obtained after extraction; the tobacco stems are extracted with water separately, and the extraction Afterwards, the tobacco stem material is obtained. The extraction process conditions are as follows: the ratio of tobacco raw material to water is 1:6, the pH is 4-6, the extraction temperature is 50°C, and the extraction time is 2-3 hours.

[0060] (2) Solid-liquid separation is performed on the mixed end material, and the separated solid phase material is coarsely ground to make a mixed end slurry; the tobacco stem material is subjected to solid-liquid separation after pre-grinding, and the separated solid phase material is coarsely ground to make Tobacco stem paste. Combine the mixed powder slurry and the to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
widthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for improving the filler retention rate of a papermaking-method reconstituted tobacco product by employing a ternary composite filler. The method comprises the steps of (1) adding water to tobacco raw materials for extraction separately; (2) carrying out solid-liquid separation on the extracted materials separately, treating solid-phase materials through a pulping technology to prepare solid-phase slurry, combining the solid-phase slurry, adding the ternary composite filler and carrying out papermaking through a headbox to prepare a reconstituted tobacco substrate, combining various water-phase materials and then carrying out purification and concentration to prepare a coating liquid; and (3) coating the reconstituted tobacco substrate with the coating liquid, drying with an oven, perfuming with a drying cylinder and finally slicing to prepare the reconstituted tobacco product. According to the method, the retention rate of the filler in the reconstituted tobacco product can be improved, so that the physical property, the liquid absorption performance, the appearance performance and the like of the reconstituted tobacco are improved and the smoking quality of the substrate is improved.

Description

technical field [0001] The invention relates to the field of papermaking reconstituted tobacco leaves, in particular to a method for improving the filler retention rate of papermaking reconstituted tobacco products by using diatomite, titanium dioxide and calcium carbonate ternary composite fillers. Background technique [0002] Paper-process reconstituted tobacco (Paper-process reconstituted tobacco), also known as tobacco sheet, is a kind of "artificial tobacco leaf" made by processing tobacco by-products and waste materials using modern extraction and separation technology and improved papermaking technology, also known as papermaking. The reconstituted tobacco leaf is mainly made of tobacco pulp made from waste materials in tobacco processing such as tobacco stems, shredded tobacco and tobacco powder, mixed with a certain amount of wood pulp and fillers, and then copied into a substrate by a paper machine and then dipped and coated. have to. [0003] Reconstituted tobac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A24B15/12A24B15/18
CPCA24B15/12A24B15/18
Inventor 戴路周国俊卢昕博史春云徐建詹望成胡雅军杨艳芹智锁红赵路灿尹洁杨洋
Owner CHINA TOBACCO ZHEJIANG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap