Antiskid wear-resistant mat and manufacture method thereof

A technology for floor mats and substrate layers, applied in the direction of carpets, etc., can solve the problems of easy wear and slip, and achieve the effects of good wear resistance, good strength and stable quality

Inactive Publication Date: 2017-06-30
广东雅丽斯佳新材料有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the PVC floor mats currently on the market generally have the defects of being easy to slip and wear.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of non-slip wear-resisting mat, comprises PVC base material layer and the thread braiding layer that is attached to the upper surface of PVC base material layer, and described PVC base material layer comprises the raw material of following weight portion:

[0052] PVC resin 80 parts

[0053] Plasticizer 25 parts

[0054] Filler 25 parts

[0055] Stabilizer 2 parts

[0056] Impact modifier 5 parts

[0057] Wear-resistant modifier 4 parts

[0058] Anti-slip agent 3 parts

[0059] Lubricant 0.8 parts.

[0060] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin at a weight ratio of 1:1.

[0061] The plasticizer is a mixture composed of diisononyl cyclohexane 1,2-dicarboxylate, dioctyl adipate and epoxidized soybean oil in a weight ratio of 1.5:0.8:1.

[0062] The filler is nano-active calcium carbonate with a particle size of 10 nm and treated with a silane coupling agent.

[0063] The stabilizer is composed of calcium la...

Embodiment 2

[0081] A kind of non-slip wear-resisting mat, comprises PVC base material layer and the thread braiding layer that is attached to the upper surface of PVC base material layer, and described PVC base material layer comprises the raw material of following weight portion:

[0082] PVC resin 85 parts

[0083] Plasticizer 28 parts

[0084] Filler 28 parts

[0085] Stabilizer 3 parts

[0086] Impact modifier 6 parts

[0087] Wear-resistant modifier 5 parts

[0088] Anti-slip agent 3.5 parts

[0089] Lubricant 0.9 parts.

[0090] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin at a weight ratio of 1:1.2.

[0091] The plasticizer is a mixture composed of diisononyl cyclohexane 1,2-dicarboxylate, dioctyl adipate and epoxidized soybean oil in a weight ratio of 1.8:0.9:1.

[0092] The filler is nano-active calcium carbonate with a particle size of 20nm and treated with a silane coupling agent.

[0093] The stabilizer is composed of calci...

Embodiment 3

[0111] A kind of non-slip wear-resisting mat, comprises PVC base material layer and the thread braiding layer that is attached to the upper surface of PVC base material layer, and described PVC base material layer comprises the raw material of following weight portion:

[0112] PVC resin 90 parts

[0113] 30 parts plasticizer

[0114] Filling agent 30 parts

[0115] Stabilizer 4 parts

[0116] Impact modifier 7 parts

[0117] Wear-resistant modifier 6 parts

[0118] Anti-slip agent 4 parts

[0119] Lubricant 1 part.

[0120] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin in a weight ratio of 1:1.5.

[0121] The plasticizer is a mixture composed of diisononyl cyclohexane 1,2-dicarboxylate, dioctyl adipate and epoxidized soybean oil in a weight ratio of 2:1:1.

[0122] The filler is nano-active calcium carbonate with a particle size of 30nm and treated with a silane coupling agent.

[0123] The stabilizer is composed of calcium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a mat, specifically to an antiskid wear-resistant mat and a manufacture method thereof. The antiskid wear-resistant mat includes a PVC substrate layer and a silk thread weaved layer attached to the upper surface of the PVC substrate layer. The PVC substrate layer includes the following raw materials, by weight part, 80-100 parts of a PVC resin, 25-35 parts of a plasticizer, 25-35 parts of a filler, 2-6 parts of a stabilizer, 5-9 parts of an impact modifier, 4-8 parts of a wear-resistant modifier, 3-5 parts of an antiskid agent, and 0.8-1.2 parts of a lubricant. The mat is good in wear resistance and skid resistance, is eco-friendly and non-toxic, and is excellent in strength, toughness, flame resistance, aging resistance and comprehensive properties.

Description

technical field [0001] The invention relates to the technical field of floor mats, in particular to a non-slip and wear-resistant floor mat and a preparation method thereof. Background technique [0002] With the development of economic construction, people's living standards are also constantly improving. There will be some floor mats in people's rooms and cars, and the floor mats are used to isolate the coldness of the ground. Traditional carpet mats are generally difficult to clean, not easy to dry after cleaning, and have the defects of mold and smell, which bring many changes to the use. At present, a new kind of PVC floor mat has appeared on the market. This kind of floor mat is almost completely made of PVC material, which is easy to clean and easy to dry. However, PVC floor mats on the market generally have the defects of being easy to slip and wear. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L9/06C08L7/00C08L23/30C08L91/00C08L21/00C08K13/06C08K9/06C08K3/26C08K5/103C08K5/20C08K5/11C08K3/34C08K7/20C08K3/22C08K3/38A47G27/02
CPCC08L27/06A47G27/0281C08K2201/003C08K2201/011C08K2201/014C08L2201/02C08L2205/025C08L2205/035C08L2205/06C08L2205/08
Inventor 徐祥林罗恺青
Owner 广东雅丽斯佳新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com