A kind of preparation method of mesoporous Y-type molecular sieve

A molecular sieve and mesoporous technology, applied in the direction of crystalline aluminosilicate zeolite, octahedral crystalline aluminosilicate zeolite, etc., can solve the problems of limited application range and long process, and achieve the goal of improving environmental protection efficiency, reducing consumption, and simple process Effect

Active Publication Date: 2019-09-24
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above method has a long process and the scope of application is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of mesoporous Y-type molecular sieve
  • A kind of preparation method of mesoporous Y-type molecular sieve
  • A kind of preparation method of mesoporous Y-type molecular sieve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] According to 1Al 2 o 3 : 15SiO 2 : 16Na 2 O: 320H 2 O molar ratio, 8.2g NaOH was added to 55ml deionized water, stirred to a clear solution, 3.0g sodium metaaluminate was added to the above solution, then 35.8g water glass (modulus 2.5) was added, and the stirring was continued at room temperature until All dissolved, and then aged at 30°C for 20 hours to obtain the directing agent.

[0037] Treat NaY molecular sieves in glycerol at 190°C for 2 hours, the mass mixing ratio of Y molecular sieves and glycerin is 1:5, and then treat the obtained glycerin mixture, inorganic directing agent and N,N-dimethyl-N-[3 -(trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxyethyl cellulose pre-mixed solution with a degree of polymerization of 1500 were mixed at 80°C for 1 hour, Y-type molecular sieve, inorganic directing agent and N,N— The mass mixing ratio of dimethyl-N-[3-(trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxymethyl cellulos...

Embodiment 2

[0048] According to 1Al 2 o 3 : 15SiO 2 : 16Na 2 O: 320H 2 O molar ratio, 8.2g NaOH was added to 55ml deionized water, stirred to a clear solution, 3.0g sodium metaaluminate was added to the above solution, then 35.8g water glass (modulus 2.5) was added, and the stirring was continued at room temperature until All dissolved, and then aged at 30°C for 20 hours to obtain the directing agent.

[0049] Treat NaY molecular sieves in glycerin at 200°C for 2 hours, the mass mixing ratio of Y molecular sieves and glycerin is 1:4, and then treat the obtained glycerin mixture, inorganic directing agent and N,N-dimethyl-N-[3 -(Trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxymethyl cellulose pre-mixed solution with a degree of polymerization of 200 were mixed at 80°C for 1 hour, Y-type molecular sieve, inorganic directing agent and N,N— The mass mixing ratio of dimethyl-N-[3-(trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxymethyl cellulos...

Embodiment 3

[0053] According to 1Al 2 o 3 : 15SiO 2 : 16.5Na 2 O: 320H 2 O molar ratio, 9.4g of water glass (modulus 3.3) was added to 6.9g of sodium metaaluminate solution, stirred to dissolve, and then aged at 45°C for 5 hours to obtain the directing agent.

[0054] Treat NaY molecular sieves in glycerin at 190°C for 2 hours. The mass mixing ratio of Y molecular sieves and glycerin is 1:6. -(trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxymethyl cellulose pre-mixed solution with a degree of polymerization of 500 were mixed at 80°C for 1 hour, Y-type molecular sieve, inorganic guiding agent and N,N— The mass mixing ratio of dimethyl-N-[3-(trimethoxysilyl)propyl]octadecyl ammonium chloride, ethanol and carboxymethyl cellulose is 1:0.2:0.3:5:0.5, and then sealed Treat the mixture at 100°C for 12 hours in a reaction kettle, filter the mixture, wash with water, and dry at 100°C for 5 hours, and then roast it at 550°C for 5 hours to obtain a molecular sieve sample,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
full width at half maximumaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

A preparation method of a mesoporous Y-type molecular sieve is characterized by comprising: mixing a Y-type molecular sieve with glycerol at 150-200 DEG C for 0.5-5 h, mixing the obtained glycerol treated liquid mixture with an inorganic guiding agent, a quaternary ammonium compound, ethanol and cellulose at 30-80 DEG C for 0.5-2 h, placing the mixture in a reactor, treating at 80-120 for 2-20 hours, and recycling the product to obtain the mesoporous Y-type molecular sieve, wherein the mass ratio of the Y-type molecular sieve to the glycerol is 1:(2-15), and the mass ratio of the Y-type molecular sieve to the inorganic guiding agent, quaternary ammonium compound, ethanol and cellulose is 1:(0.1-10):(0.02-1):(0.1-10):(0.005-1).

Description

technical field [0001] The invention relates to a method for preparing a mesoporous Y-type molecular sieve, and more specifically relates to a method for modifying a Y-type molecular sieve to obtain a mesoporous Y-type molecular sieve. Background technique [0002] Y-type molecular sieves (HY, REY, USY) have been the main active components of catalytic cracking (FCC) catalysts since they were first used in the 1960s. However, with the intensification of heavy crude oil, the content of polycyclic compounds in FCC feedstock increased significantly, but its diffusion capacity in zeolite channels decreased significantly. In order to overcome the defects of conventional microporous molecular sieves, reducing the crystal size of molecular sieves and introducing mesopores into molecular sieve crystals can effectively improve their diffusion properties. Compared with traditional microporous molecular sieves, mesoporous molecular sieves have excellent internal and external diffusion...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/24
Inventor 李文林达志坚罗一斌郑金玉
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com