Method utilizing camellia oleifera shells to prepare plant fiber-based particle board and particle board

A technology of camellia oleifera husk and plant fiber, which is applied in the pretreatment, application, and household components of molding materials, and can solve problems such as environmental pollution, waste of resources, discarding or incineration of camellia oleifera husk

Inactive Publication Date: 2017-07-14
CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the current situation that Camellia oleifera husks are often discarded or incinerated, causing pollution to the environment and wasting resources, the present invention provides a highly efficient and brand-new utilization method, ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method utilizing camellia oleifera shells to prepare plant fiber-based particle board and particle board
  • Method utilizing camellia oleifera shells to prepare plant fiber-based particle board and particle board
  • Method utilizing camellia oleifera shells to prepare plant fiber-based particle board and particle board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The method for preparing plant fiber-based particle board by utilizing camellia oleifera husk of the present embodiment comprises:

[0028] (1) According to the liquid-solid ratio of 1:10, mix the NaOH solution with a concentration of 2% and the camellia oleifera husk fragments with a diameter of 3mm to 5mm. The pretreatment time is 1h, and the camellia oleifera husk is washed repeatedly until it becomes neutral. After filtering out the moisture in a ventilated place, dry it in an oven at 103°C for subsequent use; (2) after selecting and removing impurities, use the phenolic glue quality as 16% of the quality of the camellia oleifera husk obtained after pretreatment to sizing, and mix evenly (3) Lay the camellia oleifera husk obtained by sizing in the mold, under hot pressing pressure 4MPa, preset density is 0.8 g / m 3 , under the condition of hot pressing temperature of 170° C., hot pressing for 12 minutes to obtain plant fiber-based particle board.

[0029] The perfor...

Embodiment 2

[0034] The method for preparing plant fiber-based particle board by utilizing camellia oleifera husk of the present embodiment comprises:

[0035] (1) Use microwave radiation to pretreat the camellia oleifera shell. Before the pretreatment, soak the camellia oleifera shell in water for 24 hours, the radiation power is 5kW, and the radiation time is 50s; Sizing 16% of the quality of the camellia oleifera shell obtained after pretreatment, and mixing uniformly; (3) laying the camellia oleifera shell obtained by sizing in a mould, at a hot pressing pressure of 4MPa, and a preset density of 0.8g / m 3 , under the condition of hot pressing temperature of 170° C., hot pressing for 12 minutes to obtain plant fiber-based particle board.

[0036] The performance of the prepared plant fiber-based particle board was tested, and the results are shown in Table 2.

[0037] Table 2: Performance test results of the plant fiber-based particle board prepared by the method of Example 2

[0038...

Embodiment 3

[0040] The method for preparing plant fiber-based particle board by utilizing camellia oleifera husk of the present embodiment comprises:

[0041](1) Soak the camellia oleifera husk in hot water at 70°C for 60 minutes; (2) after selection and removal of impurities, use urea-formaldehyde glue as 16% of the quality of the camellia oleifera husk obtained after pretreatment, and mix well ; (3) Spread the Camellia oleifera husk obtained by sizing in the mould, under hot pressing pressure 4MPa, preset density is 0.8g / m 3 , under the condition of hot pressing temperature of 130° C., hot pressing for 12 minutes to obtain plant fiber-based particle board.

[0042] The performance of the prepared plant fiber-based particle board was tested, and the results are shown in Table 3.

[0043] Table 3: The performance test results of the plant fiber-based particle board prepared by the method of Example 3

[0044]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Static bending strengthaaaaaaaaaa
Elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a plant fiber-based particle board and a preparation method of the plant fiber-based particle board. Before gluing, camellia oleifera shells are pretreated, the pretreated camellia oleifera shells are mixed with glues evenly and then horizontally laid in a mould to be formed in a hot pressing mode, and the plant fiber-based particle board is obtained. The plant fiber-based particle board is good in mechanical performance, the static bending strength is 1.49 MPa-3.5 MPa, the elastic modulus is 383 MPa-530 MPa, and the internal bonding strength is 0.31 MPa-1.02 MPa. Compared with other biomass materials, the used camellia oleifera shells have the characteristics of being low price, reproducible, rich and intensive in yield and the like. The used overall working procedure is short, the method is simple, and the method has special significance for improving the high quality utilization way of camellia oleifera shell resources and relieving the current situation that forest resources are deficient.

Description

technical field [0001] The invention belongs to the field of utilization of agricultural and forestry wastes, in particular to the field of utilization of camellia oleifera husks, and in particular relates to a method for preparing plant fiber-based particle boards by using oleifera oleifera husks. Background technique [0002] Plant fiber-based particle board refers to a new type of composite material with special microstructure and properties prepared by compounding woody or plant raw materials with other materials. In the middle of the 20th century, the rapid growth of the global economy and the population explosion caused unprecedented burdens on the earth. The development of "low-carbon economy" has become the development theme of the international community. Facing the growing development needs of human society, single wood products or wooden materials As a result, the shortage of supply in the market has intensified, and the reserves of forest resources have plummeted...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27N3/02B27N3/10B27N3/08B27N1/00B27N1/02
CPCB27N3/02B27N1/00B27N1/02B27N3/08B27N3/10
Inventor 胡进波苌姗姗胡嘉裕刘元彭开元陈桂华
Owner CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap