Nano-carbon molecular high-performance lubricating oil

A nano-carbon, high-performance technology, applied in the direction of lubricating composition, petroleum industry, etc., can solve the problems of poor dispersion stability of nano-solid lubricating materials, large-scale, high-efficiency application restrictions, and easy to cause adhesion, etc., to achieve suitable for large-scale Large-scale industrial application, excellent dispersion stability, and the effect of not easy to adhere

Inactive Publication Date: 2017-07-18
方珺
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, these nano solid lubricating materials have the disadvantages of poor dispersion stability, insufficient heat resistance, and easy adhesion, etc., which

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Accurately weigh 80 parts of mineral oil, 50 parts of engine oil, 25 parts of trimethylolpropane oleate, 20 parts of hydrogenated rosin glyceride, 10 parts of nano-polytetrafluoroethylene, 10 parts of acrylic resin, p-hydroxybenzene 8 parts of propyl formate, 8 parts of cetyl alcohol, 7 parts of nano carbon, 7 parts of alkoxy phosphate, 6 parts of acetyl tributyl citrate, 5 parts of hydroxybenzotriazole, high alkali value sulfurized alkyl phenate calcium 3 parts, 2 parts of methyl 4-bromo-5-azaindole-2-carboxylate, 1 part of diisobutene, 3 parts of octadecyltriethoxysilane. The particle size of the nano-carbon is 5 nm.

[0022] (1) Mix and stir mineral oil, machine oil, trimethylolpropane oleate, hydrogenated rosin glyceride, and nano-polytetrafluoroethylene, transfer to a reaction kettle, heat up to 220°C, stir for 35 minutes, and cool to At room temperature, add acrylic resin, propyl p-hydroxybenzoate, cetyl alcohol, nano-carbon, acetyl tributyl citrate, ultrasonical...

Embodiment 2

[0027] Accurately weigh 85 parts of mineral oil, 55 parts of engine oil, 30 parts of trimethylolpropane oleate, 25 parts of hydrogenated rosin glyceride, 12 parts of nano-polytetrafluoroethylene, 11 parts of acrylic resin, p-hydroxybenzene 9 parts of propyl formate, 9 parts of cetyl alcohol, 8 parts of nano carbon, 8 parts of alkoxy phosphate, 7 parts of acetyl tributyl citrate, 6 parts of hydroxybenzotriazole, high alkali value sulfurized alkyl phenate calcium 4 parts, 3 parts of methyl 4-bromo-5-azaindole-2-carboxylate, 2 parts of diisobutene, 4 parts of aminopropyltrimethoxysilane. The particle size of the nano-carbon is 15 nm.

[0028] (1) Mix mineral oil, engine oil, trimethylolpropane oleate, hydrogenated rosin glyceride, and nano-polytetrafluoroethylene, mix and stir evenly, transfer to a reaction kettle, heat up to 235°C, stir for 40 minutes, and cool to At room temperature, add acrylic resin, propyl p-hydroxybenzoate, cetyl alcohol, nano-carbon, acetyl tributyl citra...

Embodiment 3

[0033] Accurately weigh 90 parts of mineral oil, 60 parts of engine oil, 35 parts of trimethylolpropane oleate, 30 parts of hydrogenated rosin glyceride, 15 parts of nano-polytetrafluoroethylene, 12 parts of acrylic resin, p-hydroxybenzene 10 parts of propyl formate, 10 parts of cetyl alcohol, 9 parts of nano carbon, 9 parts of alkoxy phosphate, 8 parts of acetyl tributyl citrate, 7 parts of hydroxybenzotriazole, high alkali value sulfurized alkyl phenate calcium 5 parts, 4 parts of methyl 4-bromo-5-azaindole-2-carboxylate, 3 parts of diisobutene, and 5 parts of chloropropyltriethoxysilane. The particle size of the nano-carbon is 25 nm.

[0034] (1) Mix mineral oil, engine oil, trimethylolpropane oleate, hydrogenated rosin glyceride, and nano-polytetrafluoroethylene, mix and stir evenly, transfer to a reaction kettle, heat up to 250°C, stir for 45 minutes, and cool to At room temperature, add acrylic resin, propyl p-hydroxybenzoate, cetyl alcohol, nano-carbon, acetyl tributyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nano-carbon molecular high-performance lubricating oil. The lubricating oil is prepared by taking mineral oil, engine oil, trimethylolpropane trioleate and glycerol ester of hydrogenated rosin as main ingredients and adding nano polytetrafluoroethylene, acrylic resin, propyl p-hydroxybenzoate, cetyl alcohol, nano-carbon, alkoxyl phosphate, acetyl tributyl citrate, hydroxybenzotriazole, overbased sulfurized calcium alkyl phenolate, methyl 4-bromo-5-azaindole-2-carboxylate, diisobutylene and surface modifier through heating stirring, ultrasonic dispersion, heating insulating, defoaming, mechanical shearing and other processes. Therefore, the lubricating oil has excellent dispersion stability and heat resistance, does not easily cause adhesion, can meet the requirement of industry, and has a relatively good application prospect.

Description

technical field [0001] The invention relates to the technical field of lubricating oil processing, in particular to a high-performance lubricating oil with nanometer carbon molecules. Background technique [0002] Lubricating oil is a liquid or semi-solid lubricant used in various types of automobiles and mechanical equipment to reduce friction and protect machinery and processed parts. It mainly plays the roles of lubrication, auxiliary cooling, rust prevention, cleaning, sealing and buffering. Lubricating oil generally consists of two parts: base oil and additives. Base oil is the main component of lubricating oil, which determines the basic properties of lubricating oil. Additives can make up for and improve the performance of base oil, endow some new properties, and are an important part of lubricating oil. [0003] In recent years, due to the unique physical, chemical and mechanical properties of nano solid lubricating materials, the industry has developed them into va...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10N30/04C10N30/08C10N10/04
CPCC10M169/044C10M2201/041C10M2203/024C10M2203/1006C10M2207/021C10M2207/2805C10M2207/2835C10M2207/289C10M2207/30C10M2209/082C10M2213/062C10M2215/223C10M2219/089C10M2223/04C10M2227/04C10N2010/04C10N2030/04C10N2030/08
Inventor 方珺
Owner 方珺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap