High-reflection low-transmittance polycarbonate material and preparation method thereof

A polycarbonate, high-reflection technology, applied in the field of polymer modified materials, can solve problems such as light reflection that have not been studied, and achieve excellent reflection and shading effects, light transmittance reduction, and excellent light reflectance effects

Active Publication Date: 2017-08-01
HEFEI GENIUS NEW MATERIALS
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent application No. 201010224699.1 is limited to LED lamp shades, and only discusses the light transmission performance, does not study the reflection of light, and uses the traditional extrusion granulation processing method to deal with the problem
At the same time, the prior art only discloses the light-shielding explanation of thicker products (for example, the invention patent of Chinese patent application number 201310267948.9 is a light-shielding material with a thickness of 2 millimeters, and the invention patent with a Chinese patent application number of 201310449220.8 is the thinnest light-shielding material with a thickness of 1 millimeter. )

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 70 parts of PC2407, 5 parts of M511, 10 parts of superfine barium sulfate and fine calcium carbonate mixture (weight ratio = 2:1), 10 parts of R-760, 2 parts of heat stabilizer, 2 parts of light stabilizer (LA -944 1.2 parts, UV-360 0.8 parts), 1 part of lubricant, mixed evenly by high-speed stirring, the above-mentioned mixture is sent into the internal mixer, fully melted and mixed under the stirring and shearing action of the rotor, and then pressed The film machine is pressed into 2 mm thin slices, and then cut into pellets with a cutter.

[0048] The internal mixer temperature is 240° C., and the internal mixer rotor speed is 75 rpm.

[0049] The prepared material was injection molded into a standard sample bar for testing according to the standard size, and the performance test results are shown in Table 2.

Embodiment 2

[0055] 75.8 parts of PC2407, 10 parts of M511, 3 parts of superfine barium sulfate and fine calcium carbonate mixture (the weight ratio of the two = 2:1), 10 parts of R-760, 0.5 parts of heat stabilizer, 0.5 parts of light stabilizer (LA -944 0.3 parts, UV-360 0.2 parts), 0.2 parts of lubricants were mixed evenly by high-speed stirring, and the above mixture was sent into the internal mixer, fully melted and mixed under the stirring and shearing action of the rotor, and then pressed The film machine is pressed into 2 mm thin slices, and then cut into pellets with a cutter.

[0056] The internal mixer temperature is 280° C., and the internal mixer rotor speed is 75 rpm.

[0057] The prepared material was injection molded into a standard sample bar for testing according to the standard size, and the performance test results are shown in Table 3.

Embodiment 3

[0063] 76.8 parts of PC2407, 10 parts of M511, 10 parts of ultra-fine barium sulfate, 2 parts of R-760, 0.5 parts of heat stabilizer, 0.5 parts of light stabilizer (LA-944 0.3 parts, UV-360 0.2 parts), lubricant 0.2 The parts are mixed evenly by high-speed stirring, and the above-mentioned mixture is sent into the internal mixer, fully melted and mixed under the stirring and shearing action of the rotor, and then pressed into 2 mm thin slices by a film press machine, and then cut into granules with a cutter. material.

[0064] The temperature of the internal mixer is 260° C., and the rotational speed of the rotor of the internal mixer is 75 rpm.

[0065] The prepared material was injection molded into a standard sample bar for testing according to the standard size, and the performance test results are shown in Table 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer modified materials and relates to a high-reflection low-transmittance polycarbonate material and a preparation method thereof. The material is prepared from the following ingredients in parts by weight: 70 to 76.8 parts of polycarbonate, 5 to 10 parts of flexibilizer, 3 to 10 parts of light diffusion agent, 2 to 10 parts of light blocking agent, 0.5 to 2 parts of heat stabilizer, 0.5 to 2 parts of light stabilizer and 0.2 to 1 part of lubricant. The ingredients are evenly mixed and then sent into an internal mixer to be extruded and mixed, then are compressed into 1 to 5-millimeter slices by a laminator and then are cut into a particle material by a cutter. The material has a good and uniform-phase component dispersion effect, has excellent light reflection and low light transmission in thinner work pieces and is suitable for being applied to optical components in the fields of lighting, displaying, automobiles, aviation and the like.

Description

[0001] (1) Technical field [0002] The invention belongs to the technical field of polymer modified materials, and in particular relates to a polycarbonate material with the advantages of high light reflectance, low light transmittance and the like and a preparation method thereof. [0003] (2) Background technology [0004] Polycarbonate (PC for short) is a transparent, amorphous thermoplastic material containing carbonate groups in its molecular chain. Polycarbonate has excellent impact resistance, good mechanical properties and electrical insulation, wide temperature range, good temperature resistance, high dimensional stability and high creep resistance. It is a rigid, hard and tough engineering plastic. Typical materials in one. But also because of its poor crystallization ability, it is an amorphous polymer, so it has excellent transparency. [0005] Due to the increasingly high requirements for light in optical products with high added value such as instrument lampsha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L51/04C08K13/02C08K3/30C08K3/26C08K5/20
CPCC08K2201/005C08L69/00C08L51/04C08K13/02C08K2003/3045C08K2003/265C08K5/20
Inventor 杨桂生高军杨莺李术
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com