High-temperature lining surface repairing material

A surface repair and lining technology, which is applied in the field of refractory materials, can solve the problems that the wear resistance cannot meet the use requirements, the kiln cannot immediately heat up and run, and the wall has poor high temperature resistance, so as to achieve good high temperature wear resistance and high temperature Good corrosion resistance and fast construction

Inactive Publication Date: 2017-08-04
郑州耐都热陶瓷有限公司
View PDF19 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The refractory materials currently used in the past have a long solidification time after repairing, and the kiln cannot immediately heat up and run.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1

[0013] The high-temperature lining surface repair material of the present invention is prepared from the following raw materials in a proportion of parts by mass, with coarse particles of Al 2 O 3 The content of 80% bauxite homogenizing material contains 16 parts of 5-3mm particle size, 22 parts of 3-1mm particle size, 22 parts of brown corundum powder with 1-0mm particle size, Al-85 special grade alum Soil homogenizing material (320 mesh) fine powder 25 parts, active α-Al 2 O 3 5 parts, high-quality silica powder 4 parts, bentonite 2 parts, Guangxi white mud 4 parts, oxalic acid 1 part, explosion-proof fiber powder 0.05 parts; the above raw materials are added to 6 parts aluminum dihydrogen phosphate solution with a specific gravity of 1.47. The first mechanical stirring and mixing, after mixing uniformly, the material is trapped for more than 24 hours, and then the second mechanical stirring, and then adding 8 parts of the same specific gravity of 1.47-1.55 al...

Example Embodiment

[0014] Example 2

[0015] The high-temperature lining surface repair material of the present invention is prepared from the following raw materials in a proportion of parts by mass, with coarse particles of Al 2 O 3 The content of 80% bauxite homogenizing material contains 18 parts of 5-3mm particle size, 20 parts of 3-1mm particle size, 23 parts of brown corundum powder with 1-0mm particle size, Al-85 special grade alum 25 parts of fine powder of soil homogenizing material, active α-Al 2 O 3 5 parts, high-quality silica powder 3 parts, bentonite 2.5 parts, Guangxi white mud 3.5 parts, oxalic acid 2 parts, explosion-proof fiber powder 0.05 parts; the above raw materials are added to 7 parts aluminum dihydrogen phosphate solution with a specific gravity of 1.50, Carry out the first mechanical stirring and mixing, after mixing uniformly, the material will be trapped for more than 24 hours, and then the second mechanical stirring, then add 8 parts of the same aluminum dihydrogen phos...

Example Embodiment

[0016] Example 3

[0017] The high-temperature lining surface repair material of the present invention is prepared from the following raw materials in a proportion of parts by mass, with coarse particles of Al 2 O 3 The content of 80% bauxite homogenizer contains 18 parts of 5-3mm particle size, 23 parts of 3-1mm particle size, 20 parts of brown corundum powder with 1-0mm particle size, and Al-85 special grade alum. 23 parts of soil homogenizing material, active α-Al 2 O 3 6 parts, high-quality silica powder 4 parts, bentonite 2 parts, Guangxi white clay 4 parts, oxalic acid 1 part, explosion-proof fiber powder 0.05 parts; the above raw materials are added with a specific gravity of 1.55 aluminum dihydrogen phosphate solution 6 parts, proceed to the first One time mechanical stirring and mixing, after mixing uniformly, the material is trapped for more than 24 hours, and then the second mechanical stirring time, and then adding 8 parts of the same aluminum dihydrogen phosphate solu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-temperature lining surface repairing material which is prepared from, by mass, 35-40 parts of coarse particle, alumina homogenizing material with Al2O3 content not lower than 80%, 20-25 parts of fine particle, brown alumina powder, 25-30 parts of fine powder, special-grade alumina homogenizing material with Al2O3 content not lower than 85%, 5-6 parts of active alpha-Al2O3, 3-5 parts of high-quality silicon dioxide micropowder, 5-7 parts of plasticizer, 1.0-2.0 parts of preservative and 0.05 part of anti-explosion fiber powder. A preparation method of the repairing material includes: adding a binding agent, stirring for the first time, mixing well, and discharging; aging for more than 24h, stirring for the second time, adding the binding agent of the same type, stirring, and extruding by an extruder to obtain the repairing material. The high-temperature lining surface repairing material is high in strength, quick in heat conduction, high in high-temperature corrosion resistance, high in high-temperature wear resistance, high in adhesive capacity, less prone to stripping, high in performance of combining with original walls and quick in construction, quick temperature-rise running can be realized after construction is finished, and safe periodic running of thermal equipment/high-temperature kiln is guaranteed.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a high-temperature lining body surface repair material. Background technique [0002] During the operation of power generation boilers, waste incinerators and other high-temperature kilns, the furnace wall is always under high temperature, and the inner wall of the furnace wall is subjected to strong scouring force, and the surface layer is easy to crack and peel off, which eventually leads to damage to the inner wall of the furnace wall. repair. The refractory materials used in the current industry have a long solidification time after repairing, and the kiln cannot be heated up immediately. The repaired wall has poor high temperature resistance, poor combination with the original wall, and wear resistance cannot meet the use requirements. Contents of the invention [0003] In order to solve the deficiencies in the prior art, the present invention pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/101C04B35/66
Inventor 魏发灿王文战魏俊辉慎东涛魏俊瑶燕军胜罗正
Owner 郑州耐都热陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap