Method for preparing arenga engleri mat through plant cementing compound

Abstract

The invention discloses a method for preparing an arenga engleri mat through a plant cementing compound. Firstly, arenga engleri silks are dried, the dried arenga engleri silks are sprayed with the cementing compound, the cementing spraying amount is 10%-20% of the mass of the arenga engleri silks, heating and drying are carried out, and pressing and shaping are carried out for manufacturing the arenga engleri mat; secondly, the surface of the shaped arenga engleri mat is subject to cementing spraying treatment, and the cementing spraying amount is 10%-20% of the mass of the arenga engleri silks; and thirdly, the arenga engleri mat obtained after cementing spraying is stacked and is subject to stacking and shaping according to needed thicknesses, and the arenga engleri mat is packed after being cut, and a finished product is obtained. The cementing compound is a natural plant cementing compound. The arenga engleri mat prepared through the plant cementing compound is environment-friendly, free of formaldehyde and other volatile organic compounds, appropriate in elasticity and good in durability.

Description

technical field

[0001] The invention belongs to the field of palm mat preparation, and in particular relates to a method for preparing mountain palm mats using plant adhesives. Background technique

[0002] Natural palm fiber possesses very strong compression resistance and elasticity. For a long time, the palm mat made of palm fiber as a raw material has been widely used in furniture such as mattresses and sofas as an excellent filling material. However, the palm fiber in the prior art In the production process of mats, most of them still use chemical adhesives to shape and reinforce the natural palm fibers. This process determines that the obtained brown mats contain more formaldehyde content, and the chemical adhesives are prone to mildew after being damp. The variable length worm is not environmentally friendly for household use, and the chemical adhesive tends to lose its cohesive force after aging, making the material loose and easy to break, thus affecting the overall...

Examples

Embodiment 1

[0014] The method for preparing mountain palm mats from the plant adhesive of the present invention, first, the brown silk is cleaned with 90°C hot water before drying, and then the brown silk is dried, the drying temperature is 100°C, and the drying time is 5 minutes. The dried brown silk is sprayed with adhesive, the amount of glue sprayed is 15% of the quality of the brown silk, heated and dried, and pressed to form a mountain palm mat. The temperature of the hot pressing and setting is 120 ° C, and the hot pressing and setting time is 40 minutes. The surface of the mountain palm mat that has been shaped is sprayed with glue. The amount of glue sprayed is 5% of the quality of the palm silk. 120°C, hot pressing and setting time for 30 minutes, cut it and pack it to get the finished product; the adhesive is a natural vegetable adhesive, and its formula is 100 parts of defatted soybean powder, 10 parts of crosslinking agent polyacrylamide, gelatin 5 parts, preservative sodium ...

Embodiment 2

[0016] The method for preparing the mountain palm mat from the plant adhesive of the present invention, firstly, the brown silk is washed with hot water of 80-90° C. before drying, and then the brown silk is dried, and the drying temperature is 80° C., and the drying time is 10 minutes. , Spray the dried brown silk with adhesive, the amount of glue sprayed is 20% of the mass of the brown silk, heat and dry, press and shape to make a mountain palm mat, the temperature for hot pressing and setting is 150°C, and the time for hot pressing and setting is 60 minutes , and then spray glue on the surface of the shaped mountain palm mat. The amount of glue sprayed is 10% of the quality of the palm silk, and then the mountain palm mat after glue spraying is overlapped and hot-pressed according to the required thickness. The temperature is 150°C, the hot-press setting time is 60 minutes, and it is cut and packaged to obtain the finished product; the adhesive is a natural vegetable adhesiv...

Embodiment 3

[0018] The palm mattress prepared in Examples 1-2 of the present invention was tested for performance, and the test results are shown in Table 1, wherein the comparative example adopts the palm mattress prepared by the same preparation method as the present invention using urea-formaldehyde resin adhesive.

[0019] The relevant performance detection data of the mountain palm mat prepared by the embodiment of the present invention 1-2 of table 1

[0020]

technical field

[0001] The invention belongs to the field of palm mat preparation, and in particular relates to a method for preparing mountain palm mats using plant adhesives. Background technique

[0002] Natural palm fiber possesses very strong compression resistance and elasticity. For a long time, the palm mat made of palm fiber as a raw material has been widely used in furniture such as mattresses and sofas as an excellent filling material. However, the palm fiber in the prior art In the production process of mats, most of them still use chemical adhesives to shape and reinforce the natural palm fibers. This process determines that the obtained brown mats contain more formaldehyde content, and the chemical adhesives are prone to mildew after being damp. The variable length worm is not environmentally friendly for household use, and the chemical adhesive tends to lose its cohesive force after aging, making the material loose and easy to break, thus affecting the overall...

Examples

Embodiment 1

[0014] The method for preparing mountain palm mats from the plant adhesive of the present invention, first, the brown silk is cleaned with 90°C hot water before drying, and then the brown silk is dried, the drying temperature is 100°C, and the drying time is 5 minutes. The dried brown silk is sprayed with adhesive, the amount of glue sprayed is 15% of the quality of the brown silk, heated and dried, and pressed to form a mountain palm mat. The temperature of the hot pressing and setting is 120 ° C, and the hot pressing and setting time is 40 minutes. The surface of the mountain palm mat that has been shaped is sprayed with glue. The amount of glue sprayed is 5% of the quality of the palm silk. 120°C, hot pressing and setting time for 30 minutes, cut it and pack it to get the finished product; the adhesive is a natural vegetable adhesive, and its formula is 100 parts of defatted soybean powder, 10 parts of crosslinking agent polyacrylamide, gelatin 5 parts, preservative sodium ...

Embodiment 2

[0016] The method for preparing the mountain palm mat from the plant adhesive of the present invention, firstly, the brown silk is washed with hot water of 80-90° C. before drying, and then the brown silk is dried, and the drying temperature is 80° C., and the drying time is 10 minutes. , Spray the dried brown silk with adhesive, the amount of glue sprayed is 20% of the mass of the brown silk, heat and dry, press and shape to make a mountain palm mat, the temperature for hot pressing and setting is 150°C, and the time for hot pressing and setting is 60 minutes , and then spray glue on the surface of the shaped mountain palm mat. The amount of glue sprayed is 10% of the quality of the palm silk, and then the mountain palm mat after glue spraying is overlapped and hot-pressed according to the required thickness. The temperature is 150°C, the hot-press setting time is 60 minutes, and it is cut and packaged to obtain the finished product; the adhesive is a natural vegetable adhesiv...

Embodiment 3

[0018] The palm mattress prepared in Examples 1-2 of the present invention was tested for performance, and the test results are shown in Table 1, wherein the comparative example adopts the palm mattress prepared by the same preparation method as the present invention using urea-formaldehyde resin adhesive.

[0019] The relevant performance detection data of the mountain palm mat prepared by the embodiment of the present invention 1-2 of table 1