Phenyl silicone rubber nano composite material and preparation method of same

A nano-composite material, phenyl silicone rubber technology, applied in the field of phenyl silicone rubber nano-composite materials and its preparation, can solve the problems of low aging resistance, easy crushing of products, general wear resistance, etc., and achieve improved aging resistance , Improve air tightness, improve the effect of reinforcement

Inactive Publication Date: 2017-08-29
HUANGSHAN SHANGYI RUBBER & PLASTIC PRODS
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. It is easy to age in the air and becomes sticky when heated. Although many manufacturers will add some anti-aging agents to the preparation of rubber materials, although it can increase the service life, it cannot fundamentally solve the aging problem.
[0007] 2. Low pressure resistance and easy deformation. Although natural rubber has high elasticity, its wear resistance is average and its aging resistance is low.
[0008] 3. Most of the rubber materials, whether it is natural rubber or synthetic rubber, need to add a certain amount of fillers to ensure the wear, elongation, hardness, tensile strength, and tear strength of rubber products. Hoarfrost, and the product is easily crushed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phenyl silicone rubber nano composite material and preparation method of same
  • Phenyl silicone rubber nano composite material and preparation method of same
  • Phenyl silicone rubber nano composite material and preparation method of same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A phenyl silicone rubber nanocomposite material, which is composed of the following parts by mass:

[0046]

Embodiment 2

[0048] A phenyl silicone rubber nanocomposite material, which is composed of the following parts by mass:

[0049]

Embodiment 3

[0051] A phenyl silicone rubber nanocomposite material, which is composed of the following parts by mass:

[0052]

[0053] In the above embodiment, the modified nano filler is one or more of modified nano silica or modified mica powder.

[0054] In the above embodiment, the catalyst is nano zinc oxide.

[0055] In the above embodiment, the curing agent is sulfur.

[0056] In the above embodiment, the coupling agent is a silane coupling agent.

[0057] In the above embodiment, the peanut shell powder is a phenolic substance extracted from peanut shells (for example, Yang Yunxu's technical literature published in "Extraction of Phenolic Substances from Peanut Shells" in the third issue of 1994 has made clear that this The extraction method and application of the substance; and such as: Ji Rencai, Lv Jinkui, Wang Chunju, etc., also disclosed the extraction of the substance in the technical document "Extracting phenolic compounds from peanut shells and peanut shell phenolic phenol formald...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a phenyl silicone rubber nano composite material and a preparation method of same. The composite material is composed of, by mass, 100 parts of phenyl silicone rubber, 6-12 parts of modified nano-filler, 6-12 parts of a catalyst, 12-16 parts of a curing agent, 1-3 parts of a coupling agent, 1-5 parts of carbon fibers, and 1-3 parts of peanut shell powder. The preparation method includes the steps of primary mixing, secondary mixing and a curing reaction. The composite material has high-temperature resistant, low-temperature resistant and anti-impact effects, has elastic effect under a thinner condition, and is free of pulverization even after long time use.

Description

Technical field [0001] The invention relates to a phenyl silicone rubber nano composite material and a preparation method thereof. Background technique [0002] With the occurrence of the rubber industry, sealing rings are widely used, rubber seals occupy a very important position in the development of the national economy, and the creation of rubber seals has maintained a double-digit growth. [0003] With the improvement of the product technology level of my country's rubber and plastic seal manufacturing industry, the transfer of the world's processing and manufacturing industry to China and the effect of price leverage, the level of China's export of rubber and plastic seals has increased in recent years, and some products with higher technical content Has entered the international market. This situation has brought great development opportunities to domestic rubber and plastic seal manufacturers. [0004] The rapid economic development has brought about an increase in fixed ass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08K13/06C08K5/13C08K3/36C08K3/34C08K7/06
CPCC08K3/34C08K3/36C08K5/13C08K7/06C08K13/06C08K2201/011C08L2201/08C08L83/04
Inventor 陈尚彪
Owner HUANGSHAN SHANGYI RUBBER & PLASTIC PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products