Hot-stamping forming method for zinc plating steel plate or steel strip

A technology of hot stamping forming and hot stamping, which is applied in forming tools, hot dipping process, coating, etc., to achieve the effects of saving energy consumption, reducing heating temperature, and shortening holding time

Active Publication Date: 2017-09-05
BAOSHAN IRON & STEEL CO LTD
View PDF7 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a hot stamping forming method of zinc-based coated steel sheet or steel strip. Blanking is carried out, and finally hot stamping and in-mold quenching are carried out. The forming temperature range is 400-650°C, which can avoid substrate cracks caused by local stress and LME, and is used to solve the problem that current hot stamping forming steel cannot avoid substrate cracks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-stamping forming method for zinc plating steel plate or steel strip
  • Hot-stamping forming method for zinc plating steel plate or steel strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be described in further detail below in conjunction with the accompanying drawings and specific embodiments.

[0034] Since the zinc-based hot stamping process in the prior art is easy to cause cracks in the substrate, in order to overcome the defects in the prior art, the present invention provides a method that can simultaneously improve the hot stamping efficiency and avoid the hot stamping of zinc-based hot stamping steel. Hot stamping forming process for substrate cracks. After the process of the invention is used for hot stamping, the tensile strength of the steel plate or steel strip is greater than 1500MPa, and at the same time, the substrate cracks caused by local stress and LME are avoided.

[0035] The present invention firstly provides a steel for hot stamping, its composition is mainly (all data are mass %): C: 0.1%-0.5%, Si: 0.1%-0.5%, Mn: 0.5%-3.0%, B : 0%~0.010%, Ti: 0%~0.20%, Nb: 0%~0.20%, V: 0%~1.0%,, W: 0%~1.0%, Cr: 0%~1.0%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hot-stamping forming method for a zinc plating steel plate or a steel strip. According to the hot-stamping forming method, the steel plate or the steel strip is conveyed into a vertical heating annealing furnace, the temperature is kept for a certain time, the steel plate is completely austenitized, a pre-cooling device is used when the steel plate leaves the annealing furnace, the steel plate is cooled to 650-700 DEG C at the cooling rate higher than 30 DEG C / s, then blanking is performed according to the part shape and size, then the steel plate is quickly transferred into a mold for hot-stamping forming, the steel plate is hardened at the speed higher than 30 DEG C / s, and the hot-stamping forming temperature is kept between 400 DEG C and 650 DEG C. Base plate cracks caused by partial stress and liquid metal embrittlement (LME) can be avoided, and the method is used for solving the problem that the base plate cracks cannot be avoided for existing zinc-based hot-stamping formed steel.

Description

technical field [0001] The invention relates to the field of metal materials, and is mainly applicable to the field of forming thin steel plates for automobile bodies. It is a forming method for hot stamping steel plates and steel strips, and is mainly used for manufacturing structural parts such as automobile B pillars, door anti-collision beams, and bumpers. Background technique [0002] The "light weight" of automobiles can directly reduce emissions and fuel consumption, which is the goal of the development of today's automobile manufacturing industry. The application of high-strength steel and ultra-high strength has become one of the mainstream development trends in the field of automobile manufacturing. However, due to the problems of poor shape, high processing forming load, and large springback when ultra-high-strength steel plates are cold-worked, these problems affect ultra-high strength. Therefore, hot stamping is an important way to realize ultra-high-strength st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21D22/02B21D37/16B21C37/02C23C2/06C22C38/04C22C38/02C22C38/14C22C38/12C22C38/18C22C38/16C22C38/08
CPCB21C37/02B21D22/02B21D22/022B21D37/16C22C38/002C22C38/005C22C38/02C22C38/04C22C38/08C22C38/105C22C38/12C22C38/14C22C38/16C22C38/18C23C2/06
Inventor 毕文珍洪继要王利
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products