Hydrophilic coating with high antistatic property and preparation method thereof

A hydrophilic, high-resistance technology, applied in conductive coatings, alkali metal silicate coatings, etc., to achieve the effect of improving surface smoothness, improving user experience, and good hydrophilic performance

Active Publication Date: 2017-09-08
GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD +1
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the problems existing in the prior art, the present invention provides a hydrophilic coating with high antistatic performance and a preparation method thereof, which solves the partial discharge and dust viscosity caused by the poor conductivity of the base material, has good hydrophilic performance, and improves the application performance. The user's experience, reduce the difficulty of cleaning and other advantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0068] The preparation method of the above-mentioned hydrophilic coating with high antistatic performance is as follows: mixing the components together according to the above-mentioned proportion.

[0069] Specifically, when the auxiliary agent includes adhesion promoter, wetting and dispersing agent and defoamer, the preparation method of the coating with high antistatic performance of hydrophilic type comprises the following steps:

[0070] 1) Preparation of wet dispersion system:

[0071] Mix the wetting and dispersing agent with the solvent according to the ratio, then add the nano-sol and mix to obtain a wetting and dispersing system;

[0072] 2) Prepare the conductive system:

[0073] Mix the silicate solution with the adhesion promoter and defoamer, then add the conductive additive according to the proportion, and mix to obtain the conductive auxiliary system;

[0074] 3) Prepare hydrophilic coating with high antistatic properties:

[0075] Add conductive filler to t...

Embodiment 1

[0088] The coating of hydrophilic type high antistatic performance comprises each component of following weight: Multilayer graphene conductive filler is 1.8 kilograms, and Hostastat HS1 conduction aid is 1.5 kilograms, and silicate solution is 31 kilograms (comprising lithium silicate solution 16 kilograms) kg, sodium silicate solution 5 kg, potassium silicate solution 10 kg), SiO 2 / TiO 2 Nano sol is 25 kg, solvent (ie isopropanol) is 39.7 kg, Bayowet929 adhesion promoter is 0.3 kg, KP360 wetting and dispersing agent is 0.4 kg, BYK-053 defoamer is 0.3 kg.

[0089] The preparation method of the coating of this hydrophilic type high antistatic performance is as follows:

[0090] (1) Preparation of wet dispersion system:

[0091] Add 0.4 kg of KP360 wetting and dispersing agent and 39.7 kg of isopropanol solvent into the reactor at room temperature, stir at a low speed of 100 r / min to dissolve the two, and then add 25 kg of SiO 2 / TiO 2 Add the nano-sol, adjust the stirring s...

Embodiment 2

[0097] The coating of hydrophilic type high antistatic performance comprises each component of following weight: single-layer graphene conductive filler is 0.3 kilograms, and Hostastat HS1 conduction aid is 1.5 kilograms, and silicate solution is 31 kilograms (comprising lithium silicate solution 16 kilograms) kg, sodium silicate solution 5 kg, potassium silicate solution 10 kg), SiO 2 / TiO 2 Nano sol is 25 kg, solvent (ie isopropanol) is 41.2 kg, Bayowet929 adhesion promoter is 0.3 kg, KP360 wetting and dispersing agent is 0.4 kg, BYK-053 defoamer is 0.3 kg.

[0098] The preparation method of the coating of this hydrophilic type high antistatic performance is as follows:

[0099] (1) Preparation of wet dispersion system:

[0100] At room temperature, add 0.4 kg of KP360 wetting and dispersing agent and 41.2 kg of isopropanol solvent into the reactor, stir at a low speed of 100 r / min to dissolve the two, and then add 25 kg of SiO 2 / TiO 2 Add the nano-sol, adjust the stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hydrophilic coating with a high antistatic property and a preparation method thereof. The hydrophilic coating with the high antistatic property is prepared from the following components in parts by weight: 0.3-1.8 parts of conductive filler, 0.5-1.5 parts of conductive auxiliary, 25-50 parts of silicate solution, 10-35 parts of nano sol, 13.4-42 parts of solvent and 0.5-1 part of auxiliary. In preparation, the components are mixed according to a proportion. According to thehydrophilic coating with the high antistatic property and the preparation method thereof provided by the invention, the partial discharge and the dust viscosity caused by poor electrical conductivity of a base material are solved; the hydrophilic coating has the advantages that the hydrophilic property is good, the using experience of a user is improved, the cleaning difficulty is reduced, and the like.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a hydrophilic coating with high antistatic performance. Background technique [0002] In 2000, Professor Shirakawa of Japan and Professor MacDiarmid of the United States discovered that polyacetylene has high conductivity, which broke people's traditional thinking, that is, the concept that high molecular polymers are insulating, and made conductive polymers become the focus of many scientific research work. The focus of the researchers' research has aroused extensive attention. Conductive polymers are formed by chemical or electrochemical doping of polymers with conjugated π bonds, and a class of polymer materials whose conductivity extends from insulators to conductors. [0003] Traditional plastic parts are insulating materials, and home appliances are mostly made of plastic materials. Plastic materials have always been the main raw materials used in home appliances due to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D5/24
CPCC09D1/04C09D5/24
Inventor 赵莉
Owner GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com