Waterproof plastering gypsum and production method thereof

A plaster plaster and waterproof technology, which is applied in the field of plaster materials, can solve the problems of being easy to fall off due to moisture and poor waterproof ability, and achieve the effects of not easy to fall off due to moisture, strong bonding strength, and excellent heat insulation effect

Inactive Publication Date: 2017-09-15
HEFEI SHANGHAN DECORATION ENG CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current stucco plaster has poor waterproof ability and is easy to fall off due to moisture.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A waterproof plaster plaster, comprising the following raw materials: 55 parts of desulfurized gypsum, 42 parts of cement, 38 parts of modified kaolin, 32 parts of refractory particles, 26 parts of anhydrous magnesium chloride, 24 parts of crystal growth agent, and 21 parts of floating beads , 18 parts of silicone water repellent, 15 parts of additives and 65 parts of water;

[0027] The auxiliary agent includes the following raw materials: 3 parts of water reducing agent, 2 parts of foaming agent, 1 part of foam stabilizer, 0.6 part of gypsum retarder, 0.4 part of adhesive and 0.2 part of organic water retaining agent.

[0028] in,

[0029] The desulfurized gypsum is hemihydrate gypsum obtained by calcining waste residue produced after desulfurization of flue gas in a power plant, and the average particle size of the desulfurized gypsum is 0.035mm.

[0030] The cement is ordinary Portland cement.

[0031] The preparation method of the modified kaolin is as follows: w...

Embodiment 2

[0040] A waterproof plaster plaster, comprising the following raw materials: 65 parts of desulfurized gypsum, 44 parts of cement, 40 parts of modified kaolin, 33 parts of refractory particles, 28 parts of anhydrous magnesium chloride, 26 parts of crystal growth agent, and 23 parts of floating beads , 19 parts of silicone water repellent, 16 parts of additives and 70 parts of water;

[0041] The auxiliary agent includes the following raw materials: 4 parts of water-reducing agent, 3 parts of foaming agent, 2 parts of foam stabilizer, 1.2 parts of gypsum retarder, 0.6 part of adhesive and 0.4 part of organic water-retaining agent.

[0042] in,

[0043] The desulfurized gypsum is hemihydrate gypsum obtained by calcining waste residue produced after desulfurization of flue gas in a power plant, and the average particle size of the desulfurized gypsum is 0.075mm.

[0044] The cement is sulphoaluminate cement.

[0045] The preparation method of the modified kaolin is as follows: w...

Embodiment 3

[0054] A waterproof plastering gypsum, comprising the following raw materials: 60 parts of desulfurized gypsum, 43 parts of cement, 39 parts of modified kaolin, 32.5 parts of refractory particles, 27 parts of anhydrous magnesium chloride, 25 parts of crystal growth agent, and 22 parts of float beads , 18.5 parts of silicone water repellent, 15.5 parts of additives and 67.5 parts of water;

[0055] The auxiliary agent includes the following raw materials in parts: 3.5 parts of water reducing agent, 2.5 parts of foaming agent, 1.5 part of foam stabilizer, 0.9 part of gypsum retarder, 0.5 part of adhesive and 0.3 part of organic water-retaining agent.

[0056] in,

[0057] The desulfurized gypsum is hemihydrate gypsum obtained by calcining the waste residue produced after the desulfurization of the flue gas of the power plant, and the average particle size of the desulfurized gypsum is 0.055 mm.

[0058] The cement is slag cement.

[0059] The preparation method of the modified...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
flame retardantaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses waterproof plastering gypsum and a production method thereof, which relate to the technical field of a plastering material. The waterproof plastering gypsum comprises the following raw materials by parts: 55-65 parts of desulfurized gypsum, 42-44 parts of cement, 38-40 parts of modified kaolin, 32-33 parts of fireproof particles, 26-28 parts of anhydrous magnesium chloride, 24-26 parts of a crystal growth stimulator, 21-23 parts of floating beads, 18-19 parts of an organosilicon water repellent, 15-16 parts of an auxiliary agent, and 65-70 parts of water. The waterproof plastering gypsum has excellent waterproof performance, is not easily damped and shed, and has high stability.

Description

technical field [0001] The invention relates to the technical field of plastering materials, in particular to a waterproof plastering plaster and a preparation method thereof. Background technique [0002] my country has a long history of using gypsum cementitious materials, but the scope of application is limited. With the improvement of living standards, people's awareness and requirements for building materials such as energy saving, safety and non-toxicity have increased, and gypsum materials have a series of technical advantages. , making it an energy-saving green material that is respected internationally. The gypsum plastering layer hardens quickly, and the surface layer can be constructed within 1h-2h after the bottom layer is completed, which greatly shortens the construction period. After construction, no maintenance is required, which is conducive to the protection of the finished product. Plaster plaster can be well bonded to any base material, and is not limited...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B38/10C04B111/27C04B111/28C04B111/52
CPCC04B28/144C04B2111/27C04B2111/28C04B2111/52C04B2201/50C04B7/02C04B14/106C04B14/185C04B14/202C04B14/4643C04B22/12C04B18/082C04B24/42C04B2103/302C04B24/16C04B22/16C04B24/14C04B24/38C04B24/04C04B22/00C04B24/06C04B24/085C04B24/36C04B24/2611C04B2103/0068C04B38/10C04B7/32C04B24/287C04B24/20C04B24/2652C04B7/14C04B24/226C04B24/34C04B24/2623
Inventor 俞克波
Owner HEFEI SHANGHAN DECORATION ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap