Hollowed-out Jun procelian and preparation technology thereof

A preparation process, a technology of Jun porcelain, applied in the field of hollow Jun porcelain and its preparation technology, can solve the problems of finished porcelain such as hardness, poor wear resistance, poor high temperature resistance, easy deformation of the green body, etc., to improve the bonding force and speed up Drying rate, firming effect

Inactive Publication Date: 2017-09-22
任合超
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the technical problems of traditional hollow porcelain, such as complex process, cumbersome operation, easy deformation of green body, poor local high temperature resistance, high loss rate, poor hardness and wear resistance of finished porcelain, the present invention proposes a hollow Jun porcelain and Its preparation process, through the raw material formula of body porcelain, the firing method of body porcelain, as well as the improvement of glaze formula and glaze firing process, has realized the preparation of hollow Jun porcelain with good hardness, high molding rate and low loss-on-fire rate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation process of the body porcelain comprises the following steps:

[0035] Step 1. According to the above-mentioned parts by weight, mix each material in the main material to obtain a dry material, then add water 0.55-0.65 times its mass to the dry material, stir it evenly, send it to a ball mill, and ball mill it into a particle size It is 150~300 mesh slurry, for standby;

[0036] Step 2. According to the above weight parts, take the fish scale powder and sawdust in the pore-making granules and mix them evenly, then add a binder to the obtained mixed material, after evenly mixing, stick to PMMA with a particle size of 2-4mm The outer surface of the granules is made into pore-making granules with a particle size of 3-5mm, for use;

[0037] Step 3. After sieving and filtering the slurry prepared in step 1, the tire material is made, and then, adding 0.2-0.3 times its mass of ethanol and 0.03-0.05 times its mass of ethanol to the obtained tire material. Indu...

Embodiment 1

[0048] A kind of hollow Jun porcelain, including body porcelain and glaze porcelain. A plurality of through holes are arranged on the outer surface of the body porcelain. The treatment realizes the pre-separation of the pore-forming particles and the green body; and then sinters the green body at high temperature to realize the melting of the pore-making particles.

[0049] The firing raw material of the body porcelain is composed of main material and pore-making particles. According to parts by weight, the main material includes 30 parts of calcined kaolin, 40 parts of clay, 10 parts of soda stone, and 7 parts of volcanic stone , 3 parts of bone meal, 3 parts of purple wood knot, 0.06 parts of titanium dioxide, 20 parts of alumina, 10 parts of white feldspar, 10 parts of wind cave soil, 2 parts of black wool stone, 8 parts of iron ore Stone and 6 parts of carbon powder, the pore-making particles include 15 parts of PMMA pellets, 7 parts of fish scale powder and 11 parts of wo...

Embodiment 2

[0065] A kind of hollow Jun porcelain, including body porcelain and glaze porcelain. A plurality of through holes are arranged on the outer surface of the body porcelain. The treatment realizes the pre-separation of the pore-forming particles and the green body; and then sinters the green body at high temperature to realize the melting of the pore-making particles.

[0066] The firing raw material of the body porcelain is composed of main material and pore-making particles. According to parts by weight, the main material includes 40 parts of calcined kaolin, 48 parts of clay, 15 parts of soda stone, and 11 parts of volcanic stone , 5 parts of bone meal, 7 parts of purple wood knot, 0.08 parts of titanium dioxide, 25 parts of alumina, 15 parts of white feldspar, 12 parts of wind cave soil, 3 parts of black wool stone, 10 parts of iron ore Stone and 8 parts of carbon powder, the pore-making particles include 20 parts of PMMA pellets, 9 parts of fish scale powder and 14 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to hollowed-out Jun procelian, comprising two parts, i.e., base procelian and glazed porcelain, wherein a plurality of through holes are formed in the outer surface of the base procelian; the pre-separation between pore-making granules and a green body is realized by means of microwave treatment on the pore-making granules evenly doped in the base procelian green body through the through holes; then, the green body is subjected to high-temperature sintering, so that the pore-making granules are melted, and the hollowed-out Jun procelian is obtained. After the hollowed-out Jun procelian and a preparation technology thereof, provided by the invention, are adopted, the preparation of the hollowed-out Jun procelian which is good in finished product hardness, high in molding rate and low in loss on ignition can be realized by means of a base procelian raw material formula, a base procelian firing method and improvement for a glaze formula and a glaze firing technology.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to hollow Jun porcelain and its preparation process. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family is rich, but it is not as good as a piece of Jun porcelain". With its simple shape, exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, thousands of colors out of the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc. Known as the first of China's "Five Famous Porcelains". [0003] In the preparation process of Jun porcelain, from material selection to firing finished products, there are dozens of production processes. Generall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/135C04B33/30C04B33/34C04B38/06C04B41/86C03C8/14
CPCC03C8/14C04B33/1355C04B33/30C04B33/34C04B38/0675C04B41/5022C04B41/86C04B2235/3217C04B2235/3232C04B2235/3463C04B2235/422C04B2235/656C04B41/4539C04B41/0072C04B38/067C04B38/0665Y02P40/60
Inventor 任合超
Owner 任合超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More