A Fe-co-p-c series amorphous electrocatalyst for efficient hydrogen evolution reaction and preparation method thereof
A fe-co-p-c, electrocatalyst technology, applied in the direction of electrodes, electrolytic components, electrolytic process, etc., can solve the problems of low current density, high overpotential and poor stability of electrocatalysts, and achieve good electrocatalytic activity and low cost , good electrical conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] This embodiment prepares Fe according to the following steps 40 co 40 P 13 C 7 Amorphous alloy strip:
[0027] (1) Preparation of master alloy ingot
[0028] According to the nominal composition Fe 40 co 40 P 13 C 7 , Fe powder, Co powder with a purity of 99.9wt.%, P powder and C powder with a purity of not less than 99.00wt.% are mixed, and then melted in a vacuum electric arc furnace under the protection of high-purity Ar gas. In order to ensure the alloy composition The composition of the master alloy is uniform, and the master alloy is repeatedly turned and smelted in the furnace for more than 4 times. During each smelting process, the ferrophosphorus and carbon powder are smelted as slowly as possible to prevent the volatilization of the raw materials due to excessive temperature. Finally, the master alloy ingot is obtained after cooling.
[0029] (2) High vacuum belt
[0030] The master alloy ingot obtained in step (1) is re-melted by induction heating, a...
Embodiment 2
[0035] In this example, the Fe-Co-P-C based amorphous electrocatalyst was prepared by the same method as in Example 1, the only difference being that the nominal composition of each raw material composition was changed to obtain strips with different compositions. The size parameters of the obtained samples are shown in Table 1. After characterization, each sample has an amorphous structure and has good electrocatalytic activity.
[0036] Table 1 Composition and size parameters of some samples of Fe-Co-P-C amorphous alloy strips
[0037] Sample composition
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com