Vitrifiable flame-retardant silicone rubber foam material and preparation method thereof

A foam material and silicone rubber technology, which is applied in the field of porcelain-able flame-retardant silicone rubber foam materials, can solve the problems of loss of mechanical properties, secondary injury to personal safety, and reduction of mechanical properties.

Pending Publication Date: 2017-10-10
QINGDAO UNIV OF SCI & TECH
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, non-halogenated, low-smoke, low-toxicity, and high-efficiency are the current flame retardant research trends; secondly, when a fire occurs with traditional flame retardant materials, the mechanical properties of the material are rapidly reduced, such as using only aluminum hydroxide flame retardant, burning ashes It is powdery, completely loses its mechanical properties, and easily causes secondary damage to people's personal safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of ceramicable flame-retardant silicone rubber foam material, the mass fraction of raw materials is as follows:

[0033] Silicone rubber 100 parts,

[0034] 6 parts foaming agent,

[0035] 5 parts of foaming aid,

[0036] 5 parts of vulcanizing agent,

[0037] 20 parts of reinforcing agent,

[0038] 5 parts of structure control agent,

[0039] 20 parts of flame retardant,

[0040] 10 parts porcelain filler,

[0041] 5 parts of vitrification aid.

[0042] Its preparation process is as follows:

[0043] (1) Mix 100 parts of silicone rubber and 20 parts of reinforcing agent nano white carbon black in an internal mixer for 5 to 10 minutes, then beat on the mixer for 5 to 15 times, until the mixture is even and the next piece , heated in an oven at 180°C for 2 hours, and then parked at room temperature for 1 day, that is, the rubber compound.

[0044] (2) Add compound rubber, 5 parts of structure control agent hydroxy silicone oil, 6 parts of foaming agent H,...

Embodiment 2

[0047] A kind of ceramicable flame-retardant silicone rubber foam material, the mass fraction of raw materials is as follows:

[0048] Silicone rubber 100 parts,

[0049] 12 parts foaming agent,

[0050] 10 parts of foaming aid,

[0051] 5 parts of vulcanizing agent,

[0052] 40 parts of reinforcing agent,

[0053] 10 parts of structure control agent,

[0054] 40 parts of flame retardant,

[0055] 20 parts of porcelain filler,

[0056] 15 parts of porcelain auxiliary agent.

[0057] Its preparation process is as follows:

[0058] (1) Blend 100 parts of silicone rubber and 40 parts of nano-white carbon black as a reinforcing agent for 5-10 minutes in an internal mixer, and then beat two-sided three-cutting and triangle bags on an open mixer for 5-15 times until the mixture is uniform and the next piece , heated in an oven at 180°C for 2 hours, and then parked at room temperature for 1 day, that is, the rubber compound.

[0059] (2) Add compound rubber, 10 parts of stru...

Embodiment 3

[0062] A kind of ceramicable flame-retardant silicone rubber foam material, the mass fraction of raw materials is as follows:

[0063] Silicone rubber 100 parts,

[0064] 1 part foaming agent,

[0065] 1 part foaming aid,

[0066] 1 part vulcanizing agent,

[0067] 1 part of reinforcing agent,

[0068] 1 part of structure control agent,

[0069] 1 part of flame retardant,

[0070] 1 part porcelain filler,

[0071] 1 part of vitrification aid.

[0072] Its preparation process is as follows:

[0073] (1) Blend 100 parts of silicone rubber and 1 part of reinforcing agent nano white carbon black in an internal mixer for 5 to 10 minutes, and then beat on the mixer for 5 to 15 times, until the mixture is uniform and the next piece , heated in an oven at 180°C for 2 hours, and then parked at room temperature for 1 day, that is, the rubber compound.

[0074] (2) Add compound rubber, 1 part of structure control agent hydroxy silicone oil, 1 part of foaming agent H, 1 part of foa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a vitrifiable flame-retardant silicone rubber foam material and a preparation method thereof. The vitrifiable flame-retardant silicone rubber foam material is prepared from the following raw materials in parts by mass: 100 parts of silicone rubber, 1-10 parts of foaming agent, 1-8 parts of foaming aid, 1-5 parts of vulcanizing agent, 1-40 parts of reinforcing agent, 1-10 parts of structure controller, 1-40 parts of combustion improver, 0-20 parts of vitrification filler and 0-15 parts of vitrification aid. The silicone rubber foam material provided by the invention has the advantages of favorable flame retardancy and favorable high-temperature dimensional stability, and is vitrifiable at low temperature.

Description

technical field [0001] The invention relates to a flame-retardant silicone rubber material, in particular to a porcelain-able flame-retardant silicone rubber foam material. Background technique [0002] At present, people's awareness of environmental protection and safety is gradually increasing, and strengthening environmental protection and safety precautions has already become the consensus of mankind. Therefore, non-halogenated, low-smoke, low-toxicity, and high-efficiency are the current flame retardant research trends; secondly, when a fire occurs with traditional flame retardant materials, the mechanical properties of the material are rapidly reduced, such as using only aluminum hydroxide flame retardant, burning ashes It is powdery, completely loses its mechanical properties, and easily causes secondary damage to people's personal safety. How to improve people's escape and rescue time will be another research focus of flame-retardant materials, and porcelain-resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08K13/02C08K3/36C08K3/22C08K3/34C08K5/14C08K3/40C08J9/10
CPCC08J9/107C08L83/04C08J2203/04C08J2383/04C08J2483/06C08L2205/02C08L2203/14C08L2201/02C08K2201/011C08K2201/014C08K2201/006C08K2201/003C08L83/06C08K13/02C08K3/36C08K2003/2227C08K2003/2224C08K3/34C08K3/346C08K5/14
Inventor 马凤国李刚
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap