Artwork adhesive

A technology for adhesives and handicrafts, applied in the directions of adhesives, adhesive types, grafted polymer adhesives, etc., can solve the problem that the performance of handicraft adhesives cannot be further improved, achieve a complete degree of dissolution, avoid impurities, The effect of improving utilization

Inactive Publication Date: 2017-10-17
阜南县中信柳木工艺品有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the raw materials and production process of the existing handicraft adhesive have not changed for a long time, and the performance of the handicraft adhesive cannot be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A handicraft bonding glue, in terms of parts by mass, specifically prepared from the following components: 35 parts of neoprene rubber, 10 parts of styrene, 25 parts of water-based polyurethane resin, 2 parts of dispersant, 5 parts of toluene, dimethyl carbonate 3 parts of ester, 1 part of dichloropropane, 35 parts of methyl methacrylate, 1 part of emulsifier, 0.07 part of catalyst; its preparation method is specifically the following steps:

[0017] (1) Add the toluene, dimethyl carbonate, and dichloropropane into the stirred tank, heat to 50°C, and stir for 3 minutes;

[0018] (2) Mix the neoprene, styrene, water-based polyurethane resin, and dispersant at 110°C with a high-speed mixer, and keep warm for 5 minutes to obtain a mixture;

[0019] (3) Immediately pour the mixture into the stirring tank described in step (1), raise the temperature to 65°C, and stir for 5 minutes, each component is completely dissolved and mixed to obtain the material;

[0020] (4) Put the...

Embodiment 2

[0026] A handicraft bonding glue, in terms of parts by mass, specifically prepared from the following components: 45 parts of neoprene rubber, 15 parts of styrene, 40 parts of water-based polyurethane resin, 5 parts of dispersant, 8 parts of toluene, dimethyl carbonate 9 parts of ester, 4 parts of dichloropropane, 40 parts of methyl methacrylate, 4 parts of emulsifier, 0.2 part of catalyst; Its preparation method is specifically the following steps:

[0027] (1) Add the toluene, dimethyl carbonate, and dichloropropane into the stirred tank, heat to 60°C, and stir for 5 minutes;

[0028] (2) Mix the neoprene, styrene, water-based polyurethane resin, and dispersant at 120°C with a high-speed mixer, and keep warm for 8 minutes to obtain a mixture;

[0029] (3) Immediately pour the mixture into the stirring tank described in step (1), raise the temperature to 80°C, and stir for 8 minutes, each component is completely dissolved and mixed to obtain the material;

[0030] (4) Put th...

Embodiment 3

[0036] A handicraft bonding glue, in terms of parts by mass, specifically prepared from the following components: 40 parts of neoprene rubber, 13 parts of styrene, 34 parts of water-based polyurethane resin, 3 parts of dispersant, 6 parts of toluene, dimethyl carbonate 5 parts of ester, 3 parts of dichloropropane, 37 parts of methyl methacrylate, 2 parts of emulsifier, 0.15 part of catalyst; Its preparation method is specifically the following steps:

[0037] (1) Add the toluene, dimethyl carbonate, and dichloropropane into the stirred tank, heat to 55°C, and stir for 4 minutes;

[0038] (2) Mix the neoprene, styrene, water-based polyurethane resin, and dispersant at 115°C with a high-speed mixer, and keep warm for 6 minutes to obtain a mixture;

[0039] (3) Immediately pour the mixture into the stirring tank described in step (1), raise the temperature to 75°C, and stir for 6 minutes, each component is completely dissolved and mixed to obtain the material;

[0040] (4) Put t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Dynamic viscosityaaaaaaaaaa
Dynamic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an artwork adhesive which is specifically prepared from the following components in parts by mass: 35-45 parts of chloroprene rubber, 10-15 parts of styrene, 25-40 parts of waterborne polyurethane resin, 2-5 parts of a dispersing agent, 5-8 parts of methylbenzene, 3-9 parts of dimethyl carbonate, 1-4 parts of propylene dichloride, 35-40 parts of methyl methacrylate, 1-4 parts of an emulsifier and 0.07-0.2 part of a catalyst. Tests show that the dynamic viscosity of the artwork adhesive provided by the invention is 9.7Pa*s or greater, the peeling strength of the artwork adhesive is 6.1kg / 25mm or greater, the dynamic viscosity of a conventional artwork adhesive is only up to 8.9Pa*s, and the peeling strength of the conventional artwork adhesive is only 4.9kg / 25mm, therefore, by improving raw materials and production processes of the artwork adhesive, adhesive properties such as the viscosity and the peeling strength of the artwork adhesive are greatly improved, and remarkable effects and wide market prospects are achieved.

Description

technical field [0001] The invention belongs to the technical field of polymer compounds, and in particular relates to a handicraft adhesive. Background technique [0002] Adhesive glue, mainly used for bonding or mutual bonding of handicrafts made of bamboo, wood, rattan, iron, plastic, etc. As a kind of adhesive, adhesive glue needs to continuously improve its performance indicators such as viscosity and peel strength , should have the advantages of curing at room temperature, wide range of bonding materials, and good water resistance. But the raw material of existing handicraft adhesive glue and production technology have not changed for a long time, can't further improve the performance of handicraft adhesive glue. Contents of the invention [0003] In order to solve the above problems, the present invention provides a handicraft adhesive. [0004] The present invention is realized through the following technical solutions: [0005] A handicraft bonding glue, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F291/12C08F291/04C08F220/14C08F212/08C09J151/04C09J151/08
CPCC08F279/02C08F283/006C09J151/04C09J151/08C08F220/14
Inventor 张学清
Owner 阜南县中信柳木工艺品有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog