High-zirconium alkali-resistant glass fiber surface-reinforced short-cut felt and production method thereof

An alkali-resistant glass fiber and surface-enhancing technology, applied in textiles, papermaking, non-woven fabrics, etc., can solve problems such as inability to use reinforced cement and poor alkali resistance.

Active Publication Date: 2017-10-20
XIANGYANG HUIERJIE GLASSFIBER
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor alkali resistance of medium-alkali and non-alkali glass fibers, it cannot be used in reinforced cement to make building components and products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The composition of the high zirconium alkali-resistant glass fiber surface reinforced chopped strand mat of embodiment 1 comprises: SiO 2 , 59~62%; ZrO 2 , 15.6% ~ 16.8%; TiO 2 , 1.5~3.0%; CaO, 5.0~6.5%; NaO 2 , 11.5~12.5%; K 2 O, 1.5~2.0%; Al 2 o 3 , ≤0.15%; Fe 2 o 3 , ≤0.1%; the diameter of glass fiber monofilament is 7~8μm; cut into glass fiber monofilament with a length of 50~55mm.

[0047] The production method of the high zirconium alkali-resistant glass fiber reinforced chopped strand mat of embodiment 1 comprises the following processing steps:

[0048] ⑴Choose the following raw materials by weight: quartz sand: 50-70, potassium nitrate: 1-10, calcite: 5-10, zircon sand: 14-30, soda ash: 20-30, fluorite: 0.1-5 ;

[0049] ⑵Crush and mix the above raw materials, add them to the mixer and stir them evenly, transport them to the melting pool with non-shrinkage zirconia corundum bricks as lining or masonry, and use natural gas for melting, and use high tempe...

Embodiment 2

[0059] The composition of the high zirconium alkali-resistant glass fiber surface reinforced chopped strand mat of embodiment 2 includes: SiO 2 , 55-60%; ZrO 2 , 13.8%~15.8%; TiO 2 , 1.0~2.0%; CaO, 4.0~5.5%; NaO 2 , 12.5~13.5%; K 2 O, 1.5~2.5%; Al 2 o 3 , ≤0.25%; Fe 2 o 3 , ≤0.15%; glass fiber monofilament diameter is 7.5 ~ 8.5 μ m; cut into glass fiber monofilament with a length of 50 ~ 65 mm.

[0060] The production method of the high zirconium alkali-resistant glass fiber reinforced chopped strand mat of embodiment 2 comprises the following processing steps:

[0061] ⑴Choose the following raw materials by weight: quartz sand: 50-70, potassium nitrate: 1-10, calcite: 5-10, zircon sand: 14-30, soda ash: 20-30, fluorite: 0.1-5 ;

[0062] ⑵Crush and mix the above raw materials, add them to the mixer and stir them evenly, transport them to the melting pool with non-shrinkage zirconia corundum bricks as lining or masonry, and use natural gas for melting, and use high tem...

Embodiment 3

[0072] The composition of the high zirconium alkali-resistant glass fiber surface reinforced chopped strand mat of embodiment 3 comprises: SiO 2 , 55~65%; ZrO 2 , 13.8%~17.0%; TiO 2 , 1.0~6.5%; CaO, 4~5.0%; NaO 2 , 11.0~13.5%; K 2 O, 1~2.5%; Al 2 o 3 , ≤0.3%; Fe 2 o 3 , ≤0.2%, the diameter of glass fiber monofilament is 8~9μ|; the cut length is 50~60mm.

[0073] Embodiment 3 The production method of high zirconium alkali-resistant glass fiber reinforced chopped strand mat comprises the following processing steps:

[0074] ⑴The selected ingredients are: SiO 2 , 55~65%; ZrO 2 , 13.8%~17.0%; TiO 2 , 1.0~6.5%; CaO, 4~5.0%; NaO 2 , 11.0~13.5%; K 2 O, 1~2.5%; Al 2 o 3 , ≤0.3%; Fe 2 o 3 , ≤0.2% zirconium-containing alkali-resistant glass fiber filaments;

[0075] ⑵ In the wire drawing process, the surface is coated with a sizing agent for felting; the sizing agent is a polymer emulsion composed of an initiator, an oxidizing agent, a surfactant, an antistatic agent, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to high-zirconium alkali-resistant glass fiber surface-reinforced short-cut felt and a production method thereof, and belongs to the technical field of alkali-resistant glass fiber production. The method mainly solves the problems that existing medium-alkali and alkali-free glass fibers are poor in alkali resistance and cannot be applied to reinforced cement concrete. The felt is mainly characterized by comprising 55-64% of SiO2, 13.8-17.5% of ZrO2, 1.0-3.5% of TiO2, 4-7.0% of CaO, 11.0-13.5% of NaO2, 1.0-2.5% of K2O, 0-0.3% of Al2O3 and 0-0.2% of Fe2O3, and the felt is produced in the steps that high-zirconium alkali-resistant glass fiber filaments with the diameter of 7-9 micrometers are cut into filaments with the length of 50-75 mm, then the filaments are evenly distributed in multiple dimensions and then bonded through a powder adhesive or an emulsion adhesive, and then curing and drying are conducted. The method solves the problems that the alkali-resistant glass fibers are irregular in spray yarn distribution and poor in homogeneity, the durability can reach 60 years, and the half-life period is up to 100 years.

Description

technical field [0001] The invention belongs to the technical field of production of high-zirconium alkali-resistant glass fiber products. In particular, it relates to a production process research, felt binder research, and application technology research of using high zirconium alkali-resistant glass fiber to produce high zirconium alkali-resistant glass fiber surface reinforced chopped strand mat. Background technique [0002] At present, there are mainly glass fiber mats made of medium-alkali and non-alkali glass fibers in China, which are mainly used to strengthen resins and produce FRP products. Due to the poor alkali resistance of medium-alkali and non-alkali glass fibers, they cannot be used in reinforced cement to make building components and products. The invention of high zirconium alkali-resistant glass fiber surface-reinforced chopped strand mat overcomes the weakness of medium-alkali and non-alkali glass fiber, and makes full use of the excellent alkali resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4218D04H1/58D04H1/587C03C13/02C03C25/42
CPCC03C13/002C03C25/285D04H1/4218D04H1/58D04H1/587
Inventor 杨兴明郭清
Owner XIANGYANG HUIERJIE GLASSFIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com