Softening method capable of improving weaving performance of rattan

A rattan and performance technology is applied in the field of softening to improve the performance of rattan weaving, which can solve the problems of injury to weaving personnel, increase the difficulty of weaving, cracking and fracture of the rattan, reduce the difficulty of weaving, improve the ability of antibacterial and sun resistance, and inhibit breeding. Effect

Inactive Publication Date: 2017-10-24
阜南县宏达工艺品厂
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Rattan is a kind of vine with tough texture and extremely long body. It is often used to weave daily utensils such as rattan chairs, rattan boxes, and rattan baskets. The phenomenon of rattan cracking and fracture is very easy to occur, which not only increases the difficulty of weaving, but also causes waste of rattan and damages the weaving personnel; therefore, inventing a method for softening rattan that can effectively solve the above problems can effectively reduce the weaving Difficulty, avoid waste, improve economic efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Softening method capable of improving weaving performance of rattan

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] In the embodiment of the present invention, a kind of softening method that improves rattan weaving performance, concrete method is as follows:

[0017] (1) Put the harvested rattan into a freezer at -22°C for 110 minutes at a constant temperature, take it out, put it in a temperature of 168°C and treat it with constant temperature steam for 27 minutes, take it out, and get a treated rattan; effectively promote The high-speed movement of rattan fiber molecules strengthens the force between rattan fiber molecules;

[0018] (2) Submerge the treated rattan in the softening solution for 58 minutes and pass it into the ultrasonic wave for ultrasonic treatment, drain the liquid, wrap it with plastic wrap, put it in a refrigerator with a temperature of 2°C for 170 minutes, and take it out. Uncover the plastic wrap to get the rattan for secondary treatment; effectively promote the softening liquid to penetrate into the rattan, and enhance the interaction between the softening l...

Embodiment 2

[0024] In the embodiment of the present invention, a kind of softening method that improves rattan weaving performance, concrete method is as follows:

[0025] (1) Put the harvested rattan into a freezer at -21°C for 115 minutes at a constant temperature, take it out, put it in a temperature of 169°C and treat it with constant temperature steam for 28 minutes, take it out, and get rattan for one treatment; effectively promote The high-speed movement of rattan fiber molecules strengthens the force between rattan fiber molecules;

[0026] (2) Submerge the treated rattan in the softening solution for 59 minutes and pass it into the ultrasonic wave for ultrasonic treatment, drain the liquid, wrap it with plastic wrap, put it in a refrigerator with a temperature of 2.5°C for 175 minutes, and take it out. Uncover the plastic wrap to get the rattan for secondary treatment; effectively promote the softening liquid to penetrate into the rattan, and enhance the interaction between the s...

Embodiment 3

[0032] In the embodiment of the present invention, a kind of softening method that improves rattan weaving performance, concrete method is as follows:

[0033] (1) Put the harvested rattan into a freezer at -20°C for 120 minutes at a constant temperature, take it out, put it in a temperature of 170°C and treat it with constant temperature steam for 29 minutes, take it out, and get rattan for one treatment; effectively promote The high-speed movement of rattan fiber molecules strengthens the force between rattan fiber molecules;

[0034] (2) Submerge the treated rattan in the softening solution for 60 minutes and pass it into the ultrasonic wave for ultrasonic treatment, drain the liquid, wrap it with plastic wrap, put it in a refrigerator with a temperature of 3°C for 180 minutes, and take it out. Uncover the plastic wrap to get the rattan for secondary treatment; effectively promote the softening liquid to penetrate into the rattan, and enhance the interaction between the sof...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of rattan processing, in particular to a softening method for improving rattan weaving performance. The specific method is as follows: (1) put the harvested rattan into a freezer for constant temperature freezing, take it out, and treat it with constant temperature steam to obtain One-time treatment of rattan; (2) Immerse the primary treatment of rattan in the softening solution and pass it through ultrasonic waves for ultrasonic treatment, drain the liquid, wrap it with plastic wrap, put it in a refrigerator for constant temperature refrigeration, take it out, and uncover it (3) Microwave-dry the rattan for the second treatment; the rattan treated by the present invention has a bending angle of 80-81 degrees during weaving and use, which effectively reduces the difficulty of weaving, It saves time and labor, improves weaving efficiency, not only does not deform and crack, has strong bearing capacity, good dimensional stability, tensile strength, compression resistance and elastic strength have been greatly improved, but also can improve its antibacterial and anti-sunshine ability, and inhibit spoilage bacteria growth, prolonging its lifespan.

Description

technical field [0001] The invention belongs to the technical field of rattan processing, in particular to a softening method for improving rattan weaving performance. Background technique [0002] Rattan is a kind of vine with tough texture and extremely long body. It is often used to weave daily utensils such as rattan chairs, rattan boxes, and rattan baskets. The phenomenon of rattan cracking and fracture is very easy to occur, which not only increases the difficulty of weaving, but also causes waste of rattan and damages the weaving personnel; therefore, inventing a method for softening rattan that can effectively solve the above problems can effectively reduce the weaving Difficulty, avoid waste, improve economic efficiency. Contents of the invention [0003] In view of the above problems, the present invention aims to provide a softening method for improving rattan weaving performance. [0004] The present invention is realized through the following technical solut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K5/06B27K9/00B27K5/00B27K3/52B27K5/04
CPCB27K5/06B27K3/52B27K5/0005B27K5/0065B27K5/04B27K9/002B27K2240/20
Inventor 程昭
Owner 阜南县宏达工艺品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com