Metal product surface film plating method

A technology for metal products and surface coating, applied in metal material coating process, fusion spray plating, coating and other directions, can solve the problems of poor wear resistance and corrosion resistance, can not meet the demand, high waste wire rate, and prolong the service life , The effect of less metal consumption and less waste gas and waste water

Inactive Publication Date: 2017-10-24
HEFEI HUIZHI NEW MACHINERY TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the production of metal products in our country, in order to enhance the surface hardness and corrosion resistance of metal products, the process of plating hard chromium on the surface of metal products is generally used. The disadvantages are low hardness, poor wear resistance and corrosion resistance, and easy carbon deposition. Difficult to clean, high waste silk rate
Especially for high-strength industrial yarn, the existing technology can no longer meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for coating a metal product surface, characterized in that it comprises the following steps:

[0022] (1) Cleaning and shot blasting surface treatment of metal product blanks;

[0023] (2) Dye the cleaned and shot-peened surface-treated metal product blanks and then wire-draw them to draw out the desired texture;

[0024] (3) Cleaning and activating the surface of the metal product blank treated in step (2); evaporating and ionizing the cathode through an electric arc to generate plasma;

[0025] (4) The plasma is reacted with the charged reaction gas in the vacuum chamber, and the reactant is deposited on the surface of the metal product blank to be plated by plasma spraying.

[0026] The metal product is selected from one of iron, aluminum alloy, magnesium alloy, zinc alloy and copper alloy.

[0027] The concrete method of described dry cleaning is as follows:

[0028] First wipe the surface of the metal product with a dry cloth to remove grease and dust, ...

Embodiment 2

[0037] A method for coating a metal product surface, characterized in that it comprises the following steps:

[0038] (1) Cleaning and shot blasting surface treatment of metal product blanks;

[0039] (2) Dye the cleaned and shot-peened surface-treated metal product blanks and then wire-draw them to draw out the desired texture;

[0040] (3) Cleaning and activating the surface of the metal product blank treated in step (2); evaporating and ionizing the cathode through an electric arc to generate plasma;

[0041] (4) The plasma is reacted with the charged reaction gas in the vacuum chamber, and the reactant is deposited on the surface of the metal product blank to be plated by plasma spraying.

[0042] The metal product is selected from one of iron, aluminum alloy, magnesium alloy, zinc alloy and copper alloy.

[0043] The concrete method of described dry cleaning is as follows:

[0044] First wipe the surface of the metal product with a dry cloth to remove grease and dust, ...

Embodiment 3

[0053] A method for coating a metal product surface, characterized in that it comprises the following steps:

[0054] (1) Cleaning and shot blasting surface treatment of metal product blanks;

[0055] (2) Dye the cleaned and shot-peened surface-treated metal product blanks and then wire-draw them to draw out the desired texture;

[0056] (3) Cleaning and activating the surface of the metal product blank treated in step (2); evaporating and ionizing the cathode through an electric arc to generate plasma;

[0057] (4) The plasma is reacted with the charged reaction gas in the vacuum chamber, and the reactant is deposited on the surface of the metal product blank to be plated by plasma spraying.

[0058] The metal product is selected from one of iron, aluminum alloy, magnesium alloy, zinc alloy and copper alloy.

[0059] The concrete method of described dry cleaning is as follows:

[0060] First wipe the surface of the metal product with a dry cloth to remove grease and dust, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal product surface film plating method. The metal product surface film plating method comprises the following steps: (1) the cleaning and the shot blasting surface treatment are performed on a metal product blank; (2) the wire drawing is performed on the metal product blank to draw out needed lines after the cleaning, the shot blasting surface treatment and the metal blackening; (3) the surface cleaning and the activation are performed on the metal product blank after treatment in the step (2); and a cathode is evaporated and ionized to generate plasma through arc; and (4) the plasma is reacted with filled reaction gas in a vacuum chamber; and reactants are deposited on the surface of the metal product blank to be plated through plasma spraying. Film plating products are excellent in functions and appearances and suitable for such industries as electronics, household appliances and vehicles, and deserve popularization and application.

Description

technical field [0001] The invention relates to the technical field of metal products, in particular to a method for coating the surface of metal products. Background technique [0002] At present, in the production of metal products in our country, in order to enhance the surface hardness and corrosion resistance of metal products, the process of plating hard chromium on the surface of metal products is generally used. The disadvantages are low hardness, poor wear resistance and corrosion resistance, and easy carbon deposition. It is not easy to clean, and the waste silk rate is high. Especially for high-strength industrial yarn, the existing technology can no longer meet the demand. The surface hardness of hard chrome is HV850-1100, and the friction coefficient is 0.16-0.17. When the temperature reaches 80°C, the surface hardness begins to decrease. The higher the temperature, the lower the hardness, and the decrease can reach up to 50%. Contents of the invention [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C4/134C23C4/02
CPCC23C4/134C23C4/02
Inventor 解正来
Owner HEFEI HUIZHI NEW MACHINERY TECH CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More