A method for welding low-grade non-oriented silicon steel with laser welding machine

A technology of laser welding machine and oriented silicon steel, which is applied in the field of metallurgy, can solve the problems of increasing the magnetic properties, increasing the difficulty of stable operation of the production line, and decreasing the welding performance of steel plates, so as to improve the welding quality, improve the section size of the welding toe, and reduce the fracture of the weld seam. Band rate effect

Active Publication Date: 2019-06-04
BAOTOU IRON & STEEL GRP
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Low-grade non-oriented silicon steel is generally designed with low-carbon steel components. Silicon and manganese elements are added to low-carbon steel to improve the magnetic properties of the steel plate, especially when the silicon content exceeds 1.0%. Welding performance declines, making it more difficult for the stable operation of the production line

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for welding low-grade non-oriented silicon steel with laser welding machine
  • A method for welding low-grade non-oriented silicon steel with laser welding machine
  • A method for welding low-grade non-oriented silicon steel with laser welding machine

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0035] Below in conjunction with example the present invention will be further described.

[0036] 1. When welding 50W800 / 50W600, the thickness of the steel strip is below 2.5mm (including 2.5mm), the welding machine speed is 4.5m / min, the laser focus of the welding machine is selected at -3mm, and the secondary shear value is selected as 0.5mm. The cupping test was carried out after welding, and the results showed that the quality of the weld seam was excellent and met the requirements.

[0037] 2. When welding 50W800 / 50W600, the thickness of the steel strip is 2.5mm to 3.5mm (including 3.5mm), the welding machine speed is 3.75m / min, the laser focus of the welding machine is selected at -3mm, and the secondary shear value is selected as 0.5 mm. The cupping test was carried out after welding, and the results showed that the quality of the weld seam was excellent and met the requirements.

[0038] 3. When welding 50W800 / 50W600, the thickness of the steel strip is 3.5mm to 6.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for welding low-grade non-oriented silicon steel through a laser welding machine. The method sequentially comprises the following steps that a steel band is centered; shearing is conducted; a lapping table is centered; secondary shearing is conducted; preheating is conducted; weld joint pre-levelling is conducted; weld joint welding is conducted; postheating is conducted; and weld joints are cooled. In the weld joint welding process, the laser focal distance of the laser welding machine is set to be -3 mm, and the welding speed is lowered when silicon steel with the thickness being greater than 3 mm is welded. According to the method, the laser focal distance value is fixed, the range of a weld joint heat affected zone is adjusted through speed, and the weld joint band breakage rate is effectively lowered; and meanwhile, secondary shearing is additionally conducted before welding for improving the weld toe section size, and thus the welding quality is improved.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a method for welding low-grade non-oriented silicon steel with a laser welder. Background technique [0002] Laser welding is the use of high-energy laser pulses to locally heat materials in a small area. The energy of laser radiation diffuses into the interior of the material through heat conduction, and the material is melted to form a specific molten pool. It is a new type of welding method, mainly aimed at the welding of thin-walled materials and precision parts, which can realize spot welding, butt welding, lap welding, sealing welding, etc., with high depth-to-width ratio, small weld width, and small heat-affected zone. The deformation is small, the welding speed is fast, the weld seam is smooth and beautiful, no treatment is required or only simple treatment is required after welding, the weld seam quality is high, there is no air hole, it can be precisely controlled, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/21B23K26/32B23K26/70
CPCB23K26/21B23K26/32B23K26/70
Inventor 韩玉龙
Owner BAOTOU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com