Cutter head passivating and grinding abrasive and preparation method thereof

A tool head and abrasive technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of reduced tool life, low passivation polishing efficiency, single passivation abrasive, etc., to save costs, speed up polishing or dullness Improved processing efficiency and easy-to-obtain results

Inactive Publication Date: 2017-11-24
杭州希恩希拓斯精密机械有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cemented carbide tool has a sharp edge after it has just been ground, and direct use will greatly reduce the service life of the tool. In order to prolong the service life of the tool, it is often necessary to passivate or polish the sharp edge. Currently on the market Commonly used passivation abrasives are relatively simple. For example, in the patent application number 201510827632.X, the name is "a kind of abrasive for tool polishing or passivation", which discloses a formula abrasive mixed with broken walnut peel particles and diamond powder; In the patent No. 201610882805.2, titled "A Process for Passivating Industrial Tools", diamond powder is used as the abrasive for passivation. It can be seen from the above that the current passivation grinding has a single abrasive composition and low passivation polishing efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The abrasive used for tool polishing or passivation provided in this embodiment includes walnut shell particles, black corundum, green silicon carbide, boron carbide, chrome corundum, diamond fine powder, and industrial gear oil that are uniformly stirred with each other.

[0021] Specifically, the particle size of walnut shell is 1 mm to 1.5 mm, the preferred particle size of black corundum is F40, the particle size of green silicon carbide is F400, the particle size of boron carbide is F400, the particle size of chrome corundum is F400, and the particle size of diamond powder is preferably W20.

[0022] 100-120 parts of walnut shell particles, 20-30 parts of black corundum, 3-6 parts of green silicon carbide, 3-6 parts of boron carbide, 5-10 parts of chrome corundum, 1-3 parts of diamond micropowder, 2-3 parts of industrial gear oil share.

[0023] The ratio of walnut shell particles to black corundum is 11:3, the ratio of walnut shell particles to industrial gear oil...

Embodiment 2

[0029] Embodiment 2: The abrasive used for tool polishing or passivation provided by this embodiment includes walnut shell particles, black corundum, green silicon carbide, boron carbide, chrome corundum, diamond fine powder, and industrial gear oil that are uniformly stirred with each other.

[0030] Specifically, the particle size of walnut shell is 0.8 mm to 1.2 mm, the preferred particle size of black corundum is F54, the particle size of green silicon carbide is F500, the particle size of boron carbide is F500, the particle size of chrome corundum is F500, and the particle size of diamond powder is preferably W20.

[0031] 100-120 parts of walnut shell particles, 20-30 parts of black corundum, 3-4 parts of green silicon carbide, 3-4 parts of boron carbide, 5-6 parts of chrome corundum, 2-3 parts of diamond powder, 2-3 parts of industrial gear oil share.

[0032] The ratio of walnut shell particles to black corundum is 11:2, the ratio of walnut shell particles to industria...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cutter head passivating and grinding abrasive and a preparation method thereof. The cutter head passivating and grinding abrasive comprises 100-120 parts of walnut shell particles, 20-30 parts of black corundum, 3-6 parts of green silicon carbide, 3-6 parts of boron carbide, 5-10 parts of chrome corundum, 1-3 parts of diamond micro-powder and 2-3 parts of industrial gear oil. The preparation method is simple; the prepared abrasive has high hardness and mechanical strength; the cutter head passivating and grinding abrasive provided by the invention has effects of being able to polish or passivate a surface of a cutter, particularly increasing cutter polishing or passivating efficiency, also having relatively wide range of application, and being able to polish cutters or molds made of hard alloy, ceramic, metal and many other materials.

Description

technical field [0001] The invention relates to the technical field of grinding materials, in particular to a passivation grinding material for a cutter head. Background technique [0002] With the development of my country's industrial technology, especially the development of numerical control technology in recent years, the application of cemented carbide cutting tools in the fields of automobiles, molds, and aerospace has become more and more extensive. The cemented carbide tool has a sharp edge after it has just been ground, and direct use will greatly reduce the service life of the tool. In order to prolong the service life of the tool, it is often necessary to passivate or polish the sharp edge. Currently on the market Commonly used passivation abrasives are relatively simple. For example, in the patent application number 201510827632.X, the name is "a kind of abrasive for tool polishing or passivation", which discloses a formula abrasive mixed with broken walnut peel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14
CPCC09K3/1472
Inventor 徐海英徐安辉
Owner 杭州希恩希拓斯精密机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products