Light-weight and shock-absorbing combined shoe sole and production method thereof

A production method and lightweight technology, applied in footwear, other household appliances, applications, etc., can solve the problems of rubber material aging, low cell density, difficult to control, etc., to achieve good resilience and shock absorption, and inhibit frost spit. , the effect of slow migration

Inactive Publication Date: 2017-11-28
LILANG CHINA
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used outsole materials are all kinds of wear-resistant rubber, and midsole materials are mostly made of light, resilient EVA or PU foam materials, but these materials also have some problems in use, such as rubber materials have aging, Frost is difficult to control. The EVA material used as the midsole has problems such as large cells, small cell density, and unevenness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A lightweight, shock-absorbing composite shoe sole comprising an outsole and a midsole, the outsole consisting of the following components:

[0061] 8.9 parts of standard rubber, 55.55 parts of butadiene rubber

[0062] 26.66 parts of styrene-butadiene rubber 9 parts of isoprene rubber

[0063] 28 parts of white smoke, 6 parts of white oil

[0064] 1 part of polystyrene, 1.6 parts of anti-aging agent

[0065] 1 part of microcrystalline wax, 3 parts of white smoke active agent

[0066] Polyethylene glycol 3 parts resin 2 parts

[0067] 2.2 parts of anti-emetic cream, 2.6 parts of wear-resistant oil

[0068] 6 parts of zinc oxide, 13.33 parts of nano calcium

[0069] The midsole consists of the following components:

[0070] EVA7350 60 parts EVA7470 50 parts

[0071] POE thermoplastic elastomer 10 parts talcum powder 20 parts

[0072] Foaming agent 3.4 parts Bridging agent 0.8 parts

[0073] 2.6 parts of zinc oxide, 1.2 parts of stearic acid

[0074]Zinc stearat...

Embodiment 2

[0094] A lightweight, shock-absorbing composite shoe sole comprising an outsole and a midsole, the outsole consisting of the following components:

[0095] Standard rubber 7 parts Butadiene rubber 50 parts

[0096] 25 parts of styrene-butadiene rubber 8 parts of isoprene rubber

[0097] 25 parts of white smoke, 5 parts of white oil

[0098] 0.8 parts of polystyrene Anti-aging agent 1.5 parts

[0099] 1 part microcrystalline wax 3 parts white smoke active agent

[0100] Polyethylene glycol 3 parts resin 2 parts

[0101] Anti-emetic cream SK 2 parts wear-resistant oil 2 parts

[0102] Zinc oxide 5 parts Nano calcium 12 parts

[0103] The midsole consists of the following components:

[0104] EVA7350 55 parts EVA7470 45 parts

[0105] POE thermoplastic elastomer 8 parts talcum powder 8 parts

[0106] Foaming agent 3 parts Bridging agent 0.5 parts

[0107] Zinc oxide 2 parts stearic acid 1 part

[0108] Zinc stearate 1 part Flowing agent 2 parts

[0109] Quick curing ag...

Embodiment 3

[0127] A lightweight, shock-absorbing composite shoe sole comprising an outsole and a midsole, the outsole consisting of the following components:

[0128] Standard glue 10 parts Butadiene rubber 60 parts

[0129] 30 parts of styrene-butadiene rubber 10 parts of isoprene rubber

[0130] 30 parts of white smoke, 8 parts of white oil

[0131] Polystyrene 1.2 parts Anti-aging agent 2 parts

[0132] 1 part microcrystalline wax 4 parts white smoke active agent

[0133] Polyethylene glycol 4 parts resin 3 parts

[0134] Anti-emetic cream SK 3 parts wear-resistant oil 3 parts

[0135] Zinc oxide 7 parts Nano-calcium 15 parts

[0136] The midsole consists of the following components:

[0137] EVA7350 65 parts EVA7470 55 parts

[0138] POE thermoplastic elastomer 12 parts talcum powder 12 parts

[0139] Foaming agent 5 parts Bridging agent 1 part

[0140] Zinc oxide 3 parts Stearic acid 1.5 parts

[0141] Zinc stearate 1.5 parts Flowing agent 3 parts

[0142] Fast curing age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production technology of a shoe sole, in particular to a light-weight and shock-absorbing combined shoe sole and a production method thereof. The combined shoe sole consists of an outsole and a midsole, wherein the outsole is produced from a rubber material by mixing, performing open mixing, vulcanizing and other processes; the midsole is produced from an EVA material by mixing, performing open mixing, granulating, foaming once, and performing oil pressing twice. The raw materials and the processes of the light-weight and shock-absorbing combined shoe sole provided by the invention are optimized, so that various problems of the rubber material and the EVA material in application are effectively solved; a finished product is light in weight, good in resilience and excellent in shock-absorbing effect, and is not prone to aging and frosting problems.

Description

technical field [0001] The invention relates to a processing technology for shoe soles, in particular to a light-weight, shock-absorbing combined shoe sole and a manufacturing method thereof. Background technique [0002] Consumers are increasingly focusing on comfort and safety when choosing footwear, especially athletic and casual footwear. In order to ensure that the shoes can be light, not bound, and have better shock-absorbing and rebounding properties when worn, more and more attention has been paid to the improvement and development of shoe soles in this field, and many functional shock-absorbing products have emerged. Commonly used outsole materials are all kinds of wear-resistant rubber, and midsole materials are mostly made of light weight, good resilience EVA or PU foam materials, but these materials also have some problems in use, such as rubber materials have aging, Frost is difficult to control. As the EVA material of the midsole, there are problems such as la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L9/06C08L7/00C08L91/06C08L71/02C08L101/00C08L25/06C08L91/00C08L23/08C08K13/02C08K3/22C08K3/26C08K5/09C08K3/34C08K5/098C08J9/04B29D35/12A43B13/04
Inventor 陈国仲戴纳·尼德瑞姚志刚欧锦蓥史志颖
Owner LILANG CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap