Environment-friendly flame-retardant polyurethane foam material for interior trim sealing strip of limo and preparation method thereof

A foaming material and a sealing strip technology are applied in the field of polyurethane environmentally friendly flame-retardant foaming materials for RV interior sealing strips and the field of preparation thereof, which can solve the hidden dangers of increasing fire safety and increasing RV safety, reducing fire safety and stability, and reducing internal combustion. The environmental protection performance of the decorative sealing strip is poor, so as to achieve the effect of increasing fire safety, reducing weight and weight.

Inactive Publication Date: 2017-12-08
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to reduce the overall weight of the existing caravan, it will reduce its fire safety and stability. Since people spend almost half of the time in the caravan every day, the reduction of its fire safety increases the safety hazards of the caravan. Some RV interior sealing strips have poor environmental protection performance, and long-term use will cause great harm to the environment and the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly flame-retardant polyurethane foam material for interior trim sealing strip of limo and preparation method thereof
  • Environment-friendly flame-retardant polyurethane foam material for interior trim sealing strip of limo and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of the polyurethane environment-friendly flame-retardant foaming material for the above-mentioned RV interior sealing strip, comprising the following preparation steps:

[0017] (1) Raw material treatment: JTM polyether 4110, polyether 4110 and isocyanate were dried at a drying temperature of 40°C and a drying time of 6 hours;

[0018] (2) Weighing ratio: According to the mass ratio, weigh 2.5 parts of silicone oil, 9 parts of diethanolamine, 3 parts of catalyst APM9, 35 parts of flame retardant TCPP and 3.5 parts of water, and JTM polyether 4110 after drying : 55 parts and polyether 4110: 23 parts;

[0019] (3) Prepare the mixture: add the weighed JTM polyether 4110, polyether 4110, silicone oil, diethanolamine, catalyst APM9, flame retardant TCPP and water into the reaction kettle in order to fully stir, and the stirring time is 0.5h. The stirring temperature is 50°C, the stirring speed is 250r / min, and the mixture can be obtained;

[0020] (4) ...

Embodiment 2

[0022] A preparation method of the polyurethane environment-friendly flame-retardant foaming material for the above-mentioned RV interior sealing strip, comprising the following preparation steps:

[0023] (1) Raw material treatment: JTM polyether 4110, polyether 4110 and isocyanate are dried at a drying temperature of 40°C and a drying time of 8 hours;

[0024] (2) According to the mass ratio, weigh 2.8 parts of silicone oil, 13 parts of diethanolamine, 4 parts of catalyst APM9, 38 parts of flame retardant TCPP and 3.8 parts of water, and JTM polyether 4110:65 parts and poly Ether 4110:28 parts;

[0025] (3) Prepare the mixture: add the treated JTM polyether 4110, polyether 4110, silicone oil, diethanolamine, catalyst APM9, flame retardant TCPP and water into the reactor in turn for full stirring. The stirring time is 1.5h. The temperature is 80° C., and the stirring speed is 280 r / min, and the mixture can be obtained.

[0026] (4) Synthetic foaming material: add the isocya...

Embodiment 3

[0028] A preparation method of the polyurethane environment-friendly flame-retardant foaming material for the above-mentioned RV interior sealing strip, comprising the following preparation steps:

[0029] (1) Raw material treatment: Dry JTM polyether 4110, polyether 4110 and isocyanate at a drying temperature of 40°C and a drying time of 7 hours;

[0030] (2) According to the mass ratio, weigh 2.65 parts of silicone oil, 11 parts of diethanolamine, 3.5 parts of catalyst APM9, 36.5 parts of flame retardant TCPP and 3.65 parts of water, and JTM polyether 4110:60 parts and poly Ether 4110: 25.5 parts;

[0031] (3) Prepare the mixture: add the treated JTM polyether 4110, polyether 4110, silicone oil, diethanolamine, catalyst APM9, flame retardant TCPP and water into the reaction kettle in turn for full stirring, the stirring time is 1h, the stirring temperature The temperature is 65°C, the stirring speed is 265r / min, and the mixture can be obtained;

[0032] (4) Synthetic foami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly flame-retardant polyurethane foam material for an interior trim sealing strip of a limo and a preparation method thereof. The foam material comprises isocyanate and a mixture, wherein the ratio of the isocyanate to the mixture in parts by mass is: isocyanate: mixture=1:1.5; the mixture comprises the following raw materials in parts by weight: 55 to 65 parts of JTM polyether 4110, 23 to 28 parts of polyether 4110, 2.5 to 2.8 parts of a stabilizer, 9 to 13 parts of diethanolamine, 3 to 4 parts of a catalyst APM9, 35 to 38 parts of a flame retardant and 3.5 to 3.8 parts of water. The foam material prepared from the raw materials which are reasonably proportioned has efficient flame retardancy, and is safe and environmentally friendly, the interior trim sealing strip of the limo prepared from the foam material is high in fire safety and stability, and hazards to the environment and human bodies are avoided.

Description

technical field [0001] The invention relates to a composite material and a preparation method thereof, in particular to a polyurethane environment-friendly flame-retardant foaming material for a car interior sealing strip and a preparation method thereof. Background technique [0002] With the development of the automobile industry, the caravan has gradually entered people's lives. The caravan is equivalent to a mobile home. The caravan can satisfy people's good travel life and alleviate the problem of lack of houses. Its internal configuration is complete, and the interior of the caravan needs to be sealed. The sealing strips are used to increase the sealing and heat preservation functions of the RV, and the fire safety of the sealing strips is extremely important. In addition to the fire safety, the sealing strips must ensure their stability and meet the requirements of lightweight. [0003] In order to reduce the overall weight of the existing caravan, it will reduce its ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08K5/521C08G101/00
CPCC08G18/4804C08G2101/00C08K5/521
Inventor 朱章娣朱凌宇纪朝根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com