High-temperature purple cobalt oxide ceramic glaze and preparation method thereof

A technology of cobalt oxide and ceramic glaze, applied in the field of ceramics, can solve the problems of unsatisfactory and stable color development effect, and achieve the effects of improving the smoothness of the glaze surface, saving fuel costs, and increasing the viscosity

Inactive Publication Date: 2018-01-09
SHENYANG JIANZHU UNIVERSITY
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Purple ceramic glaze has always been a very difficult ceramic glaze, and the color development effect has not been ideal and stable for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A cobalt oxide high-temperature purple ceramic glaze is prepared by first preparing a cobalt oxide high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt oxide high-temperature purple ceramic glaze. The cobalt oxide high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0032] Potassium feldspar powder 39%, silicon dioxide 19.6%, spherical clay 5%, dolomite 6.9%, talc 14.7%, sodium pyroborate 11.8%, cobalt carbonate 2%, manganese dioxide 1%.

[0033] A method for preparing cobalt oxide high-temperature purple ceramic glaze, comprising the following steps: firstly preparing cobalt oxide high-temperature purple ceramic glaze, then glazing and sintering to obtain copper carbonate high-temperature purple ceramic glaze; wherein, the preparation of cobalt oxide high-temperature purple ceramic glaze Methods as below:

[0034] Step 1, preparation of cobalt oxide high ...

Embodiment 2

[0040] A cobalt oxide high-temperature purple ceramic glaze is prepared by first preparing a cobalt oxide high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt oxide high-temperature purple ceramic glaze. The cobalt oxide high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0041] Potassium feldspar powder 35%, silicon dioxide 15%, spherical clay 8%, dolomite 8%, talc 18%, sodium pyroborate 13%, cobalt carbonate 2%, manganese dioxide 1%.

[0042]A method for preparing cobalt oxide high-temperature purple ceramic glaze, comprising the following steps: firstly preparing cobalt oxide high-temperature purple ceramic glaze, then glazing and sintering to obtain copper carbonate high-temperature purple ceramic glaze; wherein, the preparation of cobalt oxide high-temperature purple ceramic glaze Methods as below:

[0043] Step 1, preparation of cobalt oxide high temperatu...

Embodiment 3

[0049] A cobalt oxide high-temperature purple ceramic glaze is prepared by first preparing a cobalt oxide high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt oxide high-temperature purple ceramic glaze. The cobalt oxide high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0050] Potassium feldspar powder 45%, silicon dioxide 15%, spherical clay 4%, dolomite 9%, talc 10%, sodium pyroborate 8%, cobalt oxide 5%, manganese dioxide 4%.

[0051] A method for preparing cobalt oxide high-temperature purple ceramic glaze, comprising the following steps: firstly preparing cobalt oxide high-temperature purple ceramic glaze, then glazing and sintering to obtain copper carbonate high-temperature purple ceramic glaze; wherein, the preparation of cobalt oxide high-temperature purple ceramic glaze Methods as below:

[0052] Step 1, preparation of cobalt oxide high temperature p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature purple cobalt oxide ceramic glaze and a preparation method thereof, belonging to the ceramic field. The high-temperature purple cobalt oxide ceramic glaze is prepared by the steps of firstly preparing a high-temperature purple cobalt oxide ceramic glaze material, and carrying out glazing and high-temperature sintering, wherein the high-temperature purplecobalt oxide ceramic glaze material contains the following raw materials in percentage by mass: 35%-45% of feldspar powder, 15%-25% of silicon dioxide, 4%-8% of spherical clay, 5%-11% of dolomite, 10%-20% of talcum, 8%-15% of sodium pyroborate, 2%-5% of cobalt oxide and 1%-4% of manganese dioxide. By virtue of long-term adjustment and multiple experiments of a glaze formula, long-term experimentsat -30 DEG C show that the phenomenon that a glaze surface cracks or falls does not appear, and the glaze surface can resist ordinary acid-base corrosion.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a cobalt oxide high-temperature purple ceramic glaze and a preparation method thereof. Background technique [0002] Ceramic glaze is an important raw material that must be used in the production of ceramics. It has a strong protective effect on the ceramic body. At the same time, the physical properties of silicate make the glass enamel on the ceramic surface effectively resistant to acid and alkali corrosion. Very good antibacterial properties. Ordinary ceramic color glazes are achieved by adding metal colorants to the glass enamel to achieve color development during the firing process. Such glaze colors are often single in color and cannot highlight the artistic beauty of the ceramic color glaze itself and the high-temperature firing process. special artistic effects produced in Cobalt oxide high-temperature purple ceramic glaze effectively overcomes the lack of single colo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C03C8/00C04B41/86
Inventor 沈海泳吕美
Owner SHENYANG JIANZHU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com