Regenerated bricks and preparation method thereof

A technology of recycled bricks and recycled aggregates, applied in the field of building materials, can solve the problems of occupying land resources, polluting the environment, environmental pollution, etc., achieving extensive social benefits, simple preparation methods, and good water permeability.

Inactive Publication Date: 2018-01-19
GUILIN CHUNXIAO ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, construction waste is mainly treated by traditional open-air stacking and deep excavation for landfill. Although this method has a large processing capacity, is convenient and simple, and has low processing costs, it actually occupies a large amount of land resources and produces irreparable environmental pollution.
If such a large amount of construction waste cannot be recycled in time, it will not only pollute the environment, but also cause a serious waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Regenerated bricks and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The regenerated brick of this embodiment is made of the following raw materials: 20 kg of recycled construction waste aggregate, 15 kg of aggregate modifier, 5 kg of gelling agent, 20 kg of water reducing agent, 10 kg of regenerated magnesia carbon brick particles, 20 kg of steel fiber, zeolite Powder 5kg, slag 15kg, cement 30kg, water 90kg and polyamide 5kg, wherein, the construction waste regenerated aggregate refers to the construction waste obtained after crushing, sieving, and removing foreign matter, and the particle size is 2-10mm. The gelling agent is a mixture of light magnesium oxide, magnesium chloride and magnesium sulfate in a mass ratio of 50:20:30.

[0024] The preparation method of above-mentioned regenerated brick, comprises the steps:

[0025] (1) Take the following raw materials: 10kg recycled aggregate from construction waste, 25kg aggregate improver, 10kg gelling agent, 15kg water reducing agent, 5kg regenerated magnesia carbon brick particles, 15kg...

Embodiment 2

[0030] The regenerated brick of this embodiment is made of the following raw materials: 30 kg of recycled construction waste aggregate, 10 kg of aggregate modifier, 10 kg of gelling agent, 15 kg of water reducing agent, 15 kg of regenerated magnesia carbon brick particles, 15 kg of steel fiber, zeolite Powder 10kg, slag 10kg, cement 50kg, water 60kg and polyamide 10kg, wherein, the construction waste regenerated aggregate refers to the construction waste obtained after crushing, sieving, and removing foreign matter, and the particle size is 2-10mm. The gelling agent is a mixture of light magnesium oxide, magnesium chloride and magnesium sulfate in a mass ratio of 50:20:30.

[0031] The preparation method of above-mentioned regenerated brick, comprises the steps:

[0032] (1) Take the following raw materials: 25kg of recycled construction waste aggregate, 20kg of aggregate modifier, 15kg of gelling agent, 10kg of water reducing agent, 10kg of regenerated magnesia carbon brick p...

Embodiment 3

[0037] The regenerated brick of this embodiment is made of the following raw materials: 40 kg of recycled construction waste aggregate, 5 kg of aggregate modifier, 15 kg of gelling agent, 10 kg of water reducing agent, 20 kg of regenerated magnesia carbon brick particles, 10 kg of steel fiber, zeolite Powder 15kg, slag 5kg, cement 70kg, water 30kg and polyamide 15kg, wherein, the construction waste regenerated aggregate refers to the construction waste obtained after crushing, sieving and removing foreign matter, and the particle size is 2-10mm. The gelling agent is a mixture of light magnesium oxide, magnesium chloride and magnesium sulfate in a mass ratio of 50:20:30.

[0038] The preparation method of above-mentioned regenerated brick, comprises the steps:

[0039] (1) Take the following raw materials: 40kg of recycled construction waste aggregate, 15kg of aggregate modifier, 20kg of gelling agent, 5kg of water reducing agent, 15kg of regenerated magnesia carbon brick parti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses regenerated bricks and a preparation method thereof and belongs to the technical field of building materials. The regenerated bricks are prepared from the following raw materials in parts by weight: 20 to 40 parts of construction waste recycled aggregate, 5 to 15 parts of an aggregate modifier, 5 to 15 parts of a gelatinizing agent, 10 to 20 parts of a water reducer, 10 to20 parts of magnesia carbon brick regenerated grains, 10 to 20 parts of steel fibers, 5 to 15 parts of zeolite powder, 5 to 15 parts of furnace slag, 30 to 70 parts of cement, 30 to 90 parts of waterand 5 to 15 parts of polyamide. The regenerated bricks disclosed by the invention have the advantages of high strength, good wearing resistance, stable quality, long service life and low cost; wastescan be changed into valuable things, and environment protection and energy saving are realized; the regenerated bricks have very good economic benefits and wide social benefits.

Description

technical field [0001] The invention relates to a recycled brick and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] Construction waste is the main component of urban waste, accounting for about 30%-40% of the total urban waste. In 2004 alone, my country produced about 6 billion tons of construction waste, and the data from 2008 to 2011 must be far greater than this number. At present, construction waste is mainly treated by traditional open-air stacking and deep excavation and landfill. Although this method has a large processing capacity, is convenient and simple, and has low processing costs, it actually occupies a large amount of land resources and produces irreversible environmental pollution. If such a large amount of construction waste cannot be recycled in time, it will not only pollute the environment, but also cause a serious waste of resources. Contents of the invention [0003] One of the obj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/06C04B111/20
Inventor 黄云鸿李力
Owner GUILIN CHUNXIAO ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap