Energy-saving efficiency increasing primer-topcoat anti-corrosion coating and preparation method thereof

A technology for anti-corrosion coatings and bottom surfaces, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as personal safety threats, long intervals, environmental damage, etc., to reduce industrial three wastes, increase anti-corrosion performance, and market prospects broad effect

Inactive Publication Date: 2018-02-02
CHANGSHU FANGTA COATING CHEM
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to obtain a good anti-corrosion effect, it is usually necessary to carry out strict surface treatment on the substrate before painting, and it is generally necessary to use a primer, a primer, a topcoat, or a primer and a topcoat. The amount of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] An energy-saving and efficiency-enhancing bottom-surface-integrated anti-corrosion coating, comprising the following components in parts by weight: 30 parts of epoxy resin, 10 parts of water-based polyurethane resin, 25 parts of glass flakes, 10 parts of environmentally friendly pigments and fillers, 3 parts of silane coupling agent, 0.5 parts of thixotropic agent, 1 part of reactive diluent, 8 parts of curing agent, 1 part of auxiliary agent and 70 parts of solvent.

[0023] Wherein, the epoxy resin is a mixture of epoxy resins E-44 and E-20 in a mass ratio of 1:2.5.

[0024] The glass flakes have a flake structure with a size of 1.5-2 μm in thickness and 40-50 μm in average diameter.

[0025] The thixotropic agent is a mixture of fumed silica, castor oil and polyamide wax at a ratio of 2:1:1.5.

[0026] The curing agent is an aliphatic polyamine low-temperature curing agent; the solvent is deionized water.

[0027] The environment-friendly pigmen...

Example Embodiment

[0034] Example 2

[0035] An energy-saving and efficiency-enhancing bottom-surface-integrated anti-corrosion coating, comprising the following components in parts by weight: 40 parts of epoxy resin, 15 parts of water-based polyurethane resin, 30 parts of glass flakes, 15 parts of environmentally friendly pigments and fillers, 5 parts of silane coupling agent, 1.5 parts of thixotropic agent, 2 parts of reactive diluent, 15 parts of curing agent, 3 parts of auxiliary agent and 80 parts of solvent.

[0036] Wherein, the epoxy resin is a mixture of epoxy resins E-44 and E-20 in a mass ratio of 1:3.

[0037] The glass flakes have a flake structure with a size of 1.5-2 μm in thickness and 40-50 μm in average diameter.

[0038] The thixotropic agent is a mixture of fumed silica, castor oil and polyamide wax at a ratio of 3:1:1.5.

[0039] The curing agent is an aliphatic polyamine low-temperature curing agent; the solvent is deionized water.

[0040] The environment-friendly pigme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Average film diameteraaaaaaaaaa
Surface dry timeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an energy-saving efficiency increasing primer-topcoat anti-corrosion coating and a preparation method thereof. The anti-corrosion coating comprises epoxy resin, waterborne polyurethane resin, glass flakes, environment friendly pigments and fillers, silane coupling agents, thixotropic agents, activated diluents, curing agents, auxiliaries and solvents. The preparation methodincludes the steps: (1) glass flake pretreatment; (2) raw material mixing. By a reasonable formula design and the preparation method, the prepared anti-corrosion coating has excellent anti-corrosioneffects and long anti-corrosion effects, the anti-corrosion performance of the coating is effectively enhanced, the primer-topcoat coating can be directly sprayed and cured at low temperature, has rust removal functions and has the advantages of energy conservation, emission reduction, safety and environmental protection, the construction process is effectively simplified, industrial three industrial wastes are decreased, and the market prospect is wide.

Description

technical field [0001] The invention relates to the field of anti-corrosion coatings, in particular to an energy-saving and efficiency-enhancing bottom-surface-integrated anti-corrosion coating and a preparation method thereof. Background technique [0002] Corrosion greatly shortens the service life of steel and other equipment, causing a lot of waste of manpower and financial resources. For example, the direct and indirect economic losses caused by the shutdown and maintenance of large power stations due to equipment corrosion are very alarming; the corrosion of chemical equipment leads to frequent equipment accidents , the service life is reduced, and the loss caused is also great. Therefore, it is very necessary to develop anti-corrosion coatings with excellent performance to reduce or delay the corrosion of equipment and prolong its service life. [0003] As a simple and effective material protection and decoration method, paint coating can effectively improve the corr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D5/08C09D7/62C09D7/61C09D7/65C09D7/63
CPCC08K2003/321C08K2003/327C08L2205/025C08L2205/035C09D5/08C09D163/00C08L63/00C08L75/04C08L91/00C08L77/00C08K13/06C08K9/06C08K7/00C08K3/36C08K3/32
Inventor 钱强
Owner CHANGSHU FANGTA COATING CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap