Preparation method and application of visible light Fenton catalyst

A catalyst and visible light technology, applied in the direction of catalyst activation/preparation, chemical instruments and methods, heterogeneous catalyst chemical elements, etc., can solve the problems of insufficient reactivity and poor photocatalytic performance, and achieve a wide range of visible light response frequency, large Good specific surface area and good stability

Inactive Publication Date: 2018-02-09
周开珍
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] FeWO 4 It is a material with broad application prospects in the fields of optics, electricity, magnetism, conductor / superconductor, catalysis, and biology. Research hotspots for scientific researchers, but the current FeWO 4 Its photocatalytic performance is poor, and its reactivity in the visible light Fenton reaction is insufficient. Studies have found that its photo-Fenton reaction activity can be improved by doping and modifying it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of visible light Fenton composite catalyst, comprising the following steps:

[0024] (1) Take ferrous nitrate and lithium nitrate and add them to deionized water, so that the molar ratio of ferrous ions and lithium ions is 1:1, stir and dissolve to obtain solution A;

[0025] (2) Weigh Li 2 WO 4 2H 2 O was added to deionized water, stirred and dissolved to obtain Li 2 WO 4 solution, to Li 2 WO 4 Add isobutanol in the solution, the addition of isobutanol is every 1mmolM 2 WO 4 2H 2 O was added to 8mL, and stirred evenly to obtain solution B;

[0026] (3) Slowly add solution A to solution B and stir evenly so that the molar ratio of ferrous ions, lithium ions and tungsten ions is 2:2:1, then add sodium hydroxide solution to adjust the pH of solution B to 8.5, The mixture C was obtained, and the mixture C was transferred to a hydrothermal reactor and sealed, and reacted at 190° C. for 18 hours;

[0027] (4) After the reaction kettle is natur...

Embodiment 2

[0030] A preparation method of visible light Fenton composite catalyst, comprising the following steps:

[0031] (1) Take ferrous chloride and lithium nitrate and add them to deionized water, so that the molar ratio of ferrous ions and lithium ions is 1:1, stir and dissolve to obtain solution A;

[0032] (2) Weigh tungstate Na 2 WO 4 2H 2 O was added to deionized water, stirred and dissolved to obtain Na 2 WO 4 solution, to Na 2 WO 4 Add isobutanol in the solution, the addition amount of isobutanol is every 1mmol Na 2 WO 4 2H 2 Add 10mL of O and stir evenly to obtain solution B;

[0033] (3) Slowly add solution A to solution B and stir evenly so that the molar ratio of ferrous ions, lithium ions and tungsten ions is 2:2:1, then add sodium hydroxide solution to adjust the pH value of solution B to 8.8, The mixture C was obtained, and the mixture C was transferred to a hydrothermal reactor and sealed, and reacted at 195° C. for 16 hours;

[0034] (4) After the reactio...

Embodiment 3

[0036] A preparation method of visible light Fenton composite catalyst, comprising the following steps:

[0037] (1) Take ferrous sulfate and lithium nitrate and add them to deionized water, so that the molar ratio of ferrous ions and lithium ions is 1:1, stir and dissolve to obtain solution A;

[0038] (2) Weigh tungstate K 2 WO 4 2H 2 O was added to deionized water, stirred and dissolved to obtain K 2 WO 4 solution, to K 2 WO 4 Add isobutanol in the solution, the addition of isobutanol is every 1mmolK 2 WO 4 2H 2 O was added to 12mL and stirred evenly to obtain solution B;

[0039] (3) Slowly add solution A to solution B and stir evenly so that the molar ratio of ferrous ions, lithium ions and tungsten ions is 2:2:1, then add sodium hydroxide solution to adjust the pH value of solution B to 9.0, The mixture C was obtained, and the mixture C was transferred to a hydrothermal reactor and sealed, and reacted at 200° C. for 12 hours;

[0040] (4) After the reaction ke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method and application of a visible light Fenton catalyst, belonging to the technical field of photocatalyst preparation. The method includes the following steps: weighing soluble ferrous salt and soluble lithium salt in molar ratio and adding them into deionized water; weighing tungstate M2WO4·2H2O and adding them into deionized water; , The molar ratio of lithium ions and tungsten ions is 2:2:1, then add sodium hydroxide solution to make the solution alkaline, transfer the mixed solution to a hydrothermal reaction kettle for reaction; after the reaction is completed, centrifuge, and centrifuge the obtained precipitate After washing and drying, the visible light Fenton catalyst Li2Fe2WO7 powder is obtained. The method adopts a hydrothermal method to synthesize Li2Fe2WO7, the preparation method is simple and controllable, and the obtained product has better visible light catalytic activity. It can be used for the treatment of organic wastewater.

Description

【Technical field】 [0001] The invention relates to the technical field of photocatalyst preparation, in particular to a preparation method and application of a visible light Fenton catalyst. 【Background technique】 [0002] The development of green, efficient, economical and less secondary pollution environmental purification technology is an important research field of environmental pollution control and prevention technology. Photocatalytic technology achieves efficient degradation of organic pollutants by utilizing hydroxyl radicals generated during the reaction process, but most of the previous photocatalytic technologies use ultraviolet light as the excitation source, which has high cost, low light utilization efficiency, and natural sunlight Mid-ultraviolet light only accounts for <5%. In recent years, the use of solar photocatalysis to treat refractory organic pollutants in wastewater has attracted widespread attention from scholars at home and abroad. Introducing vi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/888B01J35/10B01J37/03B01J37/10C02F1/30C02F1/72C01G49/00C02F101/30
CPCB01J23/888B01J23/002B01J35/004B01J35/10B01J37/031B01J37/10B01J2523/00C01G49/009C02F1/30C02F1/725C02F2101/30C02F2305/026C02F2305/10B01J2523/11B01J2523/69B01J2523/842
Inventor 周开珍
Owner 周开珍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap