Wear-resisting wood floor board and preparation method thereof
A wood floor and wood-plastic technology, applied in construction, building structure, floor and other directions, can solve the problems of poor floor hardness and wear resistance, children and the elderly falling down, complicated production process, etc., and achieve strong adhesion and production technology. Simple, low-cost effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] A wear-resistant wooden floor, which comprises 30-60 parts by weight of nickel slag, 10-20 parts of tea leaves, 4-8 parts of titanium dioxide, 2-4 parts of bentonite, 2-6 parts of emulsion, and 2-6 parts of stearic acid 1 to 2 parts of wood-plastic impact-resistant filler, 1 to 2 parts of dispersant, and 1 to 2 parts of film-forming aid.
[0016] Described wear-resisting wooden floor, by weight, by 45 parts of nickel slag, 15 parts of tea leaves, 6 parts of titanium dioxide, 3 parts of bentonite, 4 parts of emulsion, 4 parts of stearic acid, 1.5 parts of wood-plastic impact-resistant filler, It consists of 1.5 parts of dispersant and 1.5 parts of film-forming aid.
[0017] The wear-resistant wooden floor and its preparation method include the following steps:
[0018] a. Mix nickel slag and tea leaves according to the ratio of 1:1, then add 1:1 bentonite and emulsion mixture, stir to obtain product A;
[0019] b. Add titanium dioxide and stearic acid to the prepared p...
Embodiment 2
[0022] A kind of wear-resisting wooden floor, by weight, by 30 parts of nickel slag, 10 parts of tea leaves, 4 parts of titanium dioxide, 2 parts of bentonite, 2 parts of emulsion, 2 parts of stearic acid, 1 part of wood-plastic impact-resistant filler, dispersed 1 part of agent, 1 part of film-forming aid.
[0023] The wear-resistant wooden floor and its preparation method include the following steps:
[0024] a. Mix nickel slag and tea leaves according to the ratio of 1:1, then add 1:1 bentonite and emulsion mixture, stir to obtain product A;
[0025] b. Add titanium dioxide and stearic acid to the prepared product A, then add wood-plastic anti-impact filler, dispersant and film-forming aid at a ratio of 1:1:1, stir and heat to 50-70°C, and mix well Stir, granulate, and extrude to form.
[0026] The wood-plastic impact-resistant filler is maleic anhydride grafted polyethylene.
Embodiment 3
[0028] A kind of wear-resisting wooden floor, by weight, by 60 parts of nickel slag, 20 parts of tea leaves, 8 parts of titanium dioxide, 4 parts of bentonite, 6 parts of emulsion, 6 parts of stearic acid, 2 parts of wood-plastic impact-resistant filler, dispersed 2 parts of agent and 2 parts of film-forming aid.
[0029] The wear-resistant wooden floor and its preparation method include the following steps:
[0030] a. Mix nickel slag and tea leaves according to the ratio of 1:1, then add 1:1 bentonite and emulsion mixture, stir to obtain product A;
[0031] b. Add titanium dioxide and stearic acid to the prepared product A, then add wood-plastic anti-impact filler, dispersant and film-forming aid at a ratio of 1:1:1, stir and heat to 50-70°C, and mix well Stir, granulate, and extrude to form.
[0032] The wood-plastic impact-resistant filler is maleic anhydride grafted polyethylene.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap