Composition of light-diffusing material and preparation method of composition

A composition and light diffusion technology, which is applied in the field of PC/PS alloy materials, can solve the problems of PC/PS alloy materials with light diffusion properties that have not yet been developed, and achieve the effect of cost reduction

Inactive Publication Date: 2018-02-23
中山市华塑塑胶科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above introductions are related to the research and development of PC / PS, PC / PS alloy materials with light diffusion properties have not yet been developed, and our country is still in a blank state in PC / PS alloy products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Composition of light-diffusing materials: Polycarbonate polymer (PC) is SABIC (formerly GE) PC 2200 accounting for 30%, polystyrene polymer (Zhanjiang Xinzhongmei 525 (white background)) accounting for 64%, organic Silicon-type light diffusing agent (Japan Shin-Etsu KMP-590) accounted for 0.8%, styrene-maleic anhydride copolymer compatibilizer (Shanghai Huawen SMA-700) accounted for 5%, antioxidant β-(3,5-di tert-butyl-4-hydroxyphenyl) n-octadecyl propionate (BASF Irganox 1076) accounted for 0.2%, antioxidant tris (2,4-di-tert-butylphenyl) phosphite (BASF Irganox 168 ) accounts for 0.1%, and the weather resistance agent 2-(2′-hydroxyl-5′-methylphenyl)benzotriazole (Tinuvin P produced by BASF) accounts for 0.2%.

[0024] The preparation process of the composition of the light diffusion material is as follows:

[0025] Step 1, calculate by weight percentage, first put into blast oven and dry 3 hours after polycarbonate polymer (PC) and polystyrene polymer (PS) are weighe...

Embodiment 2

[0029] Composition of light-diffusing materials: Polycarbonate polymer (PC) is SABIC (formerly GE) PC 2200 accounting for 40%, polystyrene polymer (Zhanjiang Xinzhongmei 525 (white background)) accounting for 54%, acrylic acid Resin-type light diffusing agent (Japan Zhongyuan Chemical MP90) accounted for 0.8%, styrene-maleic anhydride copolymer compatibilizer (Shanghai Huawen SMA-700) accounted for 5%, antioxidant β-(3,5-di tert-butyl-4-hydroxyphenyl) n-octadecyl propionate (BASF Irganox 1076) accounted for 0.2%, antioxidant tris (2,4-di-tert-butylphenyl) phosphite (BASF Irganox 168 ) accounted for 0.1%, weathering agent 2-(2'-hydroxy-5'-methylphenyl) benzotriazole (BASF Tinuvin P) accounted for 0.2%.

[0030] The preparation process of the composition of the light diffusion material of embodiment 2 is the same as the preparation process of the composition of the light diffusion material of embodiment 1, the difference is that the weight of each component in the composition of...

Embodiment 3

[0032] Composition of light-diffusing materials: Polycarbonate polymer (PC) is SABIC (formerly GE) PC2200 accounting for 50%, polystyrene polymer (Zhanjiang Xinzhongmei 525 (white background)) accounting for 44%, silicone Type light diffusing agent (Japan Shin-Etsu KMP-590) accounted for 0.8%, styrene-acrylonitrile-glycidyl methacrylate terpolymer (Jiangsu compatibilizer Jiangsu Co., Ltd. SAG-002) accounted for 5%, anti- Oxygen agent β-(3,5-di-tert-butyl-4-hydroxyphenyl) n-octadecyl propionate (BASF Irganox1076) accounts for 0.2%, antioxidant tris(2,4-di-tert-butylbenzene Base) phosphite (BASF Irganox 168) accounted for 0.1%, weathering agent bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate (BASF Tinuvin 770) accounted for 0.2%.

[0033]The preparation process of the composition of the light diffusion material of embodiment 3 is the same as the preparation process of the composition of the light diffusion material of embodiment 1, the difference is that the weight of each comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composition of a light-diffusing material and a preparation method of the composition. The composition comprises, by weight, 30-45% of polycarbonate polymers, 55-65% of polystyrene polymers, 0.6-0.8% of light-diffusing agent, 0.5-5% of compatilizers, 0.3-0.8% of antioxidant and 0.2-0.6% of weather-proofing agent. The light-diffusing PC / PS alloy material has the advantagesof high mobility, light transmittance, haze and temperature resistance.

Description

technical field [0001] The invention relates to the technical field of PC / PS alloy materials, in particular to a composition of a light diffusion material and a preparation method thereof. Background technique [0002] In recent years, there have been many studies on light-diffusing PCs. Most of the light diffusion plates are based on polycarbonate polymer (PC), and different types of diffusing agents are added to obtain different effects. With rising raw material prices, LED manufacturers are looking for alternatives to light-diffusing PC. At this time, a light-diffusing PS material appears. The light-diffusing PS material is based on polystyrene, which can greatly reduce the cost of the lampshade material. However, not all environments are suitable for the use of light-diffusing PS. The long-term heat resistance of light-diffusing PS is only between 66°C and 75°C, and it will deform when the LED is lit for a long time. [0003] Japan's Idemitsu Co., Ltd. saw the market ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L69/00C08L35/06C08L33/00C08K5/134C08K5/526C08K5/3475B29C47/92B29C48/92
CPCC08L25/06B29C48/92B29C2948/92704C08L69/00C08L2201/08C08L2201/10C08L2203/20C08L35/06C08K5/1345C08K5/526C08K5/3475C08L33/00C08L25/08C08K5/3435
Inventor 颜红兵司徒冠明
Owner 中山市华塑塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap