Anti-corrosion treatment process for parts of sampling machine

A technology of anti-corrosion treatment and sampling machine, which is applied to anti-corrosion coatings, pre-treated surfaces, special surfaces, etc., can solve the problems of anti-corrosion layer falling off, and achieve the effect of avoiding impact and friction and avoiding penetration

Inactive Publication Date: 2018-03-06
SICHUAN XINGZHI ZHIHUI INTPROP OPERATION CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide anticorrosion treatment process for sampler parts, so as

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1:

[0022] The anti-corrosion treatment process of sampling machine components includes the following steps:

[0023] 1) The surface of each part of the sampling machine is cleaned of impurities and rust;

[0024] 2). The surface of each part of the sampling machine after step 1) is frosted;

[0025] 3). Immerse the sampling tube of the sampling machine in the matured rare earth preservative. After the rare earth preservative is deposited on the surface of the sampling tube, take it out and dry it naturally at room temperature. The temperature of the sampling tube during the immersion deposition process is 80 ℃, the immersion time is 30minmin, the rare earth preservative is a mixture of aminopropyltriethoxysilane, lanthanum oxide, ethanol and deionized water in a weight ratio of 3:1:3:4, and the curing treatment Is to stand for 60 hours at room temperature;

[0026] 4) Spray the surface of other parts of the sampling machine with the cured rare earth preservative;

[00...

Example Embodiment

[0028] Example 2:

[0029] The anti-corrosion treatment process of sampling machine components includes the following steps:

[0030] 1) The surface of each part of the sampling machine is cleaned of impurities and rust;

[0031] 2). The surface of each part of the sampling machine after step 1) is frosted;

[0032] 3). Immerse the sampling tube of the sampling machine in the cured rare earth preservative. After the rare earth preservative is deposited on the surface of the sampling tube, take it out and dry it naturally at room temperature. The temperature of the sampling tube during the immersion deposition process is 130 ℃, the immersion time is 60min, the rare earth preservative is a mixture of aminopropyltriethoxysilane, lanthanum oxide, ethanol and deionized water in a weight ratio of 3:1:3:4, and the aging treatment is Let stand for 70 hours at room temperature;

[0033] 4) Spray the surface of other parts of the sampling machine with the cured rare earth preservative;

[0034] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-corrosion treatment process for parts of a sampling machine. The anti-corrosion treatment process comprises the following steps that 1), impurity removal and rust removal are carried out on the surface of each part of the sampling machine; 2), sanding is carried out on the surface of each part which is subjected to the treatments in the step 1) of the sampling machine; 3), a sampling pipe of the sampling machine is soaked in rare-earth preservative which is subjected to a curing treatment, the rare-earth preservative is taken out after deposited on the surface of the sampling pipe, and then the rare-earth preservative is naturally air-dried at normal temperature; 4) the rare-earth preservative which is subjected to the curing treatment is sprayed on the surfaces of the other parts of the sampling machine; and 5), the sampling pipe which is subjected to the treatment in the step 3) is coated with an antioxygenic resin layer, and the other parts of the sampling machine are coated with the antioxygenic resin layer. According to the anti-corrosion treatment process, on one hand, the corrosion-resistant layer can be prevented from being impacted and rubbed and the anti-corrosion layer is firmly adhered to the surface of the sampling pipe, and on the other hand, the problem that the surface of the sampling pipe is corroded and damaged as oxygen and water in the atmosphere permeate and diffuse to the surface of the sampling pipe can be prevented.

Description

Technical field [0001] The invention relates to the technical field of beneficiation, in particular to an anticorrosive treatment process for sampling machine parts. Background technique [0002] In the process of beneficiation, due to the heavy workload, it is impossible to take all the materials for analysis; also cannot take some materials for analysis at will, but through sampling, obtain the test of appropriate weight, properties and composition representative of the raw materials. Sample, then analyze and test. The process of collecting a part of the sample from a large batch of materials is called sampling. [0003] The equipment used for sampling is a sampling machine. In order to meet the stability of its structure, the sampling machine is generally made of metal. During the sampling process, the sampling machine will directly contact the sample and cause the corrosion of the sampling parts. The corrosion ability of the sample is different. The degree of corrosion varies...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B05D5/00B05D3/00B05D7/24C09D5/08
Inventor 谭逢林
Owner SICHUAN XINGZHI ZHIHUI INTPROP OPERATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products