Antibacterial polypyrrole/sulfosalicylic acid nanorod and preparation method and application thereof

A technology of sulfosalicylic acid and polypyrrole, applied in the field of medical biological materials, can solve problems such as normal cytotoxicity, and achieve the effects of improving biological activity, improving antibacterial properties and good biocompatibility

Inactive Publication Date: 2018-03-13
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the silver ion antibacterial coating has good antibacterial properties, it is highly toxic to normal cells

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial polypyrrole/sulfosalicylic acid nanorod and preparation method and application thereof
  • Antibacterial polypyrrole/sulfosalicylic acid nanorod and preparation method and application thereof
  • Antibacterial polypyrrole/sulfosalicylic acid nanorod and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of antibacterial polypyrrole / sulfosalicylic acid nanorods, comprising the following steps:

[0031] (1) Pretreatment of the titanium sheet: Soak the electrode material titanium sheet in 1mol / L hydrochloric acid for 10 minutes to remove the surface oxide layer, and then ultrasonically clean it in deionized water, absolute ethanol and acetone for 20 minutes to remove the oil on the surface and other impurities, after vacuum drying;

[0032] (2) Select a three-electrode system, use the titanium sheet after step (1) as the working electrode, the copper sheet as the counter electrode, and the saturated calomel electrode as the reference electrode, and use the mixed solution of pyrrole monomer and sulfosalicylic acid As an electrolyte solution, by electrochemical constant current method (the current density is 0.6mA / cm 2 , the reaction time is 10min, and the temperature of the reaction is normal temperature), polymerized on the surface of the working ele...

Embodiment 2

[0040] A preparation method of antibacterial polypyrrole / sulfosalicylic acid nanorods, comprising the following steps:

[0041] (1) Pretreatment of the titanium sheet: Soak the electrode material titanium sheet in 1mol / L hydrochloric acid for 10 minutes to remove the surface oxide layer, and then ultrasonically clean it in deionized water, absolute ethanol and acetone for 20 minutes to remove the oil on the surface and other impurities, after vacuum drying;

[0042] (2) Select a three-electrode system, use the titanium sheet after step (1) as the working electrode, the copper sheet as the counter electrode, and the saturated calomel electrode as the reference electrode, and use the mixed solution of pyrrole monomer and sulfosalicylic acid As an electrolyte solution, by electrochemical constant current method (the current density is 0.7mA / cm 2 , the reaction time is 10min, and the reaction temperature is 25°C), polymerize on the surface of the working electrode to obtain polyp...

Embodiment 3

[0045] An antibacterial polypyrrole / sulfosalicylic acid nanorod and a preparation method thereof, comprising the following steps:

[0046] (1) Pretreatment of the titanium sheet: soak the electrode material titanium sheet in 1 mol / L hydrochloric acid for 10 minutes to remove the surface oxide layer, and then ultrasonically clean it in deionized water, absolute ethanol and acetone for 30 minutes in turn to remove the oil on the surface. and other impurities, use after vacuum drying;

[0047] (2) Selecting a three-electrode system, using the titanium sheet treated in step (1) as the working electrode, the copper sheet as the counter electrode, the saturated calomel electrode as the reference electrode, and using the mixed solution of pyrrole monomer and sulfosalicylic acid It is an electrolyte solution by electrochemical constant current method (current density is 1.5mA / cm 2 , the reaction time was 10 min, and the reaction temperature was 25 °C), polypyrrole / sulfosalicylic acid n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of medical biomaterials and discloses an antibacterial polypyrrole / sulfosalicylic acid nanorod and a preparation method and application thereof. The methodcomprises that through a three-electrode system with a metal material as a working electrode, a mixed solution of a pyrrole monomer and sulfosalicylic acid as an electrolyte solution undergo a polymerization reaction on the surface of the working electrode through an electrochemical constant current method to produce a polypyrrole / sulfosalicylic acid nanorod, wherein the mixed solution of a pyrrole monomer and sulfosalicylic acid is obtained by dissolving a pyrrole monomer and sulfosalicylic acid in a phosphate buffer solution. The polypyrrole / sulfosalicylic acid nanorod is produced on the surface of the working electrode so that surface biological activity and antibacterial performances are improved. The preparation method has simple processes and a stable structure and has a potential application value in the field of the biological material.

Description

technical field [0001] The invention belongs to the technical field of medical biological materials, and relates to a polypyrrole / sulfosalicylic acid nanorod with antibacterial properties and a preparation method and application thereof. Background technique [0002] Medical titanium and its alloys are commonly used hard tissue implant materials in clinical practice. They have good biocompatibility, mechanical properties and machining properties, and are ideal hard tissue replacement materials. However, an inert biological layer is easily formed on the surface of pure titanium, and there are problems such as poor biological activity and poor antibacterial properties, which restrict the application and development of titanium and its alloy bone repair materials. In order to improve the antibacterial performance of titanium and its alloy materials, the current main research approach is to construct silver ion-loaded or antibiotic coatings. Although silver-ion-loaded antibacte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/54A61L27/06A61L27/34A61L27/50C25D9/02
CPCA61L27/06A61L27/34A61L27/50A61L27/54A61L2300/404A61L2430/02C25D9/02C08L79/04
Inventor 宁成云周文浩于鹏翟锦霞易新陈俊琪
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com