Medical self-adhesive elastic bandage preparation method

A self-adhesive elastic bandage, medical technology, applied in bandages, medical science, absorbent pads and other directions, can solve the problems of human skin allergy, not easy to tear, feel greasy, etc., achieve excellent air permeability, strong acid and alkali resistance, reduce stimulatory effect

Inactive Publication Date: 2018-03-16
安徽斯麦特医学技术开发有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the adhesives used in self-adhesive elastic bandages at home and abroad mainly use natural latex or its modified products. Due to the presence of protein in natural latex, it is easy to cause human skin allergies, and long-term storage will cause corruption, mold, and deterioration. Therefore, Natural rubber latex or its modified products are gradually replaced by artificially synthesized adhesives. In the prior art, adhesives for self-adhesive elastic bandages have the disadvantages of being sticky to the hand, greasy to the touch, and too strong to be easily torn apart.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of medical self-adhesive elastic bandage, comprising the following steps:

[0017] (1) In parts by weight, mix 32 parts of methacrylic anhydride, 18 parts of methyl methacrylate, 10 parts of methyl acrylate, 24 parts of deionized water, and 3 parts of dodecylamine, and heat to 75°C, Stir continuously for 60min to prepare mixed emulsion;

[0018] (2) Slowly add the modifier to the mixed emulsion prepared in step (1), raise the temperature of the mixed solution to 86°C, keep stirring for 300 minutes, cool to room temperature, and filter with a 150-mesh sieve. A binder is prepared, wherein the modifying agent is made of the following components by weight: 16 parts of trifluoroethyl acrylate, 35 parts of methyl tributylketoximosilane, and 3 parts of potassium persulfate;

[0019] (3) After adding a stabilizer to the adhesive prepared in step (2), stir evenly, and then paint the prepared adhesive on both sides of the elastic bandage to obtain a medical ...

Embodiment 2

[0025] A preparation method of medical self-adhesive elastic bandage, comprising the following steps:

[0026] (1) In parts by weight, mix 34 parts of methacrylic anhydride, 20 parts of methyl methacrylate, 14 parts of methyl acrylate, 26 parts of deionized water, and 5 parts of dodecylamine, and heat it to 78°C. Stir continuously for 65min to obtain a mixed emulsion;

[0027] (2) Slowly add the modifier to the mixed emulsion prepared in step (1), raise the temperature of the mixed solution to 88°C, keep stirring for 330 minutes, cool to room temperature, and filter with a 150-mesh sieve. A binder is prepared, wherein the modifying agent is made of the following components by weight: 20 parts of trifluoroethyl acrylate, 38 parts of methyl tributylketoxime silane, and 5 parts of potassium persulfate;

[0028] (3) After adding a stabilizer to the adhesive prepared in step (2), stir evenly, and then paint the prepared adhesive on both sides of the elastic bandage to obtain a med...

Embodiment 3

[0034] A preparation method of medical self-adhesive elastic bandage, comprising the following steps:

[0035] (1) In parts by weight, after mixing 36 parts of methacrylic anhydride, 22 parts of methyl methacrylate, 16 parts of methyl acrylate, 30 parts of deionized water and 6 parts of dodecylamine, heated to 80°C, Stir continuously for 70min to prepare mixed emulsion;

[0036] (2) Slowly add the modifier to the mixed emulsion prepared in step (1), raise the temperature of the mixed solution to 90°C, keep stirring for 350 minutes, cool to room temperature, and filter with a 150-mesh sieve. A binder is prepared, wherein the modifying agent is made of the following components by weight: 22 parts of trifluoroethyl acrylate, 40 parts of methyl tributylketoximosilane, and 6 parts of potassium persulfate;

[0037] (3) After adding a stabilizer to the adhesive prepared in step (2), stir evenly, and then paint the prepared adhesive on both sides of the elastic bandage to obtain a me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a medical self-adhesive elastic bandage, which comprises the following steps: (1) After mixing methacrylic anhydride, methyl methacrylate, methyl acrylate, deionized water and laurylamine, heating to After 75-80°C, keep stirring for 60-70min to prepare a mixed emulsion; (2) Slowly add modifier to the mixed emulsion prepared in step (1), and raise the temperature of the mixed solution to 86-90 ℃, keep stirring for 300‑350min, cool to room temperature, and filter through a 150-mesh sieve to obtain the binder; (3) add stabilizer to the binder prepared in step (2), stir evenly, Then the finished adhesive is painted on the front and back sides of the elastic bandage to obtain a medical self-adhesive elastic bandage. In the medical self-adhesive elastic bandage prepared by the invention, the adhesive does not stick to the skin, has no greasy feeling, does not strain the wound when it is torn off, and has excellent air permeability.

Description

technical field [0001] The invention belongs to the technical field of medical bandage preparation, and in particular relates to a preparation method of medical self-adhesive elastic bandage. Background technique [0002] Bandages are widely used in real life, and different injuries use different bandages. Self-adhesive elastic bandages are widely used in various industries such as medical dressing, industrial operation protection, field operation, and sports protection. This kind of self-adhesive bandage is sprayed with a layer of adhesive on the front and back of traditional medical bandages. The self-adhesiveness between them greatly facilitates bandaging and fixing, increases air permeability, and also reduces the skin pain after tearing off. At present, the adhesives used in self-adhesive elastic bandages at home and abroad mainly use natural latex or its modified products. Due to the presence of protein in natural latex, it is easy to cause human skin allergies, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/24A61L15/58A61L15/42
CPCA61L15/28A61L15/24A61L15/42A61L15/58C08L5/04C08L33/00
Inventor 张明
Owner 安徽斯麦特医学技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap