Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

An epoxy permeable brick

A technology of permeable bricks and epoxy, which is applied in the field of building materials, can solve the problems of serious energy consumption and high cost of permeable bricks, and achieve the effects of improving production efficiency, facilitating fabrics, and simple processes

Active Publication Date: 2021-03-26
重庆亲禾生态环境科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the problems of high cost and serious energy consumption of the permeable bricks in the prior art, and provide a new epoxy permeable brick. Through the selection of raw materials and specific proportion design, the epoxy permeable brick has Good water permeability and wear resistance, but also has the advantages of low cost and easy production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An epoxy permeable brick
  • An epoxy permeable brick
  • An epoxy permeable brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An epoxy permeable brick, comprising a base material and a fabric, the fabric being composed of the following raw materials by weight: 1936 g of silica sand, 153.6 g of bisphenol A epoxy resin, 45.1 g of T31 curing agent, and 59.84 g of hydrophilic curing agent g, 1.1 g of coupling agent KH560, 2.4 g of water and 3.3 g of nano silicon dioxide modified by coupling agent.

[0027] The fineness of the silica sand in this embodiment is 70-120 mesh.

[0028] The curing agent in this embodiment is a polyamine curing agent phenalkamine.

[0029] The hydrophilic curing agent in this embodiment is a curing agent containing highly active primary amine, secondary amine or tertiary amine group in the molecular chain, and the main chain or side chain of the molecule contains a hydrophilic group. Further, this embodiment The hydrophilic curing agent in the example is a polyamine modified curing agent with a molecular weight of 2000.

[0030] The epoxy resin in this embodiment is bi...

Embodiment 2

[0032] An epoxy permeable brick, comprising a base material and a lining, the lining is composed of the following raw materials by weight: 1864g of silica sand, 67.6g of epoxy resin, 19g of curing agent, 21.4g of hydrophilic curing agent, and 12g of coupling agent , water 12g and nano silicon dioxide 2g.

[0033] The fineness of the silica sand in this embodiment is 40-70 mesh.

[0034] The curing agent in this embodiment is polyamine curing agent polyamide.

[0035] The hydrophilic curing agent in this embodiment is a curing agent containing highly active primary amine, secondary amine or tertiary amine group in the molecular chain, and the main chain or side chain of the molecule contains a hydrophilic group. Further, this embodiment The hydrophilic curing agent in the example is a polyamine modified curing agent with a molecular weight of 2000.

[0036] The epoxy resin in this embodiment is bisphenol F.

Embodiment 3

[0038] An epoxy permeable brick, comprising a base material and a lining, the lining is composed of the following raw materials by weight: 1800g of silica sand, 92.4g of epoxy resin, 23.2g of curing agent, 70g of hydrophilic curing agent, and 4.4g of coupling agent g, water 7.2g and nano silicon dioxide 2.8g.

[0039] The fineness of the silica sand in this embodiment is 40-70 mesh.

[0040] The curing agent in this embodiment is polyamine aromatic amine.

[0041] The hydrophilic curing agent in this embodiment is a curing agent containing highly active primary amine, secondary amine or tertiary amine group in the molecular chain, and the main chain or side chain of the molecule contains a hydrophilic group. Further, this embodiment The hydrophilic curing agent in the example is a polyamine modified curing agent with a molecular weight of 600.

[0042] The epoxy resin in this embodiment is bisphenol S.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an epoxy water-permeable brick and belongs to the technical field of building materials. The water-permeable brick comprises a bottom layer and a surface layer; the surface layer comprises the following raw materials in parts by weight: 88-96 parts of silica sand, 1.95-6.86 parts of epoxy resin, 0.39-2.05 parts of a curing agent, 0.5-5.4 parts of a hydrophilic curing agent,0.05-3.00 parts of a coupling agent, 0.05-3.00 parts of water and 0.1-0.5 part of nano silica. According to the invention, the hydrophilic curing agent and the non-hydrophilic resin are used so thata water permeation function is realized. Compared with the prior art, the water-permeable brick has the advantages that the raw materials are easy to obtain, the process is simple, the preparation cost is low, the prepared water-permeable brick is ecological and environmentally friendly, and the water-permeable, wear-resistant and water-retaining properties are good.

Description

technical field [0001] The invention relates to a permeable brick, in particular to an epoxy permeable brick, which belongs to the technical field of building materials. Background technique [0002] Permeable bricks originated in the Netherlands. During the process of building the city from the sea, the Dutch found that the ground after the sea water was drained would cause continuous land subsidence due to long-term lack of contact with water. Once the dykes on the coastline are washed away, the seawater will quickly rush to cities much lower than sea level and submerge the entire coastal city. In order to prevent the ground from sinking, the Dutch made a small pavement brick with a length of 200 mm, a width of 100 mm, and a height of 50 or 60 mm, which was laid on the street surface, and a gap of 2 mm was reserved between the bricks. In this way, when it rains, the rainwater will seep into the ground through the gaps between the bricks. Afterwards, the Shubroko Company ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/14
CPCC04B26/14C04B2111/00284C04B2111/00612C04B14/06C04B24/121C04B22/002C04B14/062C04B24/302C04B24/42C04B24/287C04B2103/0068
Inventor 邓华余朝洪甘小炎王田堂杜涛杨昕熊浩
Owner 重庆亲禾生态环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com