System and method for producing pellet

A technology for pellets and green pellets, which is applied in the field of systems for producing pellets, can solve the problems of low single-machine production capacity, high production and maintenance costs, uneven heating, etc., so as to reduce equipment and production costs and shorten production processes. Process, the effect of reducing the amount of powder returned

Pending Publication Date: 2018-03-20
JIANGSU PROVINCE METALLURGICAL DESIGN INST
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shaft furnace roasting process is the earliest pellet roasting method adopted in the world. The drying, preheating, roasting and cooling of the green pellets are all carried out and completed in a rectangular shaft furnace. This method has simple process, compact structure and low investment. , but due to its small single-machine production capacity and poor adaptability to raw materials, it is generally only suitable for roasting magnetite pellets, and cannot handle hematite, limonite, etc., uneven heating, poor product quality, etc. However, there are many insurmountable flaws in this method, which make this method more problematic
The belt roasting machine process requires a large amount of heat-resistant alloy steel, high production and maintenance costs, high requirements for the stability of raw materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • System and method for producing pellet
  • System and method for producing pellet
  • System and method for producing pellet

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0074] Example 1

[0075] Add 53.6% of a hematite TFe, mixed with bentonite and water to make pellets. The green pellets have a particle size of 8-16mm and a moisture content of 8.7%; the green pellets are stepped into the annular roasting device and the pellets are made The pellet passes through the drying zone, the preheating zone, the roasting zone and the soaking zone in sequence to be dried, preheated, roasted and soaked in order to obtain metallized pellets. The angle of the drying zone is 80° and the temperature is 250°C; The angle of the preheating zone is 105° and the temperature is 350-950°C; the angle of the baking zone is 135° and the temperature is 1350°C; the angle of the soaking zone is 40° and the temperature is 1100°C; the thickness of the cloth is 60mm. The metalized pellets are cooled to obtain pellets, wherein the average compressive strength of the pellets is 2695N / ball, and the FeO content is 0.21%.

Example Embodiment

[0076] Example 2

[0077] A certain magnetite TFe61.2%, mixed with bentonite and water to make pellets, the particle size of the green pellets is 8-16mm, and the moisture content is 9.3%; the green pellets are stepped into the annular roasting device and the pellets are made The pellets go through drying zone, preheating zone, roasting zone and soaking zone in order to be dried, preheated, roasted and soaked in order to obtain metallized pellets. The angle of the drying zone is 75° and the temperature is 200 ℃; the angle of the preheating zone is 135° and the temperature is 400-1000℃; the angle of the baking zone is 120° and the temperature is 1250°C; the angle of the soaking zone is 30° and the temperature is 1050°C; the thickness of the cloth is 100mm. The metalized pellets are cooled to obtain pellets, wherein the average compressive strength of the pellets is 3250N / ball, and the FeO content is 0.63%.

Example Embodiment

[0078] Example 3

[0079] A certain limonite TFe 45.6% is mixed with bentonite and water to make pellets to obtain a green pellet with a particle size of 8-16 mm and a moisture content of 12.3%; the green pellets are stepped into the annular roasting device and the pellets are made The pellets pass through the drying zone, preheating zone, roasting zone and soaking zone in sequence to dry, preheat, roast and soak in order to obtain metallized pellets, where the angle of the drying zone is 105° and the temperature is 300°C; The angle of the preheating zone is 120° and the temperature is 400-1000°C; the angle of the baking zone is 105° and the temperature is 1300°C; the angle of the soaking zone is 30° and the temperature is 1000°C; the thickness of the cloth is 150mm. The metalized pellets are cooled to obtain pellets, wherein the average compressive strength of the pellets is 2234N / ball, and the FeO content is 0.81%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a system and a method for producing a pellet, wherein the system comprises a pellet making device, an annular roasting device and a cooling device; the pellet making device comprises an iron-containing material inlet, an additive inlet, a water inlet and a raw pellet outlet; the annular roasting device comprises an annular furnace body and a plurality of nozzles; a furnacechamber is defined inside the furnace body; a drying region, a preheating region, a roasting region and a uniform heating region which communicate with one another are defined in the furnace chamber;the drying region comprises a feeding hole which is connected with the raw pellet outlet; the preheating region and the roasting region are each provided with a flue; the uniform heating region comprises a discharging hole; the bottom wall of the annular furnace body is rotatable and is suitable for supporting a material to sequentially pass through the drying region, the preheating region, the roasting region and the uniform heating region; and the plurality of nozzles are arranged on the inner wall of the annular furnace body and are suitable for injecting gas and air into the furnace chamber. The system is low in equipment cost and production cost and applicable to various iron-containing materials, and when being adopted for producing the pellet, the system also has the advantages of short technological process, good pellet quality and the like.

Description

technical field [0001] The invention belongs to the field of metallurgy, in particular, the invention relates to a system and method for producing pellets. Background technique [0002] At present, the main roasting processes of pellets mainly include shaft furnace pellet production process, belt roaster pellet production process and chain grate-rotary kiln pellet production process. The shaft furnace roasting process is the earliest pellet roasting method adopted in the world. The drying, preheating, roasting and cooling of the green pellets are all carried out and completed in a rectangular shaft furnace. This method has simple process, compact structure and low investment. , but due to its small single-machine production capacity and poor adaptability to raw materials, it is generally only suitable for roasting magnetite pellets, and cannot handle hematite, limonite, etc., uneven heating, poor product quality, etc. However, there are many problems in this method due to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/24C22B1/02C22B1/26
CPCC22B1/02C22B1/2406C22B1/26
Inventor 闫方兴任中山石晓莉曹志成吴道洪
Owner JIANGSU PROVINCE METALLURGICAL DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap