Micro-alloy building steel bar containing V, Nb and Cr and production method of micro-alloy building steel bar

A production method and construction steel technology, applied in the field of iron and steel metallurgy, can solve the problems of low nitrogen content and few types of vanadium nitride alloys, and achieve the effects of high nitrogen yield, simple operation, and stable nitrogen yield

Inactive Publication Date: 2018-03-20
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of low nitrogen content and few types of vanadium nitride alloys used in the preparation of nitrogen-containing alloy steels, the present invention provides a new method for preparing nitrogen-containing alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Micro-alloy building steel bar containing V, Nb and Cr and production method of micro-alloy building steel bar
  • Micro-alloy building steel bar containing V, Nb and Cr and production method of micro-alloy building steel bar
  • Micro-alloy building steel bar containing V, Nb and Cr and production method of micro-alloy building steel bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1 uses the inventive method to prepare containing V, Nb, Cr microalloy building steel bar

[0050] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 150mm×150mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0051] First, add 120 tons of molten iron and 20 tons of steel scrap into the converter, and the added molten iron S is 0.59%. After the molten iron and steel scrap are added to the converter, the molten iron and steel scrap are initially smelted into molten steel by using the function of the converter to remove C by blowing oxygen. When the composition...

Embodiment 2

[0062] Embodiment 2 prepares containing V, Nb, Cr microalloy building steel bar with the inventive method

[0063] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 200mm×200mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0064] Firstly, 120 tons of molten iron and 20 tons of scrap steel are added into the converter, and the S content of the added molten iron is 0.051%. After the molten iron and steel scrap are added to the converter, the molten iron and steel scrap are initially smelted into molten steel by using the function of the converter to blow oxygen to remove C. W...

Embodiment 3

[0075] Embodiment 3 prepares the bar material containing V, Nb, Cr microalloy building steel with the inventive method

[0076] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 200mm×200mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0077] Firstly, 120 tons of molten iron and 20 tons of steel scrap are added into the converter, and the S content of the added molten iron is 0.050%. After the molten iron and steel scrap are added to the converter, the molten iron and steel scrap are initially smelted into molten steel by using the function of the converter to blow oxygen t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of steel and iron metallurgy and particularly relates to a micro-alloy building steel bar containing V, Nb and Cr and a production method of the micro-alloy buildingsteel bar to solve the problem that a selected vanadium nitride alloy for preparing nitrogen-containing alloy steel is low in nitrogen content and few in variety. The micro-alloy building steel bar comprises the components of, by weight, 0.15-0.30% of C, 0.30-1.00% of Si, 0.60-1.30% of Mn, 0.0060-0.0180% of N, 0.040% or the less of P, 0.040% or the less of S, 0.010-0.100% of V, 0.010-0.030% of Nb, 0.10-0.60% of Cr and the balance Fe and inevitable impurities. The key of the preparation method is that an N-containing core-spun yarn is fed on a small platform behind a furnace, and N is adjustedto the appropriate level. According to the production method, operation is easy, the nitrogen yielding rate is high and stable, the production cost can further be effectively reduced, and thus the micro-alloy building steel bar and the LF production method are worthy of being used and popularized.

Description

technical field [0001] The invention belongs to the field of iron and steel metallurgy, and in particular relates to a microalloy building steel bar containing V, Nb and Cr and a production method thereof. Background technique [0002] Microalloyed steel mainly refers to the steel whose performance can be obviously improved by adding a small amount or a trace amount of certain elements in the steel, especially the strength index of the steel. Under the existing technical conditions, microalloyed steel is mainly obtained by adding a small amount or a small amount of vanadium, niobium and titanium. The mechanism of microalloying is: after adding vanadium, niobium and titanium as trace elements into molten steel, they combine with carbon and nitrogen in molten steel to form carbon and nitrogen compound particles, namely V(C, N), Nb( C, N) and Ti (C, N) particles, these particles have a certain effect of precipitation strengthening and grain refinement, which can significantly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/24C22C38/26C21D8/08
CPCC22C38/02C21D8/065C21D8/08C22C38/001C22C38/04C22C38/24C22C38/26
Inventor 邓通武刘明郭跃华冉准
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com