Non-cement-based ceramic tile adhesive

A tile adhesive, non-cement technology, which is applied in the field of building materials, can solve the problems of tile falling off, etc., and achieve the effect of improving heat-resistant adhesive strength and flexibility, high flexibility, and strong cohesion

Inactive Publication Date: 2018-03-27
桂林市漓江机电制造有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problem in the prior art that tile adhesives tend to fall off when bonding on high-temperature, large-deformed substrates, the present invention provides a non-cement-based tile adhesive with high viscosity, high toughness and high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-cement-based ceramic tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of non-cement base ceramic tile adhesive, its raw material and parts by weight are as follows:

[0018] 35 parts of quartz sand, 1 part of basalt fiber, 1 part of redispersible latex powder, 0.5 part of carbon fiber, 0.5 part of water-retaining agent, 25 parts of emulsion, 0.2 part of film-forming aid, and 0.2 part of defoamer.

Embodiment 2

[0020] A kind of non-cement base ceramic tile adhesive, its raw material and parts by weight are as follows:

[0021] 40 parts of quartz sand, 1.5 parts of basalt fiber, 2 parts of redispersible latex powder, 1 part of carbon fiber, 0.6 part of water retaining agent, 28 parts of emulsion, 0.3 part of film-forming aid, and 0.3 part of defoamer.

Embodiment 3

[0023] A kind of non-cement base ceramic tile adhesive, its raw material and parts by weight are as follows:

[0024] 60 parts of quartz sand, 2 parts of basalt fiber, 3 parts of redispersible latex powder, 2 parts of carbon fiber, 0.8 part of water retaining agent, 30 parts of emulsion, 0.4 part of film-forming aid, and 0.4 part of defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a non-cement-based tile adhesive, which comprises the following raw materials in parts by weight: 35-60 parts of quartz sand, 1-2 parts of basalt fiber, 1-3 parts of redispersible latex powder, and 0.5-2 parts of carbon fiber , 0.5-0.8 parts of water-retaining agent, 25-30 parts of emulsion, 0.2-0.4 parts of film-forming aid, and 0.2-0.4 parts of defoaming agent. The non-cement-based tile adhesive provided by the invention has strong cohesive force, high temperature resistance, and much higher flexibility than cement-based products, which can effectively solve the problem of tiles that are prone to appear when cement-based products are bonded to high-temperature, large-deformed bases. Shedding problem.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a non-cement based tile adhesive. Background technique [0002] At present, most of the tile adhesives on the market are cement-based tile adhesives. Cement-based tile adhesives are rigid products and are used in some special places, such as high-temperature places, areas with large vibrations, and large deformation of the base layer. , there are certain security risks. Contents of the invention [0003] Aiming at the problem in the prior art that tile adhesives tend to fall off when bonding on high-temperature and large-deformed substrates, the present invention provides a non-cement-based tile adhesive with high viscosity, high toughness and high temperature resistance. [0004] The present invention is achieved through the following technical solutions: [0005] A non-cement-based tile adhesive, comprising the following raw materials in parts by weight: 35-60 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/06
CPCC04B26/06C04B2111/00637C04B2201/50C04B24/06C04B14/4643C04B24/2623C04B14/386C04B24/383C04B24/42C04B24/023C04B24/045
Inventor 方杰敏
Owner 桂林市漓江机电制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap