A kind of wind power blade and preparation method thereof

A technology for wind power blades and shells, applied in the field of wind power blades and their preparation, can solve the problems of lack of toughness and unreliable strength of wind power blades, and achieves enhanced strength and toughness, simple and reasonable preparation method, high tensile strength and elasticity. The effect of modulus

Active Publication Date: 2019-10-29
上海玻璃钢研究院东台有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, wind power generation is generally carried out through large-scale wind power blades, and the strength performance of wind power blades is particularly critical. The current wind power blades are generally formed by pouring epoxy resin into each part and then bonding them. Fibers improve the strength of wind turbine blades. The most commonly used reinforcing fibers are glass fibers and carbon fibers. However, the strength of wind turbine blades made of such materials is not very reliable and has no toughness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wind power blade and preparation method thereof
  • A kind of wind power blade and preparation method thereof
  • A kind of wind power blade and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Such as figure 1 and 2 As shown, a wind turbine blade includes an upper shell 1 , a lower shell 2 , and an edge connecting portion 3 . Both ends of the upper shell 1 and the lower shell 2 are fixedly connected by two edge connecting parts 3 . The inner side of the upper housing 1 is provided with a plurality of upper arc-shaped grooves 11 . The inner side of the lower shell 2 is provided with a plurality of lower arc-shaped grooves 21 . Both the upper arc-shaped groove 11 and the lower arc-shaped groove 21 are provided with reinforcing ribs 4, and the reinforcing ribs 4 include boron fibers and gypsum whiskers, and the mass ratio of boron fibers and gypsum whiskers is 3:1. The upper shell and the lower shell include epoxy resin and nylon fiber, and the mass ratio of nylon fiber to epoxy resin is 1:5. The edge connection part includes epoxy resin, glass fiber, gypsum whisker, and nano-scale aluminum oxide, wherein the weight parts of epoxy resin, glass fiber, gypsum ...

Embodiment 2

[0035] Such as figure 1 and 2 As shown, a wind turbine blade includes an upper shell 1 , a lower shell 2 , and an edge connecting portion 3 . Both ends of the upper shell 1 and the lower shell 2 are fixedly connected by two edge connecting parts 3 . The inner side of the upper housing 1 is provided with a plurality of upper arc-shaped grooves 11 . The inner side of the lower shell 2 is provided with a plurality of lower arc-shaped grooves 21 . Both the upper arc-shaped groove 11 and the lower arc-shaped groove 21 are provided with reinforcing ribs 4, and the reinforcing ribs 4 include boron fibers and gypsum whiskers, and the mass ratio of boron fibers and gypsum whiskers is 3:1.5. The upper shell and the lower shell include epoxy resin and nylon fiber, and the mass ratio of nylon fiber and epoxy resin is 1:7. The edge connection part includes epoxy resin, glass fiber, gypsum whisker, and nano-scale aluminum oxide, wherein the weight parts of epoxy resin, glass fiber, gyps...

Embodiment 3

[0042] Such as figure 1 and 2As shown, a wind turbine blade includes an upper shell 1 , a lower shell 2 , and an edge connecting portion 3 . Both ends of the upper shell 1 and the lower shell 2 are fixedly connected by two edge connecting parts 3 . The inner side of the upper housing 1 is provided with a plurality of upper arc-shaped grooves 11 . The inner side of the lower shell 2 is provided with a plurality of lower arc-shaped grooves 21 . Both the upper arc-shaped groove 11 and the lower arc-shaped groove 21 are provided with reinforcing ribs 4, and the reinforcing ribs 4 include boron fibers and gypsum whiskers, and the mass ratio of boron fibers and gypsum whiskers is 3:2. The upper shell and the lower shell include epoxy resin and nylon fiber, and the mass ratio of nylon fiber to epoxy resin is 1:10. The edge connection part includes epoxy resin, glass fiber, gypsum whisker, and nano-scale aluminum oxide, wherein the weight parts of epoxy resin, glass fiber, gypsum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wind power blade and a preparation method thereof. The wind power blade comprises an upper-side shell, a lower-side shell and edge connecting portions. The two ends of the upper-side shell and the two ends of the lower-side shell are fixedly connected through the two edge connecting portions. The preparation method comprises the steps of shell manufacturing, reinforcementrib manufacturing and edge connecting portion manufacturing. The strength of the wind power blade is comprehensively improved.

Description

technical field [0001] The invention relates to the field of wind power generation, in particular to a wind power blade and a preparation method thereof. Background technique [0002] Wind power generation refers to converting the kinetic energy of the wind into electrical energy. Wind is a pollution-free energy source. The use of wind power generation is very environmentally friendly and can generate huge amounts of electricity. Therefore, more and more countries pay more attention to wind power generation. At present, wind power generation is generally carried out through large-scale wind power blades, and the strength performance of wind power blades is particularly critical. The current wind power blades are generally formed by pouring epoxy resin into each part and then bonding them. Fibers improve the strength of wind turbine blades. The most commonly used reinforcing fibers are glass fibers and carbon fibers. However, the strength of wind turbine blades made of such m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F03D1/06B29C70/44B29C70/74B29D99/00C08L63/00C08K7/14C08K7/08C08K7/24C08K7/06
CPCB29C70/443B29C70/745B29D99/0025B29K2063/00B29K2105/08B29K2105/12B29K2105/126B29L2031/085C08K7/06C08K7/08C08K7/14C08K7/24C08K2201/011C08K2201/016F03D1/0675C08L63/00Y02E10/72Y02P70/50
Inventor 吉玉峰夏保付韩飞张文艳张永金
Owner 上海玻璃钢研究院东台有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com