Foam card board and preparation method of same

A pallet and low-density polyethylene technology, which is applied in the field of pallets, can solve the problems of unfavorable promotion and application of wooden pallets, unfavorable promotion and application, and high price of wooden pallets, and achieves easy placement and handling, light material and low self-weight. Effect

Inactive Publication Date: 2018-04-27
DONGGUAN HEYONG PACKING
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal pallets, due to their bulkiness and high price, are not conducive to popularization and application based on cost considerations
Due to the shortage of wood, the price of wooden pallets is getting higher and higher. From the perspective of reducing costs and meeting environmental protection requirements, wooden pallets are not conducive to popularization and application, and wooden pallets need strict inspections when entering and exiting customs. formalities, further restricting its application; although cardboard has the advantages of environmental protection and light weight, it also has disadvantages such as poor mechanical properties, small load-bearing capacity and easy damage, which is easy to cause huge losses to cargo transportation
With the development of science and technology, plastic pallets have appeared, but the existing plastic pallets have problems such as high cost and heavy weight.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of foam card board, is made up of the following raw materials of weight part:

[0036] Low-density polyethylene 100 parts

[0037] Butane 0.5 parts

[0038] Talc powder 0.5 parts

[0039] Glyceryl monostearate 1 part.

[0040] The melt flow rate (190° C. / 2.16 kg) of the low-density polyethylene was 0.85 g / 10 min.

[0041] The density of the low density polyethylene is 0.92g / cm³.

[0042] The maximum transverse elongation of the low-density polyethylene is twice that of the longitudinal maximum elongation.

[0043] A kind of preparation method of foam pallet, comprises the following steps:

[0044] (1) Extrude and foam the raw materials;

[0045] (2) Forming the foamed material into a sheet;

[0046] (3) Cutting, hot pressing several layers of foam sheets to obtain the bearing surface and supporting feet of the foam pallet;

[0047] (4) Press the four supporting feet on a bearing surface to obtain a foam pallet.

[0048] The temperature of step (3) and st...

Embodiment 2

[0051] A kind of foam card board, is made up of the following raw materials of weight part:

[0052] Low-density polyethylene 100 parts

[0053] 1 part butane

[0054] 1 part talcum powder

[0055] Glyceryl monostearate 1 part

[0056] Erucamide 0.05 parts

[0057] Silicon dioxide 0.1 part.

[0058] The melt flow rate (190° C. / 2.16 kg) of the low-density polyethylene was 0.9 g / 10 min.

[0059] The density of the low-density polyethylene is 0.925g / cm³.

[0060] The maximum transverse elongation of the low-density polyethylene is twice that of the longitudinal maximum elongation.

[0061] A kind of preparation method of foam pallet, comprises the following steps:

[0062] (1) First blend low-density polyethylene, erucamide, and silicon dioxide to obtain blended pellets, then blend the blended pellets, talcum powder, and glyceryl monostearate under the action of butane extrusion foaming;

[0063] (2) Forming the foamed material into a sheet;

[0064] (3) Cutting, hot pr...

Embodiment 3

[0069] A kind of foam card board, is made up of the following raw materials of weight part:

[0070] Low density polyethylene 100 parts

[0071] Butane 1.2 parts

[0072] Talcum powder 1.2 parts

[0073] Glyceryl monostearate 1.5 parts

[0074] Erucamide 0.08 parts

[0075] Silicon dioxide 0.15 parts.

[0076] The melt flow rate (190° C. / 2.16 kg) of the low-density polyethylene was 0.91 g / 10 min.

[0077] The density of the low density polyethylene is 0.93g / cm³.

[0078]The maximum transverse elongation of the low-density polyethylene is three times that of the longitudinal maximum elongation.

[0079] A kind of preparation method of foam pallet, comprises the following steps:

[0080] (1) Blend low-density polyethylene, erucamide, and silicon dioxide first to obtain blended pellets, then extrude the blended pellets, talcum powder, and glyceryl monostearate under the action of butane foaming;

[0081] (2) Forming the foamed material into a sheet;

[0082] (3) Cutting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of card board and particularly relates to a foam card board and a preparation method of same. The foam card board includes, by weight, 100 parts of low-density polyethylene, 0.5-1.5 parts of butane, 0.5-1.5 parts of talcum powder, and 1-2 parts of glyceryl monostearate. Being different from wood card boards, the foam card board can pass customs freely,so that a limitation that the wood card board needs strict procedures during entrance and exit through the customs. Meanwhile, resource waste problem is solved by using plastic materials instead of wood and paper. The foam card board is light in weight, has functions of heat insulation, sound insulation, shock buffering and high specific strength. The foam card board also is anti-corrosion, insect-preventing, damp-proofing and mildew-proofing, is light in self weight, can be applied for long period at temperature of -70 to 130 DEG C without deformation, is high in mechanical performance, is high in bearing capacity, is easy to move during transportation, and is free of abrasion and damage during transportation of objects requiring high demands, so that the foam card board can protect the transported objects well.

Description

technical field [0001] The invention relates to the technical field of pallets, in particular to a foamed pallet and a preparation method thereof. Background technique [0002] Pallets, also called pallets, are loading and unloading pads that are used to facilitate cargo loading and unloading, transportation, storage, and distribution. They consist of a load surface that can carry a certain number of items and a forklift socket. Pallets have a wide range of uses, mostly used in food, beverages, beer, medicine, textiles, automobile manufacturing, electronic appliances, hardware machinery, logistics centers, turnover goods, and goods on shelves to facilitate cargo loading and unloading. [0003] Since the pallet is an important carrier of goods, it not only requires a relatively high load-bearing capacity, but also requires its own light weight to help reduce transportation costs. [0004] Traditional pallets include metal pallets, wooden pallets and paper pallets. Metal pal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K13/02C08K3/34C08K5/103C08K5/20C08K3/36C08K7/14C08K3/22C08K13/04C08J9/14
CPCC08J9/0023C08J9/0028C08J9/0066C08J9/0071C08J9/0085C08J9/0095C08J9/141C08J2203/14C08J2323/06
Inventor 孙和永
Owner DONGGUAN HEYONG PACKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products