Salt-tolerant non-cured waterproof coating and production process thereof

A waterproof coating and production process technology, applied in the direction of polyester coating, asphalt coating, epoxy resin coating, etc., can solve the problems of poor salt resistance, difficulty in achieving waterproof effect, easy to be corroded and peeled off, etc., to improve heat resistance and The effect of salt resistance

Active Publication Date: 2018-04-27
河南蓝翎环科防水材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current non-curing waterproof coating has poor salt resistance, making it extremely easy to be corroded and peeled off in a salty environment, making it difficult to achieve long-term waterproofing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The present embodiment provides a salt-resistant non-curing waterproof coating, the composition of which includes by parts by weight:

[0031] 60 parts of modified emulsified asphalt, 40 parts of isocyanate, 20 parts of polyethylene terephthalate particles, 15 parts of mica powder, 5 parts of polyisobutylene, 16 parts of aluminum tripolyphosphate, 15 parts of hydantoin epoxy resin, and 16 parts of anionic polyacrylamide.

[0032] Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 80 parts of base asphalt, 3 parts of SBR rubber powder, cetyl bromide 4 parts of pyridine.

[0033] The production process of this salt-resistant non-curing waterproof coating includes:

[0034] Mix modified emulsified asphalt, isocyanate, polyethylene terephthalate particles and anionic polyacrylamide in parts by weight, heat to 100°C, and keep warm for 4 ho...

Embodiment 2

[0037] The present embodiment provides a salt-resistant non-curing waterproof coating, the composition of which includes by parts by weight:

[0038] 70 parts of modified emulsified asphalt, 30 parts of isocyanate, 30 parts of polyethylene terephthalate particles, 10 parts of mica powder, 8 parts of polyisobutylene, 12 parts of aluminum tripolyphosphate, 30 parts of hydantoin epoxy resin, and 10 parts of triethanolammonium salt.

[0039] Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 70 parts of base asphalt, 10 parts of SBR rubber powder, cetyl bromide 6 parts of pyridine.

[0040] The production process of this salt-resistant non-curing waterproof coating includes:

[0041] Mix the modified emulsified asphalt, isocyanate, polyethylene terephthalate particles and triethanolammonium salt in parts by weight, heat to 150°C, and keep it war...

Embodiment 3

[0044] The present embodiment provides a salt-resistant non-curing waterproof coating, the composition of which includes by parts by weight:

[0045] 65 parts of modified emulsified asphalt, 37 parts of isocyanate, 24 parts of polyethylene terephthalate particles, 13 parts of mica powder, 6 parts of polyisobutylene, 14 parts of aluminum tripolyphosphate, 24 parts of hydantoin epoxy resin, and 15 parts of succinate ester sulfonate salt.

[0046] Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 75 parts of base asphalt, 7 parts of SBR rubber powder, cetyl bromide 5 parts pyridine.

[0047] The production process of this salt-resistant non-curing waterproof coating includes:

[0048]Mix the modified emulsified asphalt, isocyanate, polyethylene terephthalate particles and succinate ester sulfonate salt in parts by weight, and heat to 135°C and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a salt-tolerant non-cured waterproof coating, and belongs to the field of waterproof materials. The salt-tolerant non-cured waterproof coating comprises the following componentsin parts by weight: modified emulsified asphalt, isocyanate, polyethylene terephthalate particles, mica powder, polyisobutene, aluminium triphosphate, glycolylurea epoxide resin and an anionic surfactant. A preparation process comprises the following steps: mixing the modified emulsified asphalt, the isocyanate, the polyethylene terephthalate particles and the anionic surfactant in parts by weight to obtain a fused matrix; and then mixing the glycolylurea epoxide resin, the aluminium triphosphate and the fused matrix, heating the mixture for 40-70 minutes at the temperature of 180-200 DEG C,cooling to the temperature of 60-80 DEG C and then adding the mica powder and the polyisobutene, and then stirring 70-90 min. The coating is good in waterproofness, and has high salt tolerance, long waterproof characteristic can be maintained in a salty environment, and the adhesive property and the self-healing property are good.

Description

technical field [0001] The invention relates to the field of waterproof materials, in particular to a salt-resistant non-curing waterproof coating and a production process thereof. Background technique [0002] Non-curing rubber asphalt waterproof coating, made of rubber and asphalt as the main component, mixed with additives, is a waterproof coating that maintains a viscous paste within the service life. It has a prominent effect on the waterproof treatment of special parts such as deformation joints in construction projects, and is widely used in non-exposed building waterproof projects. [0003] Non-curing rubber asphalt waterproof coating is a kind of creep waterproof coating, which also has good bonding ability with metal, non-metal and concrete substrates, and has dual functions of waterproof and metal anticorrosion. Non-curing rubber asphalt waterproof coating has many advantages, such as: it will never harden, the cured content is more than 99%, does not contain vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D109/06C09D163/00C09D167/02C09D123/20C09D133/26C09D7/61C09D7/63
CPCC08K2003/327C08L2201/08C08L2205/035C09D195/00C08L9/06C08L63/00C08L67/02C08L23/22C08L33/26C08K13/02C08K3/32C08K3/34C08K5/29
Inventor 李宏伟苏怀武牛恒李翔
Owner 河南蓝翎环科防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap