Coal gasification coarse slag non-fired material and preparation method thereof

A technology of coal gasification and coarse slag, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problems of high energy consumption, low utilization rate of raw materials, and low efficiency

Inactive Publication Date: 2018-05-11
CHINA UNIV OF MINING & TECH (BEIJING)
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current ceramsite production process is still mainly high-temperature sintering method. In view of the continuous increase in the cost of raw materials and energy at this stage, and most production units have problems such as high energy consumption, low efficiency, and low utilization of raw materials, this is to a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coal gasification coarse slag non-fired material and preparation method thereof
  • Coal gasification coarse slag non-fired material and preparation method thereof
  • Coal gasification coarse slag non-fired material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0063]The present invention also provides a method for preparing the above-mentioned non-burning material, comprising: S) mixing 63-75 parts by weight of coal gasification coarse slag, 15-25 parts by weight of cement and 10-12 parts by weight of quartz sand with water , curing after molding to obtain non-burning materials; the mass ratio of the coal gasification coarse slag to cement is (4-5):1 or (2-2.52):1.

[0064] Wherein, the coal gasification coarse slag, cement and quartz sand are all the same as above, and will not be repeated here.

[0065] According to the present invention, the particle size of the coal gasification coarse slag is preferably 60 mesh or less; the raw material of the coal gasification coarse slag is preferably dried first, pulverized and then sieved to obtain the coal gasification coarse slag; the drying temperature is preferably 100°C to 120°C, more preferably 100°C to 110°C, and more preferably 105°C; the drying time is preferably 1 to 3 hours, more...

Embodiment 1～7 and comparative example 1～2

[0083] Raw material pretreatment: put the coal gasification coarse slag in an oven at 105°C for 2 hours to make it completely dry; then use a grinder to crush the dried coarse slag raw material for 2 minutes to grind the coarse slag finely; then use a 60-mesh sieve to sieve, The dry and finely ground coal cinder under the sieve was used as the test raw material, and then the coal gasification coarse slag raw material was dissolved in 32% (relative to the dry material) of 5% NaOH solution, stirred for 5 min and then filtered, and the filter residue on the filter paper was dried. as test material;

[0084] Cement can be directly used in the test without treatment;

[0085] Dry the quartz sand and crush it, then sieve the crushed quartz sand with a 60-mesh sieve, and take the dry and fine quartz sand powder as the test auxiliary material.

[0086] Mixing of raw materials: the pretreated raw materials, according to the proportioning in Table 3 (experimental group 1 is comparative...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Angleaaaaaaaaaa
Login to view more

Abstract

The invention provides a non-fired material. The non-fired material comprises, by weight, 63-75 parts of coal gasification coarse slag, 15-25 parts of cement and 10-12 parts of quartz sands; and a mass ratio of the coal gasification coarse slag to the cement is (4-5):1 or (2-2.52):1. Compared with materials in the prior art, the non-fired material has the following advantages: the coal gasification coarse slag, cement and quartz sands are mixed according to a certain ratio, the quartz sands are used to supplement glass in the coal gasification coarse slag, and the cement is used to improve theactivity of the coal gasification coarse slag, so the hardening speed of the non-fired material is accelerated, and the strength of the non-fired material is increased.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a burning-free material and a preparation method thereof. Background technique [0002] Coal gasification coarse slag has a huge output, low calorific value, and large particle size. The existing disposal and utilization methods at home and abroad are not very effective. Generally, landfill or open-air stacking are used for disposal, but these disposal methods not only encroach on precious soil resources , and because it contains heavy metal elements such as chromium (Cr) and arsenic (As), and the content of each polycyclic aromatic hydrocarbon component far exceeds the maximum content standard stipulated by the international public health and environmental organization, it has caused great harm to the environmental medium and human health. The threat of risk will also cause air pollution due to dust escape. Therefore, it is particularly important to study...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B18/02C04B18/06
CPCC04B18/027C04B18/021C04B14/06C04B18/065Y02W30/91
Inventor 张凯刘舒豪翟宇嘉
Owner CHINA UNIV OF MINING & TECH (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap