Colored stone and fiber concrete artistic board as well as manufacturing method and application thereof

A technology of fiber concrete and colored stone, applied in the field of building decoration materials, can solve the problems of long construction time, poor durability of GRC components, damage to the natural environment, etc., and achieve the effect of high bending strength, high compressive strength and wide sources

Inactive Publication Date: 2018-06-19
高志斌 +1
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, stone carving is expensive and takes a long time to build, and the mining of natural stone will destroy the natural environment, and the waste, dust, and waste water generated by the processing of natural stone will pollute the environment
The durability of GRC components is poor. After several years of u

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored stone and fiber concrete artistic board as well as manufacturing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A method for making a colored stone fiber concrete art board, comprising the steps of:

[0038]S1: Mix 1000 parts of colored stones, 825 parts of quartz sand, 355 parts of cement, 4 parts of kaolin, 3.6 parts of water reducing agent, 2 parts of retarder, 0.5 parts of coloring agent and 160 parts of water, and stir to form a surface layer slurry;

[0039] S2: 1000 parts of gravel, 825 parts of medium sand, 5.3 parts of alkali-resistant glass fiber, 355 parts of cement, 4 parts of kaolin, 3.6 parts of water reducer, 2 parts of defoamer, 2 parts of cellulose ether, and 2 parts of retarder 160 parts and 160 parts of water are mixed and stirred to form the base layer slurry;

[0040] S3: The polystyrene board is used to make a model with a ratio of 1:1 to the surface to be decorated. After repeated corrections, the bolts are pre-embedded in place after the mold is turned over with silica gel, and 5mm of surface slurry is sprayed on the surface of the silica gel mold, and it ...

Embodiment 2

[0043] A method for making a colored stone fiber concrete art board, comprising the steps of:

[0044] S1: Mix 977 parts of colored stones, 800 parts of quartz sand, 335 parts of cement, 3 parts of kaolin, 4 parts of water reducing agent, 2 parts of retarder, 0.5 parts of colorant and 154 parts of water, and stir to form a surface layer slurry;

[0045] S2: 977 parts of gravel, 800 parts of medium sand, 5 parts of alkali-resistant glass fiber, 335 parts of cement, 3 parts of kaolin, 4 parts of water reducing agent, 2 parts of defoaming agent, 2 parts of cellulose ether, and 2 parts of retarder 154 parts and 154 parts of water are mixed and stirred to form the base layer slurry;

[0046] S3: The polystyrene board is used to make a model with a ratio of 1:1 to the surface to be decorated. After repeated corrections, the bolts are pre-embedded in place after the mold is turned over with silica gel, and 5mm of surface slurry is sprayed on the surface of the silica gel mold, and it...

Embodiment 3

[0049] A method for making a colored stone fiber concrete art board, comprising the steps of:

[0050] S1: Mix 939 parts of colored stones, 800 parts of quartz sand, 382 parts of cement, 4 parts of kaolin, 3 parts of water reducing agent, 2 parts of retarder, 0.5 parts of colorant and 169 parts of water, and stir to form a surface layer slurry;

[0051] S2: 939 parts of gravel, 800 parts of medium sand, 5.5 parts of alkali-resistant glass fiber, 382 parts of cement, 4 parts of kaolin, 3 parts of water reducer, 2 parts of defoamer, 2 parts of cellulose ether, and 2 parts of retarder After mixing with 169 parts of water, stir to form the base layer slurry;

[0052] S3: The polystyrene board is used to make a model with a ratio of 1:1 to the surface to be decorated. After repeated corrections, the bolts are pre-embedded in place after the mold is turned over with silica gel, and 5mm of surface slurry is sprayed on the surface of the silica gel mold, and it is pressed in place. ,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a colored stone and fiber concrete artistic board as well as a manufacturing method and an application thereof. The colored stone and fiber concrete artistic board is formed by at least two layers of structures including a base layer and a surface layer on the base layer, wherein the base layer is a fiber concrete layer and comprises raw materials as follows: macadam, medium sand, alkali-resistant glass fiber, cement, kaolin, a water reducing agent, a defoaming agent, cellulose ether, a retarder and water; the surface layer is a colored stone concrete layer, and comprises raw materials as follows: colored stone, quartz sand, cement, kaolin, a water reducing agent, a retarder, a coloring agent and water. The surface of the colored stone and fiber concrete artistic board has a natural stone effect, and the artistic board can be hung on an external maintenance structure of a building to replace natural stone to form a building decorative surface, and has the characteristics of beauty, economy, environment friendliness and high efficiency.

Description

technical field [0001] The invention belongs to the field of building decoration materials, and in particular relates to a colored stone fiber concrete art board, its production method and application. Background technique [0002] At present, in order to achieve the European-style architectural effect, stone carving, GRC components, masonry plastering and paint are generally used for decoration. However, stone carving is expensive and takes a long time to build, and the mining of natural stone will destroy the natural environment, and the waste, dust, and waste water produced by the processing of natural stone will pollute the environment. The durability of GRC components is poor. After several years of use, some GRC component buildings have been damaged and corroded, and some have caused potential safety hazards. Masonry plastering can be used in small buildings or buildings with simple line shapes, it is difficult to achieve complex artistic shapes, and the durability of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B111/82C04B111/54
CPCC04B28/04C04B2111/00612C04B2111/542C04B2111/82C04B2201/20C04B2201/50C04B18/12C04B14/06C04B14/44C04B14/106C04B2103/302C04B24/32C04B24/06C04B2103/54C04B14/00
Inventor 高志斌宋鹍韩向阳赵川李晓莉
Owner 高志斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap