Flame-retardant polycarbonate material for electronic products and preparation method of flame-retardant polycarbonate material

A technology of flame-retardant polycarbonate and electronic products, which is applied in the field of engineering plastics, can solve the problems of flame retardancy, impact resistance and environmental safety, etc. The effect of anti-dripping effect

Inactive Publication Date: 2018-06-29
HEFEI SIBOT SOFTWARE DEV CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned analysis of the prior art, the present invention provides a flame-retardant polycarbonate material for electronic products and a preparation method thereof to solve the incompatibility of flame retardancy, impact resistance and environmental safety of existing polycarbonate materials. The technical problems obtained, and the preparation method is simple, suitable for large-scale production and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A flame-retardant polycarbonate material for electronic products, comprising the following components according to parts by mass:

[0044] Polycarbonate 45 parts;

[0045] 20 parts of polybutylene terephthalate;

[0046] 5 parts of methyl phenyl silicone resin;

[0047] 3 parts of polysiloxane;

[0048] 7 parts of triphenylphosphine oxide;

[0049] Anti-drip agent 0.3 parts;

[0050] Toughening agent 0.1 part;

[0051] Antioxidant 0.1 part;

[0052] Heat stabilizer 0.3 parts.

[0053] Wherein, the polycarbonate is bisphenol A polycarbonate, and its relative density is 1.20g / m 3 , Vicat softening temperature of 140 ℃, melt index of 25g / min.

[0054] Wherein, the polysiloxane is a polysiloxane containing epoxy functional groups at the end groups.

[0055] Wherein, the anti-drip agent is polytetrafluoroethylene.

[0056] Wherein, the toughening agent is ethylene-glycidyl methacrylate.

[0057] Wherein, the antioxidant is selected from at least one of hindered ph...

Embodiment 2

[0063] A flame-retardant polycarbonate material for electronic products, comprising the following components according to parts by mass:

[0064] Polycarbonate 54 parts;

[0065] 35 parts of polybutylene terephthalate;

[0066] 9 parts of methyl phenyl silicone resin;

[0067] 6 parts of polysiloxane;

[0068] 12 parts of triphenylphosphine oxide;

[0069] Anti-drip agent 1.8 parts;

[0070] 1 part of toughening agent;

[0071] Antioxidant 0.5 part;

[0072] Heat stabilizer 1.2 parts.

[0073] Wherein, the polycarbonate is bisphenol A polycarbonate, and its relative density is 1.24g / m 3 , Vicat softening temperature of 150 ℃, melt index of 35g / min.

[0074]Wherein, the polysiloxane is a polysiloxane containing epoxy functional groups at the end groups.

[0075] Wherein, the anti-drip agent is polytetrafluoroethylene.

[0076] Wherein, the toughening agent is ethylene-glycidyl methacrylate.

[0077] Wherein, the antioxidant is selected from at least one of hindered p...

Embodiment 3

[0083] A flame-retardant polycarbonate material for electronic products, comprising the following components according to parts by mass:

[0084] Polycarbonate 49.5 parts;

[0085] 27.5 parts of polybutylene terephthalate;

[0086] 7 parts of methyl phenyl silicone resin;

[0087] Polysiloxane 4.5 parts;

[0088] 9.5 parts of triphenylphosphine oxide;

[0089] 1 part of anti-drip agent;

[0090] Toughening agent 0.6 part;

[0091] Antioxidant 0.3 parts;

[0092] Heat stabilizer 0.8 parts.

[0093] Wherein, the polycarbonate is bisphenol A polycarbonate, and its relative density is 1.22g / m 3 , Vicat softening temperature of 145 ℃, melt index of 30g / min.

[0094] Wherein, the polysiloxane is a polysiloxane containing epoxy functional groups at the end groups.

[0095] Wherein, the anti-drip agent is polytetrafluoroethylene.

[0096] Wherein, the toughening agent is ethylene-glycidyl methacrylate.

[0097] Wherein, the antioxidant is selected from at least one of hinde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Vicat softening pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant polycarbonate material for electronic products and a preparation method of the flame-retardant polycarbonate material. A coating mainly comprises polycarbonate, polybutylene terephthalate, methylphenyl silicone resin, polysiloxane, triphenylphosphine oxide, an anti-dripping agent, a toughening agent, an antioxidant and a heat stabilizer. The flame-retardant polycarbonate material provided by the invention has good flame retardancy, excellent impact resistance, good light-shielding effect, lower toxicity in exposure to a high temperature than that of aconventional heat-emitting flame-retardant polycarbonate material, environmental protection and safety; housings of electronic products processed by the flame-retardant polycarbonate material have flame retardancy meeting requirements on flame retardant rating.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a flame-retardant polycarbonate material for electronic products and a preparation method thereof. Background technique [0002] Polycarbonate (PC) is one of the five widely used engineering plastics. It has comprehensive and balanced mechanical, electrical and heat resistance properties. It is especially famous for its excellent impact strength and creep resistance, high light transmittance and good mechanical properties. In particular, the impact toughness is the best among engineering plastics. Due to the excellent properties of PC, its products and their blended materials have been widely used in electronic products. [0003] Polycarbonate (PC) has a certain self-extinguishing property and emits CO2 when burning, and its flame retardant performance is better than that of ordinary plastics. However, in some occasions with high flame retardant requirements, furth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L83/04C08L27/18C08L23/08C08K5/5397
CPCC08L69/00C08L2201/02C08L2203/20C08L2205/025C08L2205/035C08L67/02C08L83/04C08L27/18C08L23/0884C08K5/5397
Inventor 吴青明
Owner HEFEI SIBOT SOFTWARE DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap