A kind of production technology of nano-silver wire transparent conductive film

A technology of transparent conductive film and nano-silver wire, applied in conductive coatings, coatings, etc., can solve the problem of few patents of nano-silver wire transparent conductive film, save manpower and material resources, reduce haze, and improve production efficiency.

Active Publication Date: 2021-04-30
LUCKY HUAGUANG GRAPHICS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are very few patents on the industrialization of nano-silver wire transparent conductive film, especially an industrialized method that can produce high-quality nano-silver wire transparent conductive film with high yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production technology of nano-silver wire transparent conductive film
  • A kind of production technology of nano-silver wire transparent conductive film
  • A kind of production technology of nano-silver wire transparent conductive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of production method of nano-silver wire transparent conductive film, comprises the following steps:

[0035](1) Substrate preparation: apply the prepared hardened coating solution on the PET film base. In terms of weight percentage, the main components of the hardened layer coating solution are: 7% pure acrylic resin, 11% ten-functional polyurethane resin %, 20% of difunctional polyurethane resin, 6% of lauric acid acrylate, 6% of methyl benzoylformate, 50% of methyl ethyl ketone; the film base is hardened; the hardness of the non-nano silver wire coated surface of the PET film base is More than 1H; light transmittance 92%, haze ≤ 0.7%, thickness of PET film base is 100μm, dyne value of coating surface ≥ 50, no cracks on the surface after hot pressing at 190°C and 5Mpa for 30 seconds; the prepared The PET film base is placed on the supply rack;

[0036] (2) Coating nano-silver wire coating solution and protective glue coating solution: the configured nano-silve...

Embodiment 2

[0044] The main steps and methods of this embodiment are the same as those of Example 1, and will not be repeated here. The difference is that 1. the composition of the hardening layer coating solution is: 5% pure acrylic resin, 13% ten-functional polyurethane resin, and two Functional group polyurethane resin 26%, tetrahydrofurfuryl acrylate 6%, phenyl bis(2,4,6-trimethylbenzoyl) phosphine oxide 3%, ethylene glycol 47%; ②Nano silver wire coating Coating amount is 10mL / m 2 .

[0045] The performance index of the transparent conductive film finished product that the present invention produces is as shown in table 2 below:

[0046] The performance index of the transparent conductive film finished product that table 2 embodiment of the present invention 2 produces

[0047]

Embodiment 3

[0049] The main steps and methods of this embodiment are the same as those of Example 1, and will not be repeated here. The difference is that 1. the composition of the hardening layer coating solution is: 5% pure acrylic resin, 18% ten-functional polyurethane resin, and two Functional group polyurethane resin 23%, tripropylene glycol diacrylate 5%, 1-hydroxy-cyclohexyl-phenyl ketone 3%, acetone 46%; ②The coating amount of nano-silver wire coating is 50mL / m 2 .

[0050] The performance index of the transparent conductive film finished product that the present invention produces is as shown in table 3 below:

[0051] The performance index of the transparent conductive film finished product that table 3 embodiment of the present invention 3 produces

[0052]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production process of nano-silver wire transparent conductive film, comprising the following steps: (1) base material preparation: the selected base material is a PET base, and the prepared PET base is hardened; (2) coating Cloth the configured coating nano-silver wire coating solution and protective glue coating solution: apply the configured nano-silver wire coating solution and protective glue coating solution to the PET film base through coating equipment respectively; (3 ) Drying: drying the coated film; (4) Winding: winding the finished product. The process of the invention can effectively improve the good rate of the nano-silver wire conductive film, and accelerate the substitution of the nano-silver wire conductive film for ITO.

Description

technical field [0001] The invention belongs to the technical field of producing transparent conductive films, and in particular relates to a production process of nano-silver wire transparent conductive films. Background technique [0002] With the shipment area of ​​domestic capacitive screens exceeding 4 million square meters in 2013, the demand for ITO conductive glass exceeded 3.6 million square meters, and the demand for ITO PET conductive film exceeded 1.4 million square meters. From the cost analysis of upstream materials in the touch screen industry, ITO materials account for about 40%. And with the development of the touch screen industry, the demand for ITO materials will increase. As the rare metal indium required for ITO materials, not only the price will continue to rise, but there will be a danger of running out. [0003] Nano-silver wire (SNW, silvernanowire) technology is to smear nano-silver wire ink material on PET substrate or glass substrate, and then u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/044C09D4/02C09D4/06C09D5/24C08L67/02
CPCC08J2367/02C08J2433/04C08J2475/04C09D4/06C09D5/24C08J7/0427
Inventor 吴敏郭佳亮周红霞王乐跃李小军万珊云
Owner LUCKY HUAGUANG GRAPHICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com